Composition for hydrogel sheet, hydrogel sheet manufactured therefrom, and method for manufacturing same
The present invention relates to a composition for a hydrogel sheet including a cellulose ether, a gelling agent, and a gelling promoter, a hydrogel sheet prepared therefrom, and a method of preparing the hydrogel sheet. According to the present invention, the composition for a hydrogel sheet can be used to prepare a hydrogel sheet capable of maintaining the shape thereof without a support by limiting a type of the gelling agent and/or a viscosity of the cellulose ether included in the composition.
1. A method of preparing a hydrogel sheet, the method comprising:
preparing a composition for a hydrogel sheet by mixing a cellulose ether, a gelling agent, and a gelling promoter;
preparing a hydrogel sheet composition solution by inputting the composition for a hydrogel sheet into hot water and performing stirring;
deaerating the hydrogel sheet composition solution by allowing air bubbles contained therein to rise;
casting the deaerated hydrogel sheet composition solution in the form of a sheet; and
gelating the casted sheet type hydrogel sheet composition solution,
wherein an aqueous 2 wt % solution of the cellulose ether has a viscosity of 15 cps to 300 cps, as measured under a condition of 20° C. using an Ubbelohde viscometer.
2. The method of claim 1 , wherein a temperature of the hot water is 70° C. to 100° C.
3. The method of claim 1 , wherein the deaeration is performed by maintaining the hydrogel sheet composition solution at 55° C. to 65° C. for 20 minutes to 60 minutes.