Method and device for producing 3D moulded parts by means of a layer construction technique
The invention relates to a method and an apparatus for producing three-dimensional models by layering in a high-speed sintering process.
1. A method of producing 3D moulded parts, comprising the steps of:
applying particulate construction material onto a construction field in a defined layer by means of a coater;
selectively printing one or more absorbers on the defined layer, wherein the absorber is a liquid or a particulate material, wherein an area of the particulate construction material in the defined layer is printed with the absorber and an area of the particulate construction material in the defined layer is without the absorber;
heating the defined layer in a first heating step to a basic temperature of the particulate construction material, which is within a sintering window of the particulate construction material, wherein the sintering window is a temperature span between a solidification temperature and a melting zone of the particulate construction material;
heating the defined layer in a second heating step which is a sintering step that leads to selective melting, by heat input, of the areas printed with absorber, at a sintering temperature above the melting temperature of the particulate construction material, wherein the areas with the selectively printed absorber heat up more than the areas without absorber, and thus a temperature difference is set between areas with and without absorber, wherein the areas without absorber remain within the sintering window, below the melting temperature; and
lowering the construction field by one layer thickness or raising the coater by one layer thickness;
wherein these steps are repeated until the desired 3D moulded part is produced; and
a temperature of the particulate construction material with the absorber is maintained above the solidification temperature of the particulate construction material;
wherein a temperature difference between areas with and without absorber is 0.5 to 30° K.
2. The method according to claim 1 , wherein additional absorber is printed around the 3D moulded part in order to produce at least one jacket which reduces or prevents solidification of the moulded part;
optionally wherein the jacket is constructed with a wall thickness of 1 to 10 mm;
optionally wherein a temperature profile is generated in the applied construction material, said temperature profile being characterised by a temperature distribution including a temperature outside the jacket (T 1 ) a temperature of the jacket area (T 2 ) and a temperature within the jacket area (T 3 ), wherein T 1 is less than T 2 and T 2 is less than T 3 .
3. The method according to claim 1 , wherein the method is characterized by one or any combination of the following:
heating takes place such that only the areas printed with absorber connect by partial melting or sintering;
the construction material is used in the form of a powder or dispersion;
the layer is heated by radiation in a planar or sweeping manner;
the temperature of the construction field and/or the construction material applied is controlled;
the same or different absorbers are used in the 3D moulded part and in a jacket;
the absorber used for the jacket prevents sintering of the construction material; or
the absorber comprises radiation-absorbing components, plasticizers for the particulate construction material or one or more substances interfering with recrystallization.
4. The method according to claim 1 , wherein one source of radiation is used for each of the one or more absorbers,
optionally, wherein the source of radiation emits infrared radiation in the wavelength range from 1 to 20 μm and/or the source of radiation is a short-wavelength IR emitter made of quartz glass.
5. The method of claim 1 , wherein two sintering lamps with different wavelength spectrums or wavelengths or energy input are used, including one sintering lamp whose spectrum is characterised by being composed of a blackbody radiation spectrums different from the other sintering lamp, or being characterised by having a spectrum which differs from a blackbody radiation spectrum.
6. The method of claim 1 , wherein the absorber is applied before the first heating step and the areas with the absorber heat up to a higher temperature than the areas without the absorber in the first heating step.
7. The method of claim 1 , wherein the particulate construction material includes a polyamide.
8. The method of claim 1 , wherein
the temperature or heat input, respectively, is achieved via an emitter or a thermolamp, at a distance from the construction field surface of 10 to 50 cm.
9. The method of claim 1 , wherein the first heating step uses an overhead lamp that is stationary and has an adjustable radiant flux; and
the second heating step uses a sintering lamp that moves over the construction field.
10. The method of claim 2 , wherein
the applied construction material is cyclically heated and cooled off within a predetermined temperature band, having a range of less than 50° K; and/or
a temperature difference between areas with and without absorber is from 0.5 to 10° K.
