Amine-based carbon dioxide adsorbent resistant to oxygen and sulfur dioxide and method of preparing the same
The core-shell type amine-based carbon dioxide adsorbent including a chelating agent resistant to oxygen and sulfur dioxide according to the present invention is an adsorbent which includes a chelating agent to inhibit oxidative decomposition of amine and has, as a core, a porous support on which an amine compound is immobilized and has, as a shell, an amine layer resistant to inactivity by sulfur dioxide, and a method of preparing the same. The amine-based carbon dioxide adsorbent including a chelating agent exhibits considerably high oxidation resistance because an added chelate compound functions to directly remove a variety of transition metal impurities catalytically acting on amine oxidation. In addition, the sulfur dioxide-resistant amine layer of the shell selectively adsorbs sulfur dioxide to protect the amine compound of the core and, at the same time, the amine compound of the core selectively adsorbs only carbon dioxide. In addition, sulfur dioxide adsorbed on the shell is readily desorbed therefrom at about 110° C. and thus remarkably improved regeneration stability is obtained during the temperature-swing adsorption (TSA) process containing sulfur dioxide.
1. An amine-based carbon dioxide adsorbent in which a chelating agent is supported on a porous support and an amine compound is bonded to the porous support,
wherein the chelating agent is selected from the group consisting of
phosphoric acid and salts in which some or all of the hydrogen cations (protons) thereof are substituted with alkali metal cations,
etidronic acid (1-hydroxyethane 1,1-diphosphonic acid, HEDP) and salts in which some or all of the hydrogen cations thereof are substituted with alkali metal cations,
ethylenediamine tetramethylene phosphonic acid (EDTMP) and salts in which some or all of the hydrogen cations thereof are substituted with alkali metal cations,
pentetic acid (diethylenetriaminepentaacetic acid, DTPA) and salts in which some or all of the hydrogen cations thereof are substituted with alkali metal cations,
dimercaptosuccinic acid (DMSA) and salts in which some or all of the hydrogen cations thereof are substituted with alkali metal cations,
aminotris(methylenephosphonic acid) and salts in which some or all of the hydrogen cations thereof are substituted with alkali metal cations,
diethylenetriamine pentamethylene phosphonic acid (DTPMP) and salts in which some or all of the hydrogen cations thereof are substituted with alkali metal cations, and disodium tetrasulfide.
2. The amine-based carbon dioxide adsorbent according to claim 1 , wherein the chelating agent is present in an amount of 0.01 to 30% by weight, with respect to the total weight of the adsorbent.
3. The amine-based carbon dioxide adsorbent according to claim 1 , wherein the amine compound comprises a unit skeletal structure represented by Formula 2 and Formula 3:
—[(CH 2 ) x —NR] y — [Formula 2]
wherein R is hydrogen or a branched chain, x is an integer of 2 to 6 and y is an integer of 1 to 100; and
—[(CH 2 ) x —NH 2 ] [Formula 3]
wherein x is an integer of 2 to 6.
4. The amine-based carbon dioxide adsorbent according to claim 1 , wherein the amine compound is amino-silane selected from the group consisting of polyalkyleneimine including polyethylenimine or polypropylenimine; 3-aminopropyl-trimethoxysilane, trimethoxy(3-methylaminopropylsilane), N,N-dimethylaminopropyl trimethoxysilane and N-(3-trimethoxysilylpropyl)diethylenetriamine.
5. The amine-based carbon dioxide adsorbent according to claim 1 , wherein the amine compound is present in an amount of 5 to 75% by weight, with respect to the total weight of the adsorbent.
6. The amine-based carbon dioxide adsorbent according to claim 1 , wherein the porous support is selected from the group consisting of silica, alumina, activated carbon and zeolite.
7. The amine-based carbon dioxide adsorbent according to claim 1 , wherein the porous support has a porosity of 0.1 to 5 cc/g.
8. The amine-based carbon dioxide adsorbent according to claim 1 , wherein the porous support is present in an amount of 25 to 95% by weight, with respect to the total weight of the adsorbent.
9. A method of preparing the amine-based carbon dioxide adsorbent of claim 1 comprising:
(a) supporting the chelating agent on the porous support by adding a porous support to a solution in which a chelating agent is dissolved in a solvent;
(b) obtaining a support supporting the chelating agent by removing the solvent;
(c) immobilizing the amine compound on the support by adding the support supporting the chelating agent of the step (b) to a solution in which an amine compound is dissolved in a solvent; and
(d) removing the solvent of step (c).
10. A method of adsorbing carbon dioxide using the adsorbent of claim 1 , comprising contacting the adsorbent with a CO 2 -comprising gas.