Conductive composition for electrode, electrode using same, and lithium ion secondary battery
A conductive composition for electrode is provided that is excellent in conductivity and dispersibility. Further, an electrode for lithium ion secondary battery with lower plate resistance and a lithium ion secondary battery excellent in rate characteristics are provided that use this conductive composition. A conductive composition for electrode, including: carbon nanofiber with a median diameter D50 value by volume from 0.1 to 8 pm; an active material; and a binder enables production of an electrode for lithium ion secondary battery with lower plate resistance and a lithium ion secondary battery excellent in rate characteristics.
1. A conductive composition for electrode, comprising: carbon nanofiber with a median diameter D50 value by volume from 0.1 to 3 μm; an active material; and a binder, wherein a content of the carbon nanofiber is from 0.1 to 1.5 mass % based on a sum total.
2. The composition of claim 1 , wherein the carbon nanofiber further has powder resistivity of, measured under a load of 9.8 MPa, 0.03 Ωcm or less and D/G from 0.5 to 1.3.
3. The composition of claim 1 , wherein the active material is selected from any one or more of LiCoO 2 , LiMn 2 O 4 , LiNiO 2 , LiMPO 4 , Li 2 MSiO 4 , LiNi X Mn (2-X) O 4 , Li(Mn X Ni Y Co Z )O 2 , Li(Al X Ni Y Co Z )O 2 , and xLi 2 MnO 3 -(1−x)LiMO 2 , where X in LiNi X Mn (2-X) O 4 satisfies relationship of 0<X<2, X, Y, and Z in Li(Mn X Ni Y Co Z )O 2 or Li(Al X Ni Y Co Z )O 2 satisfy relationship of X+Y+Z=1 and also satisfy relationship of 0<X<1, 0<Y<1, and 0<Z<1, x in xLi 2 MnO 3 -(1-x)LiMO 2 satisfies relationship of 0<x<1, and M in LiMPO 4 , Li 2 MSiO 4 , or xLi 2 MnO 3 -(1-x)LiMO 2 is one or more elements selected from Fe, Co, Ni, and Mn.
4. The composition of claim 1 , wherein the binder is selected from any one or more of polyvinylidene fluoride, polytetrafluoroethylene, a styrene-butadiene copolymer, a (meth)acrylate copolymer, polyvinyl alcohol, and a copolymer of polyvinyl alcohol and polyacrylonitrile.
5. The composition of claim 1 , wherein
the carbon nanofiber is carbon nanofiber produced using a catalyst having an active species containing cobalt as a main component, and using carbon monoxide as a carbon source;
the catalyst has the active species from 3 to 150 mass % supported on a carrier of a magnesium-containing oxide with a specific surface area from 0.01 to 5 m 2 /g; and
the carbon nanofiber is produced in conditions of a reaction temperature from 670° C. to 780° C., a carbon monoxide partial pressure from 0.04 to 0.98 MPa, a hydrogen partial pressure from 1% to 100% based on the carbon monoxide partial pressure, and a carbon monoxide gas flow rate of 1 NL/g-active species-min. or more.
6. An electrode for lithium ion secondary battery, comprising the composition of claim 1 .
7. A lithium ion secondary battery, comprising the electrode for lithium ion secondary battery of claim 6 .