Fracking proppant and method of manufacture
A material useful as a proppant comprises a core chemically reacted in situ from coal dust and a polymer derived ceramic material, such that at least a portion of the coal dust is chemically converted to a ceramic, nanoparticles, graphene, nanofibers or combinations of any of these.
1. A material useful as a proppant comprises:
a plurality of particles or rods comprised of a pyrolyzed mixture of coal dust and polymer derived ceramic material, wherein the coal dust is derived from a source of coal, is comprised of carbon, volatile organics and water and is mixed with the polymer derived ceramic material to form a composite mixture, prior to pyrolysis, the composite mixture comprising no less than 40 wt % coal dust, and the composite mixture forms a core of the plurality of particles or rods prior to pyrolysis, the core being processed and at least partially dried and heated at a temperature up to 400 degrees centigrade; and
a slip layer on a surface of the core, wherein, during pyrolysis, a substantial portion of the coal dust chemically reacts, in situ, forming, after pyrolysis is complete, ceramic, graphene, nanotubes, or nanofibers or any combination of ceramic, graphene, nanotubes or nanofibers in the core, such that the core comprises a porous ceramic composite after pyrolysis and the slip layer forms a substantially nonporous ceramic layer substantially free of coal dust particles.
2. The material of claim 1 , wherein the composite mixture comprises no less than 40 wt % and no greater than 90 wt % coal dust, and the polymer derived ceramic material comprises at least the elements silicon, oxygen and carbon.
3. The material of claim 2 , wherein the composite mixture comprises no less than 10 wt % polymer derived ceramic material and no greater than 60 wt % polymer derived ceramic material.
4. The material of claim 1 , wherein the coal dust is derived from a source of coal by pulverizing, crushing, milling or any combination of pulverizing, crushing or milling.
5. The material of claim 1 , wherein the coal dust is first sorted by centrifuging, screening or filtering, such that the coal dust is selected to have a uniform particle size range.
6. The material of claim 1 , wherein the composite mixture comprises a source of iron, and while the composite mixture is being pyrolyzed, the iron acts as a catalyst for the growth of nanotubes, graphene, nanofibers or any combination of nanotubes, graphene or nanofibers.
7. The material of claim 6 , further comprising an external layer of pyrolyzed polymer derived ceramic material substantially free of coal dust particles.
8. The material of claim 1 , wherein the sphericity of the plurality of particles is greater than 0.9.
9. The material of claim 8 , wherein the compressive fracture strength of the plurality of particles is at least 2000 psi.
10. The material of claim 8 , wherein the compressive fracture strength of the plurality of particles is at least 5000 psi.
11. The material of claim 8 , wherein the compressive fracture strength of the plurality of particles is at least 10,000 psi.
12. The material of claim 1 , wherein the particle size (PD50) of the plurality of particles is in a range from 10 microns to 1000 microns.
13. The material of claim 1 , wherein the particle size (PD50) of the plurality of particles is in a range from 20 microns to 500 microns.
14. The material of claim 13 , wherein the compressive fracture strength of the plurality of particles is at least 2000 psi.
15. The material of claim 14 , wherein the plurality of particles are selected with a median particle size (PD50) from 50 microns to 200 microns and exhibit a compressive fracture strength of at least 5000 psi.
16. The material of claim 15 , wherein the median density of the plurality of particles, after pyrolysis is no less than 1.3 g/cc and no greater than 1.8 grams per cubic centimeter.
17. The material of claim 1 , wherein the ceramic layer has a compressive fracture strength in a range from 6000 psi to 20,000 psi.
18. The material of claim 17 , wherein the ceramic layer is substantially nonporous and the core comprises a cancellous ceramic network.
19. The material of claim 1 , wherein the weight percentage of the weight of coal dust to the weight of the mixture of coal dust and polymer derived ceramic material is selected in a range from 60 wt % to 80 wt % within a core portion of the proppant.
20. The material of claim 1 , wherein the coal dust is pulverized to less than 3 microns.
21. The materials of claim 1 , wherein the median density of the plurality of particles is less than 1.5 g/cc.
22. A material useful as a proppant comprises:
a plurality of extruded, elongated rods having a rod length much greater than a rod diameter, each of the rods being comprised of a mixture of coal dust and polymer derived ceramic material, when initially extruded prior to pyrolysis, wherein the coal dust is derived from a source of coal, is comprised of carbon, volatile organics and water, and is mixed with the polymer derived ceramic material to form a composite mixture, the composite mixture being extruded under pressure into rods;
the rods being processed and at least partially dried and heated at a temperature up to 400 degrees centigrade before a slip layer is disposed on a surface of the rods, and during pyrolysis, a substantial portion of the coal dust chemically reacts, in situ, forming, after pyrolysis is complete, ceramic, graphene, nanotubes, or nanofibers or any combination of ceramic, graphene, nanotubes or nanofibers, such that the plurality of rods comprise a porous ceramic composite after pyrolysis, and the slip layer forms a ceramic shell of a substantially nonporous ceramic material, substantially free of coal dust.
23. The material of claim 22 , wherein substantially all of the coal dust is chemically reacted in at least a portion of the core, such that the portion of the core is a ceramic substantially devoid of unreacted coal dust.