Ultrahigh ductility, novel Mg—Li based alloys for biomedical applications
The invention relates to compositions including magnesium-lithium alloys containing various alloying elements suitable for medical implant devices. The devices may be constructed of the compositions or have applied thereto a coating formed therefrom. Within the structure of the magnesium-lithium alloy, there is a co-existence of alpha and beta phases. The invention also relates to methods of preparing the magnesium-lithium alloys and articles, such as medical implant devices, for use in medical applications, such as but not limited to, orthopedic, dental, craniofacial and cardiovascular surgery.
1. A biodegradable medical implant device composed of a ductile, dual phase magnesium-based alloy, consisting of:
the dual phase-magnesium-based alloy having co-existing alpha and beta phases, selected from the group consisting of:
(i) 9.00% by weight lithium based on total weight of the alloy;
0.96% by weight zinc based on total weight of the alloy;
0.01% by weight aluminum based on total weight of the alloy; and
a remainder of magnesium, or
(ii) 8.99% by weight lithium based on total weight of the alloy;
0.87% by weight zinc based on total weight of the alloy;
1.07% by weight aluminum based on total weight of the alloy; and
a remainder of magnesium, or
(iii) 6.11% by weight lithium based on total weight of the alloy;
0.92% by weight zinc based on total weight of the alloy;
0.04% by weight aluminum based on total weight of the alloy; and
a remainder of magnesium; and
optionally, an active agent,
wherein each of the alloys (i), (ii) and (iii) exhibits an elongation of about 48%, about 50% and about 45%, respectively.
2. The medical implant device of claim 1 , consisting of the active agent.
3. A coated, biodegradable medical implant device, consisting essentially of:
a substrate; and
a coating deposited on the substrate, the coating consisting of:
a ductile, dual phase-magnesium-based alloy having co-existing alpha and beta phases, selected from the group consisting of:
(i) 9.00 by weight lithium based on total weight of the alloy;
0.96% by weight zinc based on total weight of the alloy;
0.01% by weight aluminum based on total weight of the alloy; and
a remainder of magnesium, or
(ii) 8.99% by weight lithium based on total weight of the alloy;
0.87% by weight zinc based on total weight of the alloy;
1.07% by weight aluminum based on total weight of the alloy; and
a remainder of magnesium, or
(iii) 6.11% by weight lithium based on total weight of the alloy;
0.92% by weight zinc based on total weight of the alloy;
0.04% by weight aluminum based on total weight of the alloy; and
a remainder of magnesium,
wherein each of the alloys (i), (ii) and (iii) exhibits an elongation of about 48%, about 50% and about 45%, respectively.
4. The coated medical implant device of claim 3 , wherein the plasticity and ductility of said device exceeds plasticity and ductility of devices composed of magnesium containing alloys absent lithium.
5. The coated medical implant device of claim 3 , wherein said device is effective for use in orthopedic, dental, craniofacial and cardiovascular surgeries.
6. The coated medical implant device of claim 3 , wherein the said device is effective to release lithium ions as a therapeutic drug eluting device.
7. The biodegradable medical implant device of claim 1 , wherein the device is selected from the group consisting of a stent, suture, wire or staple.
8. The biodegradable medical implant device of claim 3 , wherein the device is selected from the group consisting of a stent, suture, wire or staple.