Method for manufacturing a cellulose product, cellulose product forming apparatus and cellulose product

1. A method for manufacturing a cellulose product, comprising the steps:

dry forming a cellulose blank comprising cellulose and a member selected from the group consisting of starch, fluorochemicals, alkyl ketene dimer (AKD), alkenyl succinic anhydride (ASA), rosin (acidic sizing), wax, lignin and water glass (sodium silicate) in a dry forming unit,

arranging the cellulose blank in a forming mould wherein the forming mould comprising a positive forming mould part and a negative forming mould part;

heating the cellulose blank to a forming temperature in the range of 100° C. to 200° C.; and

pressing the cellulose blank in the forming mould with a forming pressure of at least 1 MPa, characterized in that, when dry forming the cellulose blank in the dry forming unit, cellulose fibres are carried and formed to the cellulose blank by air as carrying medium, wherein the cellulose blank is formed as a continuous cellulose web in the dry forming unit, wherein the continuous cellulose web is intermittently fed to the forming mould by a feeding unit and

wherein the cellulose blank is formed into a cellulose product having a three-dimensional shape.

2. A method according to claim 1 , wherein the forming pressure is in the range of 1 MPa to 100 MPa.

3. A method according to claim 1 , wherein the heating of the cellulose blank at least partly takes place before pressing the cellulose blank.

4. A method according to claim 1 , wherein the forming mould is heated before pressing the cellulose blank.

5. A method according to claim 1 , wherein the dry forming unit comprises a separating unit, a forming wire and a compacting unit, the method further comprising the steps:

separating cellulose into detached cellulose fibres in the separating unit;

arranging the cellulose fibres onto the forming wire; and

compacting the cellulose fibres in the compacting unit to form the cellulose blank.

6. A method according to claim 5 , further comprising the step:

applying a sizing agent to the cellulose fibres to increase the hydrophobic properties and/or mechanical strength of the cellulose blank.

7. A cellulose product forming apparatus for manufacturing a cellulose product having a three-dimensional shape from a cellulose blank comprising cellulose and a member selected from the group consisting of starch, fluorochemicals, alkyl ketene dimer (AKD), alkenyl succinic anhydride (ASA), rosin (acidic sizing), wax, lignin and water glass (sodium silicate), the cellulose product forming apparatus comprising:

a heating unit configured for heating the cellulose blank to a forming temperature in the range of 100° C. to 200° C.;

a forming mould comprising a positive forming mould part and a negative forming mould part and configured to form the cellulose product by pressing the cellulose blank in the forming mould with a forming pressure of at least 1 MPa;

characterized in that the cellulose product forming apparatus further comprises a dry forming unit for forming the cellulose blank, where the cellulose fibres are carried and formed to the cellulose blank by air as carrying medium wherein the forming mould is adapted to form the cellulose blank into a cellulose product having a three-dimensional shape and where the apparatus is configured such that cellulose blank is a continuous cellulose web in the dry forming unit, wherein the continuous cellulose web is intermittently fed to the forming mould by a feeding unit.

8. A cellulose product forming apparatus according to claim 7 , characterized in that the dry forming unit comprises:

A separating unit for separating cellulose into detached cellulose fibres;

A forming wire for the cellulose fibres; and

A compacting unit for compacting the cellulose fibres to form the cellulose blank.

9. A cellulose product forming apparatus according to claim 7 ,

Characterized in that the forming mould comprises the heating unit.

10. A cellulose product forming apparatus according to claim 7 ,

Characterized in that the cellulose product forming apparatus comprises an application unit adapted to apply sizing agents to the cellulose fibres.