Localized tempering of carburized steel
A method for joining a carburized steel workpiece to a cast iron workpiece is provided that includes tempering a localized area of the carburized steel workpiece, machining the localized area to reduce carbon content, and welding the carburized steel workpiece to the cast iron workpiece at the localized area. The tempering may be performed by induction heating and results in a hardness profile of the localized area of less than 50 HRC.
1. A method of joining a carburized steel workpiece to a cast iron workpiece comprising:
tempering a localized area of the carburized steel workpiece, wherein the carburized steel workpiece is a hypoid or spiral bevel ring gear and the cast iron workpiece is a differential case;
machining the localized area to reduce carbon content after tempering the localized area; and
welding the carburized steel workpiece to the cast iron workpiece at the localized area.
2. The method according to claim 1 , wherein the tempering results in a hardness profile of the localized area of less than 50 HRC.
3. The method according to claim 1 , wherein the machining is performed using carbide tooling.
4. The method according to claim 1 , wherein the carbon content is reduced below about 0.25% by weight.
5. The method according to claim 1 , wherein the tempering is performed by induction heating.
6. The method according to claim 5 , wherein the induction heating comprises heating coils configured to match a profile of the localized area.
7. The method according to claim 1 , wherein the tempering is between about 600° F. and about 1,200° F.
8. The method according to claim 1 , wherein the carbon content is reduced without a carbon blocking paste or an alloy cap.
9. The method according to claim 1 , wherein the welding is laser welding.
10. A method of joining a carburized steel workpiece to a cast iron workpiece comprising:
induction tempering a localized area of the carburized steel workpiece such that a hardness profile of the localized area is less than 50 HRC;
machining the localized area to reduce carbon content below about 0.25% by weight after induction tempering the localized area; and
welding the carburized steel workpiece to the cast iron workpiece at the localized area.
11. The method according to claim 10 , wherein the induction heating comprises heating coils configured to match a profile of the localized area.
12. The method according to claim 11 , wherein the carburized steel workpiece is rotated within the heating coils.
13. The method according to claim 10 , wherein the tempering is between about 600° F. and about 1,200° F.