Electric double layer capacitance device
The present application is directed to electric double layer capacitance (EDLC) devices. In one aspect, the present application is directed to an electrode comprising an activated carbon cryogel having a tunable pore structure wherein: the surface area is at least 1500 m2/g as determined by nitrogen sorption at 77K and BET analysis; and the pore structure comprises a pore volume ranging from about 0.01 cc/g to about 0.25 cc/g for pores having a pore diameter of 0.6 to 1.0 nm. In another aspect, the present application is directed to an Electric Double Layer Capacitor (EDLC) device comprising an activated cryogel.
1. An electrode comprising a binder and activated carbon, wherein the activated carbon comprises:
a surface area of greater than 1500 m 2 /g, as determined by nitrogen sorption at 77 K and BET analysis; and
a pore structure comprising mesopores having a diameter ranging from 2.0 nm to 10.0 nm and a pore volume ranging from 0.01 cc/g to 0.25 cc/g for pores having a pore diameter of 0.6 nm to 1.0 nm, as determined from N 2 sorption derived DFT,
wherein the electrode has a specific capacitance of at least 100 F/g and a specific power of at least 25 W/g when each of the specific capacitance and specific power is measured in an electric double layer capacitor device comprising an electrolyte comprising equal volumes of propylene carbonate and dimethylcarbonate and further comprising 1.0 M tetraethylammonium tetrafluoroborate.
2. The electrode of claim 1 , wherein the electrode is a component in a supercapacitor, an ultracapacitor, an electric double layer capacitor or a pseudo capacitor.
3. The electrode of claim 1 , wherein the binder is selected from polytetrafluorethylene, perfluoroalkoxy polymer resin, fluorinated ethylene-propylene, polyethylenetetrafluoroethylene, polyvinylfluoride, polyethylenechlorotrifluoroethylene, polyvinylidene fluoride, polychlorotrifluoroethylene, and trifluoroethanol.
4. The electrode of claim 1 , wherein the pore structure comprises:
a pore volume ranging from 0.01 cc/g to 0.15 cc/g for pores having a diameter less than 0.6 nm;
a pore volume ranging from 0.30 cc/g to 0.70 cc/g for pores having a diameter between 1.0 nm and 2.0 nm;
a pore volume ranging from 0.15 cc/g to 0.70 cc/g for pores having a diameter between 2.0 nm and 4.0 nm;
a pore volume ranging from 0.06 cc/g to 0.50 cc/g for pores having a diameter between 4.0 nm and 6.0 nm; and
a pore volume ranging from 0.01 cc/g to 0.30 cc/g for pores having a diameter between 6.0 nm and 8.0 nm; and
wherein the pore volumes are determined from N 2 sorption derived DFT.
5. The electrode of claim 1 , wherein the specific capacitance ranges from 100 F/g to 130 F/g.
6. The electrode of claim 1 , wherein the specific power ranges from 25 W/g to 35 W/g.
7. The electrode of claim 1 , wherein the activated carbon has a surface area greater than 2000 m 2 /g, as determined by nitrogen sorption at 77K and BET analysis.
8. An Electric Double Layer Capacitor (EDLC) device comprising:
a) a positive electrode and a negative electrode, wherein each of the positive and the negative electrodes comprise activated carbon;
b) an inert porous separator; and
c) an electrolyte;
wherein the positive electrode and the negative electrode are separated by the inert porous separator, and wherein the activated carbon comprises:
a surface area of greater than 1500 m 2 /g, as determined by nitrogen sorption at 77 K and BET analysis; and
a pore structure comprising mesopores having a diameter ranging from 2.0 nm to 10.0 nm and a pore volume ranging from 0.01 cc/g to 0.25 cc/g for pores having a pore diameter of 0.6 nm to 1.0 nm, as determined from N 2 sorption derived DFT; and
wherein each of the positive and negative electrodes independently has a specific capacitance of at least 100 F/g and a specific power of at least 25 W/g when each of the specific capacitance and specific power is measured in an electric double layer capacitor device comprising an electrolyte comprising propylene carbonate and dimethylcarbonate and further comprising tetraethylammonium tetrafluoroborate.
9. The EDLC device of claim 8 , wherein the specific capacitance of each of the positive and negative electrodes is no more than 150 F/g.
