Multiple layer interlayer resisting defect formation
Multilayered interlayers comprising stiff skin or outer layers and a soft core layer(s) are disclosed. The multilayered interlayers comprise: a first polymer layer (skin layer) comprising plasticized poly(vinyl butyral) resin; a second polymer layer (core layer) comprising a blend of two (or more) plasticized poly(vinyl butyral) resins having different residual hydroxyl content; and optionally a third polymer layer (skin layer) comprising plasticized poly(vinyl butyral) resin.
1. A polymer interlayer that resists formation of iceflower defects, the polymer interlayer comprising:
at least one soft layer wherein the soft layer comprises a blend of two or more poly(vinyl butyral) resins comprising:
a first poly(vinyl butyral) resin having a first residual hydroxyl content;
a second poly(vinyl butyral) resin having a second residual hydroxyl content, wherein the difference between the first residual hydroxyl content and the second residual hydroxyl content is at least 2.0 weight percent; and
a high refractive index plasticizer having a refractive index of at least about 1.460, wherein the high refractive index plasticizer is selected from dipropylene glycol dibenzoate, tripropylene glycol dibenzoate, polypropylene glycol dibenzoate, isodecyl benzoate, 2-ethylhexyl benzoate, diethylene glycol benzoate, butoxyethyl benzoate, butoxyethyoxyethyl benzoate, butoxyethoxyethoxyethyl benzoate, propylene glycol dibenzoate, 2,2,4-trimethyl-1,3-pentanediol dibenzoate, 2,2,4-trimethyl-1,3-pentanediol benzoate isobutyrate, 1,3-butanediol dibenzoate, diethylene glycol di-o-toluate, triethylene glycol di-o-toluate, dipropylene glycol di-o-toluate, 1,2-octyl dibenzoate, tri-2-ethylhexyl trimellitate, di-2-ethylhexyl terephthalate, bis-phenol A bis(2-ethylhexaonate), di-(butoxyethyl) terephthalate, di-(butoxyethyoxyethyl) terephthalate, and mixtures thereof, wherein the first poly(vinyl butyral) resin, the second poly(vinyl butyral resin) and the high refractive index plasticizer are mixed and melt-extruded to form the at least one soft layer;
wherein the first poly(vinyl butyral) resin has a first glass transition temperature (T g ) of the plasticized first resin and the second poly(vinyl butyral) resin has a second glass transition temperature (T g ) of the plasticized second resin, and the second glass transition temperature (T g ) is from 15° C. to 40° C., and wherein the difference between the first and second glass transition temperatures (T g ) is at least 15° C.;
and wherein the soft layer of the polymer interlayer has at least one glass transition temperature (T g ) less than 15° C.;
at least one stiffer layer comprising a third poly(vinyl butyral resin) having a third residual hydroxyl content; and
a plasticizer,
wherein the polymer interlayer has a damping loss factor (η) (as measured by ISO 16940) of at least about 0.15 and a percent haze of less than 1.0% (as measured by a hazemeter in accordance with ASTM D1003-61 (Re-approved 1977)-Procedure A using Illuminant C, at an observer angle of 2 degrees).
2. The polymer interlayer of claim 1 , wherein the second poly(vinyl butyral) resin is present in an amount of from about 5 weight percent to about 45 weight percent.
3. The polymer interlayer of claim 1 , wherein the second poly(vinyl butyral) resin is present in an amount of from about 10 weight percent to about 40 weight percent.
4. The polymer interlayer of claim 1 , wherein the soft layer of the polymer interlayer has at least one glass transition temperature (T g ) less than 0° C.
5. The polymer interlayer of claim 1 , wherein the plasticizer is a mix of two or more plasticizers.
6. The polymer interlayer of claim 1 , further comprising a second high refractive index plasticizer having a refractive index of at least 1.460.
7. The polymer interlayer of claim 1 , wherein the polymer interlayer further comprises a plasticizer having a refractive index of less than about 1.450.
8. The polymer interlayer of claim 1 , wherein the percent haze is less than 0.5% (as measured by ASTM D1003-61 (Re-approved 1977)-Procedure A using Illuminant C, at an observer angle of 2 degrees).
9. The polymer interlayer of claim 1 , wherein the soft layer of the polymer interlayer has at least two different glass transition temperatures (T g ) and the difference between the at least two different glass transition temperatures (T g ) is at least 25° C.
10. The polymer interlayer of claim 9 , wherein the first glass transition temperature (T g ) is less than 0° C. and the second glass transition temperature (T g ) is from 15° C. to 40° C.
11. The polymer interlayer of claim 1 , wherein the plasticized first poly(vinyl butyral) resin has a glass transition temperature (T g ) less than 0° C. and the plasticized second poly(vinyl butyral) resin has a glass transition temperature (T g ) from 15° C. to 40° C.
