Flame retardant pressure-sensitive tape
Pressure-sensitive adhesive formulations based on acrylic or rubber adhesives are provided in combination with an aluminum phosphorous salt intumescent flame retardant and a nitrogen containing flame retardant which can act as a blowing agent through thermal decomposition. These flame retardant additives can be incorporated into the adhesive in levels of 10 to 30 percent by weight. These formulations are then placed on a polymeric flame retardant substrate in either a single-sided or double-sided form.
1. A pressure-sensitive adhesive, comprising:
an acrylic adhesive or a rubber adhesive;
aluminum diethyl phosphinate from about 14 wt % to about 29 wt %; and
a gas release agent from about 1 wt % to about 10 wt %, the gas release agent including a member selected from the group consisting of: dicyanoguanidine, phthalocyanine pigment, diazo compound, melamine cyanurate, and combinations thereof;
wherein the pressure-sensitive adhesive is non-hygroscopic and does not absorb moisture from air at greater than 1000 parts per million.
2. The pressure-sensitive adhesive of claim 1 , wherein the aluminum diethyl phosphinate is from about 15 wt % to about 21 wt %.
3. The pressure-sensitive adhesive of claim 1 , wherein the gas release agent is from about 2 wt % to about 5 wt % and the pressure-sensitive adhesive flame provides flame retardance to meet UL94 VTM-0, V-0, and the FAA 60 second vertical burn test and tests for heat and smoke release.
4. The pressure-sensitive adhesive of claim 1 , wherein the ratio of aluminum diethyl phosphinate to gas release agent is from about 2.9:1 to about 15:1.
5. The pressure-sensitive adhesive of claim 1 , wherein the ratio of aluminum diethyl phosphinate to gas release agent is about 6:1.
6. The pressure-sensitive adhesive of claim 1 , wherein the pressure-sensitive adhesive is coated on a substrate.
7. The pressure-sensitive adhesive of claim 6 , wherein the substrate includes a member selected from the group consisting of: polyimide, polyphenylene sulfide, polyphenylene oxide, polyphenylsulfone, polybenzimidazole, and combinations thereof.
8. The pressure-sensitive adhesive of claim 6 , further comprising a backing covering the pressure-sensitive adhesive, the pressure-sensitive adhesive disposed between the backing and the substrate.
9. The pressure-sensitive adhesive of claim 6 , wherein the substrate includes a flame retardant additive, the flame retardant additive including a member selected from the group consisting of: polyethylene terephthalate, polycarbonate, and combinations thereof.
10. The pressure-sensitive adhesive of claim 6 , wherein the substrate has a thickness from about 0.011 mm to about 0.254 mm.
11. The pressure-sensitive adhesive of claim 1 , further comprising from greater than 0 wt % to about 2 wt % of particles, the particles including a member selected from the group consisting of: nano zinc oxide, aluminum oxide, silicon dioxide, carbon nanotubes, and combinations thereof.
12. The pressure-sensitive adhesive of claim 1 , wherein the pressure-sensitive adhesive is coated on one side of a flame retardant substrate.
13. The pressure-sensitive adhesive of claim 12 , wherein a thickness of the pressure-sensitive adhesive is from about 0.011 mm to about 0.254 mm.
14. The pressure-sensitive adhesive of claim 1 , wherein the pressure-sensitive adhesive is coated on both sides of a flame retardant substrate.
15. The pressure-sensitive adhesive of claim 1 , wherein the pressure-sensitive adhesive is substantially insoluble in water.
16. The pressure-sensitive adhesive of claim 1 , wherein the pressure-sensitive adhesive passes ball impact testing according to IEC 61965.
17. A pressure-sensitive adhesive, comprising:
an acrylic adhesive or a rubber adhesive;
aluminum diethyl phosphinate from about 20 wt % to about 22 wt %; and
a gas release agent from about 3 wt % to about 4 wt %, the gas release agent including a member selected from the group consisting of: dicyanoguanidine, phthalocyanine pigment, diazo compound, and combinations thereof;
wherein the pressure-sensitive adhesive is non-hygroscopic and does not absorb moisture from air at greater than 1000 parts per million, provides flame retardance to meet UL94 VTM-0, V-0, and the FAA 60 second vertical burn test and tests for heat and smoke release, and passes ball impact testing according to IEC 61965.
18. A method of making a pressure-sensitive tape, comprising:
coating one side of a substrate with a pressure-sensitive adhesive, the pressure-sensitive adhesive including: an acrylic adhesive or a rubber adhesive; aluminum diethyl phosphinate from about 14 wt % to about 29 wt %; and a gas release agent from about 1 wt % to about 10 wt %, the gas release agent including a member selected from the group consisting of: dicyanoguanidine, phthalocyanine pigment, diazo compound, melamine cyanurate, and combinations thereof, wherein the pressure-sensitive adhesive is non-hygroscopic and does not absorb moisture from air at greater than 1000 parts per million.
19. The method of claim 18 , further comprising coating another side of the substrate with the pressure-sensitive adhesive.
20. The method of claim 18 , wherein the gas release agent is from about 2 wt % to about 5 wt % and the pressure-sensitive adhesive provides flame retardance to meet UL94 VTM-0, V-0, and the FAA 60 second vertical burn test and tests for heat and smoke release.