11. A method of producing 3D moulded parts, comprising the steps of:
applying particulate construction material onto a construction field in a defined layer by means of a coater;
selectively printing one or more absorbers on the defined layer, wherein the absorber is a liquid or a particulate material, wherein an area of the particulate construction material in the defined layer is printed with the absorber and an area of the particulate construction material in the defined layer is without the absorber;
heating the defined layer in a first heating step to a basic temperature of the particulate construction material, which is within a sintering window of the particulate construction material;
heating the defined layer in a second heating step which is a sintering step that leads to selective melting, by heat input, of the areas printed with absorber, at a sintering temperature above the melting temperature of the particulate construction material, wherein the areas with the selectively printed absorber heat up more than the areas without absorber, and thus a temperature difference is set between areas with and without absorber; and
lowering the construction field by one layer thickness or raising the coater by one layer thickness;
wherein these steps are repeated until the desired 3D moulded part is produced;
wherein the first heating step only uses an overhead lamp that is stationary and has an adjustable radiant flux; and
the second heating step uses a sintering lamp that moves over the construction field.
12. The method of claim 11 , wherein the first heating step to the basic temperature is effected by an emitter with a wavelength of about 3 to about 8 μm, and the sintering step is effected by an emitter with a wavelength of about 0.5 to about 1.5 μm.
13. The method of claim 12 , wherein the first heating step to the basic temperature is effected by an emitter with a wavelength of about 5 μm, or the sintering step is effected by an emitter with a wavelength of about 0.9 to about 1.2 μm.
14. The method of claim 12 , wherein the wavelength of an emitter is about the peak wavelength of a blackbody radiation.
15. The method of claim 14 , wherein the absorber is a liquid (preferably an oil-based in containing carbon particles); and
the particulate construction material has an average particle size of 50-60 μm.
16. The method of claim 12 , wherein
the particulate construction material has a melting temperature of 180-190° C., or the particulate construction material has a recrystallization temperature of 140-150° C., or both.
17. The method of claim 16 , wherein
the basic temperature is set to 145° C. to 186° C., or
the sintering temperature is set to 175° C. to 220° C., or both.
18. The method of claim 11 , wherein the particulate construction material includes a polyamide.
19. The method of claim 11 , wherein the overhead lamp is at a distance from the construction field surface of 10 to 50 cm.
20. The method according to claim 11 , wherein the method is characterized by one or any combination of the following:
heating takes place such that only the areas printed with absorber connect by partial melting or sintering;
the construction material is used in the form of a powder or dispersion;
the temperature of the construction field and/or the construction material applied is controlled;
the same or different absorbers are used in the 3D moulded part and in a jacket;
the absorber used for the jacket prevents sintering of the construction material; or
the absorber comprises radiation-absorbing components, plasticizers for the particulate construction material or one or more substances interfering with recrystallization.
21. A method of producing 3D moulded parts, comprising the steps of:
applying particulate construction material onto a construction field in a defined layer by means of a coater;
selectively printing one or more absorbers on the defined layer, wherein the absorber is a liquid or a particulate material, wherein an area of the particulate construction material in the defined layer is printed with the absorber and an area of the particulate construction material in the defined layer is without the absorber;
heating the defined layer in a first heating step to a basic temperature of the particulate construction material, which is within a sintering window of the particulate construction material;
heating the defined layer in a second heating step which is a sintering step that leads to selective melting, by heat input, of the areas printed with absorber, at a sintering temperature above the melting temperature of the particulate construction material, wherein the areas with the selectively printed absorber heat up more than the areas without absorber, and thus a temperature difference is set between areas with and without absorber; and
lowering the construction field by one layer thickness or raising the coater by one layer thickness;
wherein these steps are repeated until the desired 3D moulded part is produced;
wherein additional absorber is printed around the 3D moulded part in order to produce at least one jacket;
wherein the absorber used for the jacket which has a higher boiling point than the absorber used for the 3D moulded part;
wherein the liquid is selectively applied by means of one or more print heads;
wherein the temperature in the area printed with absorber or in the area within the jacket is maintained substantially constant until completion of the printing process and a cooling step.