Methods of making acrylamide-acrylic acid copolymers
A method of making acrylamide-acrylic acid copolymers in water-in-oil latices is described. The method results in a copolymer having randomly distributed carboxylate functionalities and is suitable for ionic crosslinking. The copolymers and their ionically crosslinked counterparts are useful for enhanced oil recovery processes.
1. A composition comprising a water-in-oil latex, the water-in-oil latex comprising a water phase and an oil phase, the water phase comprising water and monomers, the monomers consisting of acrylamide and acrylic acid, wherein the pH of the water phase is about 3.0 to 4.5; wherein the latex further comprises a surfactant mixture consisting essentially of nonionic surfactants and comprising a block copolymer.
2. The composition of claim 1 wherein the ratio of acrylamide to acrylic acid is about 60:40 to 99:1.
3. The composition of claim 1 wherein the block copolymer is a triblock copolymer comprising at least one block consisting essentially of ethylene glycol repeat units and having an HLB of about 4 to 6.
4. The composition of claim 3 wherein the triblock copolymer further comprises at least one block consisting essentially of hydroxyacid repeat units.
5. The composition of claim 4 wherein the hydroxyacid is 12-hydroxystearic acid.
6. The composition of claim 1 wherein the pH is about 3.5 to 4.0.
7. A composition comprising a water-in-oil latex formed by a method comprising
a. combining water and monomers to form a water phase, the monomers consisting of acrylamide and acrylic acid;
b. adjusting the pH of the water phase to between about 3.0 to 4.5;
c. combining a hydrocarbon solvent with a surfactant mixture to form an oil phase, the surfactant mixture consisting essentially of nonionic surfactants and comprising a block copolymer;
d. contacting the water phase and the oil phase to form a water-in-oil latex;
e. polymerizing the monomers to form a copolymer; and
f. neutralizing the water phase.
8. The composition of claim 7 further comprising the product of diluting the composition with a water source after neutralizing, wherein the copolymer concentration after diluting is about 0.01 wt % to 1.00 wt %.
9. The composition of claim 8 wherein the water source comprises water and a salt of Ca 2+ , Fe +2 , Fe +3 , Mg 2+ , Cr 2+ , Cr 3+ , Zn 2+ , or Al 3+ .
10. The composition of claim 9 wherein the salt is aluminum citrate or chromium acetate.
11. The composition of claim 7 wherein the ratio of acrylamide to acrylic acid units in the copolymer is about 50:50 to 99:1.
12. The composition of claim 7 wherein the neutralizing comprises contacting the composition with sodium hydroxide and an alkanolamide surfactant.
13. The composition of claim 12 wherein the alkanolamide surfactant is N,N-diethanololeamide.
14. A method of making a water-in-oil copolymer latex, the method comprising
a. combining water and monomers to form a water phase, the monomers consisting of acrylamide and acrylic acid;
b. adjusting the pH of the water phase to between about 3.0 to 4.5;
c. combining a hydrocarbon solvent with a surfactant mixture to form an oil phase, the surfactant mixture consisting essentially of nonionic surfactants and comprising a block copolymer;
d. contacting the water phase and the oil phase to form a water-in-oil latex;
e. polymerizing the monomers to form a copolymer; and
f. neutralizing the water phase.
15. The method of claim 14 further comprising diluting the latex with a water source after neutralizing, wherein the copolymer concentration after diluting is about 0.01 wt % to 1.00 wt %.
16. The method of claim 15 wherein the water source comprises water and a salt of Ca 2+ , Mg 2+ , Cr 2+ , Cr 3+ , Zn 2+ , or Al 3+ .
17. The method of claim 16 wherein the salt is aluminum citrate or chromium acetate.
18. The method of claim 14 wherein the neutralizing comprises contacting the composition with a neutralizing solution, the neutralizing solution comprising sodium hydroxide and an alkanolamide surfactant.
19. A method of diluting a water-in-oil copolymer latex, the method comprising adding a water source to the water-in-oil copolymer latex of claim 14 after the neutralizing, wherein the water source comprises water and a salt of Ca 2+ , Mg 2+ , Cr 2+ , Cr 3+ , Zn 2+ , or Al 3+ ; and the copolymer concentration after diluting is about 0.01 wt % to 1.00 wt %.