Thermal insulating coating film and thermal insulating paint composition
To provide a thermal insulating coating film, which can achieve excellent thermal insulating performance and far-infrared ray reflection performance when formed on, for example, the surface of an outer wall or inner wall of a house and which has excellent adhesiveness and durability. The thermal insulating coating film of the present invention contains a styrene-alkyl acrylate copolymer or a butyl acrylate-styrene copolymer, a white pigment, and hollow acrylic beads. The mass ratio of styrene-alkyl acrylate copolymer or butyl acrylate-styrene copolymer and hollow acrylic beads (hollow acrylic beads/styrene-alkyl acrylate copolymer or butyl acrylate-styrene copolymer) is 1 or less.
1. A thermal insulating coating film, comprising
a styrene-alkyl acrylate copolymer or a butyl acrylate-styrene copolymer,
polypropylene glycol monomethyl ether,
a white pigment, and
hollow acrylic beads,
wherein the hollow acrylic beads occupy 60-80 vol % in a whole coating film, and have an average particle diameter of 10 to 40 μm, and
the white pigment is rutile titanium dioxide, the rutile titanium dioxide is contained in an amount of 74 to 143 parts by mass with respect to 100 parts by mass of the styrene-alkyl acrylate copolymer or the butyl acrylate-styrene copolymer, and the rutile titanium dioxide has an average particle diameter of 0.1 to 10 μm.
2. The thermal insulating coating film according to claim 1 , wherein a hydrocarbon gas is filled inside the hollow acrylic beads.
3. A thermal insulating paint composition, comprising
a styrene-alkyl acrylate copolymer emulsion or a butyl acrylate-styrene copolymer,
polypropylene glycol monomethyl ether,
a white pigment, and
hollow acrylic beads,
wherein the hollow acrylic beads include 17 to 32 parts by mass with respect to 100 parts by mass of the styrene-alkyl acrylate copolymer emulsion with a solid content of 50 mass % or the butyl acrylate-styrene copolymer with a solid content of 50 mass %, and have an average particle diameter of 10 to 40 μm, and
the white pigment is rutile titanium dioxide, the rutile titanium dioxide is contained in an amount of 74 to 143 parts by mass with respect to 100 parts by mass of the styrene-alkyl acrylate copolymer or the butyl acrylate-styrene copolymer, and the rutile titanium dioxide has an average particle diameter of 0.1 to 10 μm.
4. The thermal insulating paint composition according to claim 3 , wherein a hydrocarbon gas is filled inside the hollow acrylic beads.