Aqueous ethylene-vinyl alcohol copolymer dispersion and oxygen barrier multilayer film coated with said dispersion
An aqueous dispersion of ethylene-vinyl alcohol copolymers suitable to be used as lacquer to realize a thin coating both for flexible or rigid substrates, characterized by excellent oxygen and carbon dioxide barrier performances especially under high humidity conditions. The dispersion comprises a first ethylene-vinyl alcohol copolymer in the form of capsules with an ethylene content comprised between 24 and 38 mol % and a second ethylene-vinyl alcohol copolymer with an ethylene content lower than 15 mol %.
1. An aqueous dispersion, comprising:
a first ethylene-vinyl alcohol copolymer in the form of capsules with an ethylene content ranging between 24 and 38 mol %; and
a second ethylene-vinyl alcohol copolymer with an ethylene content lower than 15 mol %,
wherein a weight ratio between said first ethylene-vinyl alcohol copolymer and said second ethylene-vinyl alcohol copolymer is in a range of from 0.40 to 0.70.
2. The aqueous dispersion according to claim 1 , wherein the first ethylene-vinyl alcohol copolymer in the form of capsules has an ethylene content ranging between 27 and 32 mol %.
3. The aqueous dispersion according to claim 1 , further comprising:
an alcohol in an amount ranging between 5 and 10% by weight.
4. The aqueous dispersion according to claim 1 , wherein the first ethylene-vinyl alcohol copolymer capsules have a particle size distribution with a volume mean diameter ranging between 0.1 and 10.0 μm.
5. The aqueous dispersion according to claim 4 , wherein the first ethylene-vinyl alcohol copolymer capsules with a diameter larger than 1.0 μm comprise an internal cavity.
6. The aqueous dispersion according to claim 1 , further comprising:
a filler in an amount ranging between 0.1 and 7% by weight.
7. The aqueous dispersion according to claim 6 , wherein the filler is selected from the group consisting of zeolites, graphene, graphene oxide, cellulose, and zirconium phosphate.
8. The aqueous dispersion according to claim 1 , further comprising:
tetraethoxysilane (TEOS) in an amount ranging between 25 and 100% by weight with respect to the first and second ethylene-vinyl alcohol copolymers.
9. The aqueous dispersion according to claim 1 , further comprising:
chitosan in an amount ranging between 0.5 and 5% by weight with respect to the first and second ethylene-vinyl alcohol copolymers.
10. A lacquer-coated barrier laminate, comprising:
at least a substrate; and
at least a coating layer,
wherein said coating layer comprises a first ethylene-vinyl alcohol copolymer in the form of capsules with an ethylene content ranging between 24 and 38 mol %, and a second ethylene-vinyl alcohol copolymer with an ethylene content lower than 15 mol %, wherein a weight ratio between said first ethylene-vinyl alcohol copolymer and said second ethylene-vinyl alcohol copolymer is in a range of from 0.40 to 0.70.
11. The lacquer-coated barrier laminate according to claim 10 , wherein the substrate is selected from the group consisting of polyethylene terephthalate (PET), polyamide (PA), polyethylene furanoate (PEF), polyethylene (PE), polypropylene (PP), polybutylene adipate terephthalate (PBAT), polybutylene succinate (PBS), polylactic acid (PLA), polyhydroxyalkanoates (PHA), starch blends, lignin cellulose blend, and cellophane.
12. The lacquer-coated barrier laminate according to claim 10 , wherein the substrate has a thickness ranging between 8 and 150 μm.
13. The lacquer-coated barrier laminate according to claim 10 , wherein the coating layer has a thickness ranging between 0.1 and 10.0 μm.
14. The lacquer-coated barrier laminate according to claim 10 , further comprising:
an adhesive layer.
15. The lacquer-coated barrier laminate according to claim 14 , wherein the coating layer is in contact with the adhesive layer.
16. The lacquer-coated barrier laminate according to claim 14 , wherein the adhesive layer is a polyurethane laminating adhesive.