Method for producing semi-IPN composite, and method for producing synthetic leather
The present invention relates to a method for producing a semi-IPN composite, the method including polymerizing a hydrophilic monofunctional acrylate (b1) and a polyfunctional acrylate (b2) in a solution of a polyurethane (A) prepared using an aliphatic polyisocyanate and/or an alicyclic polyisocyanate as a raw material. The present invention also relates to a method for producing a synthetic leather that includes a layer obtained by drying the semi-IPN composite obtained by the above production method. One object of the present invention is to provide a method for producing a semi-IPN composite excellent in stain resistance. The semi-INP composite obtained by the production method of the present invention is excellent in stain resistance. Therefore, the semi-IPN composite can be used particularly preferably for skin and topcoat layers of synthetic leathers for vehicles.
1. A method for producing a semi-IPN composite, the method comprising polymerizing a hydrophilic monofunctional acrylate (b1) and a polyfunctional acrylate (b2) in a solution of a polyurethane (A) prepared using an aliphatic polyisocyanate and/or an alicyclic polyisocyanate as a raw material,
wherein the hydrophilic monofunctional acrylate (b1) comprises an amido group-containing acrylamide monomer (b1-1) and an oxyethylene group-containing acrylate monomer (b1-2), and
wherein the polymerization ratio (molar ratio) between the amido group-containing acrylamide monomer (b1-1), the oxyethylene group-containing acrylate monomer (b1-2), and the polyfunctional acrylate (b2) is within the range of (b1-1)/(b1-2)/(b2)=50/49.5/0.5 to 89/1/10.
2. The method for producing a semi-IPN composite according to claim 1 , wherein the polyfunctional acrylate (b2) has an oxyalkylene group.
3. The method for producing a semi-IPN composite according to claim 1 , wherein the total amount of the hydrophilic monofunctional acrylate (b1) and the polyfunctional acrylate (b2) is within the range of 10 to 70 parts by mass based on 100 parts by mass of the polyurethane (A).