12. A polymer interlayer that resists formation of iceflower defects, the polymer interlayer comprising:
at least one soft layer wherein the soft layer comprises a blend of two or more poly(vinyl butyral) resins comprising:
a first poly(vinyl butyral) resin having a first residual hydroxyl content;
a second poly(vinyl butyral) resin having a second residual hydroxyl content, wherein the difference between the first residual hydroxyl content and the second residual hydroxyl content is at least 4.0 weight percent; and
at least one plasticizer having a refractive index of at least 1.460 selected from dipropylene glycol dibenzoate, tripropylene glycol dibenzoate, polypropylene glycol dibenzoate, isodecyl benzoate, 2-ethylhexyl benzoate, diethylene glycol benzoate, butoxyethyl benzoate, butoxyethyoxyethyl benzoate, butoxyethoxyethoxyethyl benzoate, propylene glycol dibenzoate, 2,2,4-trimethyl-1,3-pentanediol dibenzoate, 2,2,4-trimethyl-1,3-pentanediol benzoate isobutyrate, 1,3-butanediol dibenzoate, diethylene glycol di-o-toluate, triethylene glycol di-o-toluate, dipropylene glycol di-o-toluate, 1,2-octyl dibenzoate, tri-2-ethylhexyl trimellitate, di-2-ethylhexyl terephthalate, bis-phenol A bis(2-ethylhexaonate), di-(butoxyethyl) terephthalate, di-(butoxyethyoxyethyl) terephthalate, and mixtures thereof, wherein the first poly(vinyl butyral) resin, the second poly(vinyl butyral resin) and the at least one plasticizer having a refractive index of at least 1.460 are mixed and melt-extruded to form the at least one soft layer;
and wherein the plasticized first poly(vinyl butyral) resin has a glass transition temperature (T g ) less than 0° C. and the plasticized second poly(vinyl butyral) resin has a glass transition temperature (T g ) from 15° C. to 40° C. and wherein the difference between the first and second glass transition temperatures (T g ) is at least 15° C.;
and wherein the soft layer of the polymer interlayer has at least one glass transition temperature (T g ) less than 15° C.;
at least one stiffer layer comprising a third poly(vinyl butyral resin) having a third residual hydroxyl content; and
a plasticizer,
wherein the polymer interlayer has a damping loss factor (η) (as measured by ISO 16940) of at least about 0.15 and a percent haze of less than 1.0% (as measured by a hazemeter in accordance with ASTM D1003-61 (Re-approved 1977)-Procedure A using Illuminant C, at an observer angle of 2 degrees).
13. The polymer interlayer of claim 12 , wherein the plasticizer is a mix of two or more plasticizers.
14. The polymer interlayer of claim 12 , wherein the second poly(vinyl butyral) resin is present in an amount of from about 5 weight percent to about 45 weight percent.
15. The polymer interlayer of claim 12 , wherein the second poly(vinyl butyral) resin is present in an amount of from about 10 weight percent to about 40 weight percent.
16. The polymer interlayer of claim 12 , further comprising a second high refractive index plasticizer having a refractive index of at least 1.460.
17. The polymer interlayer of claim 12 , wherein the percent haze is less than 0.5% (as measured by ASTM D1003-61 (Re-approved 1977)-Procedure A using Illuminant C, at an observer angle of 2 degrees).
18. The polymer interlayer of claim 12 , wherein the soft layer of the polymer interlayer has at least two different glass transition temperatures (T g ) and the difference between at least two different glass transition temperatures (T g ) is at least 25° C.
19. A polymer interlayer that resists formation of iceflower defects, the polymer interlayer comprising:
at least one soft layer wherein the soft layer comprises a blend of two or more poly(vinyl butyral) resins comprising:
a first poly(vinyl butyral) resin having a first residual hydroxyl content;
a second poly(vinyl butyral) resin having a second residual hydroxyl content, wherein the difference between the first residual hydroxyl content and the second residual hydroxyl content is at least 2.0 weight percent; and
a high refractive index plasticizer having a refractive index of at least about 1.460, wherein the high refractive index plasticizer is selected from dipropylene glycol dibenzoate, tripropylene glycol dibenzoate, polypropylene glycol dibenzoate, isodecyl benzoate, 2-ethylhexyl benzoate, diethylene glycol benzoate, butoxyethyl benzoate, butoxyethyoxyethyl benzoate, butoxyethoxyethoxyethyl benzoate, propylene glycol dibenzoate, 2,2,4-trimethyl-1,3-pentanediol dibenzoate, 2,2,4-trimethyl-1,3-pentanediol benzoate isobutyrate, 1,3-butanediol dibenzoate, diethylene glycol di-o-toluate, triethylene glycol di-o-toluate, dipropylene glycol di-o-toluate, 1,2-octyl dibenzoate, tri-2-ethylhexyl trimellitate, di-2-ethylhexyl terephthalate, bis-phenol A bis(2-ethylhexaonate), di-(butoxyethyl) terephthalate, di-(butoxyethyoxyethyl) terephthalate, and mixtures thereof, wherein the first poly(vinyl butyral) resin, the second poly(vinyl butyral resin) and the high refractive index plasticizer are mixed and melt-extruded to form the at least one soft layer;
wherein the soft layer of the polymer interlayer has at least two different glass transition temperatures (T g ) and the difference between the at least two different glass transition temperatures (T g ) is at least 15° C., wherein the first poly(vinyl butyral) resin has a first glass transition temperature (T g ) of the plasticized first resin and the second poly(vinyl butyral) resin has a second glass transition temperature (T g ) of the plasticized second resin, and the second glass transition temperature (T g ) is from 15° C. to 40° C.;
at least one stiffer layer comprising a third poly(vinyl butyral resin) having a third residual hydroxyl content; and
a plasticizer,
wherein the polymer interlayer has a damping Loss Factor (η) (as measured by ISO 16940) of at least about 0.15 and a percent haze of less than 1.0% (as measured by a hazemeter in accordance with ASTM D1003-61 (Re-approved 1977)-Procedure A using Illuminant C, at an observer angle of 2 degrees), and wherein the second poly(vinyl butyral) resin is present in in amount of from about 5 weight percent to about 45 weight percent.
20. The polymer interlayer of claim 19 , further comprising a second plasticizer, wherein the second plasticizer has a refractive index of less than about 1.450.