Catalyst and method for preparing catalyst
A catalyst includes LTA zeolite including copper ions, wherein a Si/Al ratio of the LTA zeolite is 2 to 50. The catalyst is coated on a honeycomb carrier or a filter. The catalyst removes NOx from a reaction gas at 100° C. or above. The catalyst has an NOx conversion rate of 80% at 450° C. or above.
1. A method for manufacturing a catalyst, comprising:
preparing a first linde type A (LTA) zeolite having a Si/Al ratio is 2 or more;
preparing an ion-containing LTA zeolite by adding second species ions to the first LTA zeolite; and
preparing a copper-type LTA zeolite including copper ions by performing a copper ion exchange on the ion-containing LTA zeolite, and
thermally treating the copper-type LTA zeolite
at a temperature ranging from 400 to 750° C. at a rate of temperature rise of 1 to 30° C./min.
2. The method of claim 1 , wherein the Si/Al ratio of the first LTA zeolite is 2 to 50.
3. The method of claim 1 , wherein the preparing the ion-containing LTA zeolite comprises substituting ions in the first LTA zeolite.
4. The method of claim 1 , wherein the preparing the ion-containing LTA zeolite comprises adding the first LTA zeolite to ammonium nitrate (NH 4 NO 3 ) to obtain a mixture, and then drying the mixture.
5. The method of claim 1 , wherein the performing the copper ion exchanging on the ion-containing LTA zeolite comprises adding the ion-containing LTA zeolite to a copper precursor solution and stirring the solution.
6. The method of claim 1 , wherein the preparing the first LTA zeolite comprises using a LTA seed.
7. A method for manufacturing a catalyst, comprising:
preparing a first LTA zeolite having a Si/Al ratio is 2 or more;
preparing an ion-containing LTA zeolite by adding second species ions to the first LTA zeolite; and
preparing an iron-type LTA zeolite by performing an iron (Fe) ion exchange on the ion-containing LTA zeolite, and
thermally treating the iron-type LTA zeolite
at a temperature ranging from 400 to 750° C. at a rate of temperature rise of 1 to 30° C./min.
8. The method of claim 7 , wherein the preparing the iron ion exchange on the ion-containing LTA zeolite comprises adding the ion-containing LTA zeolite to an iron precursor solution and stirring the solution.
9. The method of claim 7 , wherein the preparing the ion-containing LTA zeolite comprises adding the first LTA zeolite to ammonium nitrate (NH 4 NO 3 ) to obtain a mixture, and then drying the mixture.
10. The method of claim 7 , wherein the performing the iron ion exchange on the ion-containing LTA zeolite further comprises:
mixing the ion-containing LTA zeolite with at least one of iron(III) nitrate nonahydrate (Fe(NO 3 ) 3 .9H 2 O), sulfuric acid hydrate (FeSO 4 .7H 2 O), iron(II) oxalate dihydrate (FeCl 2 .4H 2 O), or iron(III) chloride tetrahydrate (FeCl 2 .4H 2 O); and
stirring the mixture.
11. The method of claim 7 , wherein the preparing the first LTA zeolite comprises using an LTA seed.
12. The method of claim 7 , wherein the preparing the first LTA zeolite does not use an LTA seed.