10. The EDLC device of claim 8 , wherein the specific capacitance of each of the positive and negative electrodes independently ranges from 100 F/g to 130 F/g.
11. The EDLC device of claim 8 , wherein the specific power of each of the positive and negative electrodes independently ranges from 25 W/g to 35 W/g.
12. The EDLC device of claim 8 , wherein each of the positive and negative electrodes independently has a specific energy of at least 25 J/g.
13. The EDLC device of claim 8 , wherein each of the positive and negative electrodes independently has a specific energy ranging from 38 J/g to 45 J/g.
14. The EDLC device of claim 8 , wherein the activated carbon has a surface area greater than 2000 m 2 /g as determined by nitrogen sorption at 77K and BET analysis.
15. The EDLC device of claim 8 , wherein the pore structure comprises a pore volume ranging from 0.30 cc/g to 0.70 cc/g for pores having a diameter between 1.0 nm and 2.0 nm, as determined from N 2 sorption derived DFT.
16. The EDLC device of claim 8 , wherein the pore structure comprises a pore volume ranging from 0.15 cc/g to 0.70 cc/g for pores having a diameter between 2.0 nm and 4.0 nm, as determined from N 2 sorption derived DFT.
17. The EDLC device of claim 8 , wherein the pore structure comprises:
a pore volume ranging from 0.01 cc/g to 0.15 cc/g for pores having a diameter less than 0.6 nm;
a pore volume ranging from 0.30 cc/g to 0.70 cc/g for pores having a diameter between 1.0 nm and 2.0 nm;
a pore volume ranging from 0.15 cc/g to 0.70 cc/g for pores having a diameter between 2.0 nm and 4.0 nm;
a pore volume ranging from 0.06 cc/g to 0.50 cc/g for pores having a diameter between 4.0 nm and 6.0 nm; and
a pore volume ranging from 0.01 cc/g to 0.30 cc/g for pores having a diameter between 6.0 nm and 8.0 nm; and
wherein the pore volumes are determined from N 2 sorption derived DFT.
18. The EDLC device of claim 8 , wherein the pore structure comprises mesopores having a diameter ranging from 2.0 nm to 4.0 nm, as determined from N 2 sorption derived DFT.
19. The EDLC device of claim 8 , wherein the pore structure comprises micropores having a diameter ranging from 0.3 nm to 2.0 nm, as determined from CO 2 sorption derived DFT.
20. An electric double layer capacitor (EDLC) device comprising:
a) a positive electrode and a negative electrode, wherein each of the positive and negative electrode comprises activated carbon and polytetrafluoroethylene;
b) an inert porous separator comprising polypropylene, polyethylene or both;
c) a first and a second current collector each comprising a non-corrosive metal; and
d) an electrolyte comprising substantially equal volumes of propylene carbonate and dimethylcarbonate and further comprising about 1.0 M tetraethylammonium-tetrafluoroborate,
wherein the positive and negative electrodes are separated by the porous separator and each is in contact with one current collector, and wherein the activated carbon comprises:
a surface area of greater than 1500 m 2 /g, as determined by nitrogen sorption at 77 K and BET analysis; and
a pore structure comprising mesopores having a diameter ranging from 2.0 nm to 10.0 nm and a pore volume ranging from 0.01 cc/g to 0.25 cc/g for pores having a pore diameter of 0.6 nm to 1.0 nm, as determined from N 2 sorption derived DFT; and
wherein each of the positive and negative electrodes independently has a specific capacitance of at least 100 F/g and a specific power of at least 25 W/g, as measured in the EDLC device.
21. The EDLC device of claim 20 , wherein the specific capacitance of each of the positive and negative electrodes independently ranges from 100 F/g to 130 F/g.
22. The EDLC device of claim 20 , wherein the specific power for each of the positive and negative electrodes independently ranges from 25 W/g to 35 W/g.
23. The EDLC device of claim 20 , wherein each of the positive and negative electrodes independently has a specific energy ranging from 38 J/g to 45 J/g, as measured in the device.
24. The EDLC device of claim 20 , wherein the activated carbon has a surface area greater than 2000 m 2 /g, as determined by nitrogen sorption at 77K and BET analysis.