Latex composition
A latex composition containing a conjugated diene polymer latex and a medium-chain fatty acid glyceride, wherein a content proportion of the medium-chain fatty acid glyceride is 1 to 40 parts by weight with respect to 100 parts by weight of the conjugated diene polymer. In the present invention, a medium-chain fatty acid forming the medium-chain fatty acid glyceride is preferably a fatty acid having 6 to 18 carbon atoms. In the present invention, the medium-chain fatty acid glyceride is preferably a medium-chain fatty acid triglyceride. The latex composition preferably further contains a crosslinking agent.
1. A latex composition comprising:
a conjugated diene polymer latex; and
a fatty acid glyceride of a fatty acid having 6 to 18 carbon atoms, wherein
a content proportion of the fatty acid glyceride is 1 to 40 parts by weight with respect to 100 parts by weight of the conjugated diene polymer, and
the conjugated diene polymer is a synthetic polyisoprene, a styrene-isoprene-styrene block copolymer, or a nitrile group-containing conjugated diene copolymer.
2. The latex composition according to claim 1 , wherein
the fatty acid glyceride is a fatty acid triglyceride.
3. The latex composition according to claim 1 , further comprising
a crosslinking agent.
4. A molded film consisting of the latex composition according to claim 1 .
5. A packaging structure comprising:
a coating film consisting of the latex composition according to claim 1 , the coating film bonding at least a part of a first sheet substrate and at least a part of a second sheet substrate to form a laminate, the packaging structure being capable of containing an article to be packaged between the first sheet substrate and the second sheet substrate.
6. The latex composition according to claim 1 , wherein
the conjugated diene polymer latex comprises water and a conjugated diene polymer.
7. The latex composition according to claim 1 , wherein
the content proportion of the fatty acid glyceride is 1 to 30 parts by weight with respect to 100 parts by weight of the conjugated diene polymer.
8. The latex composition according to claim 1 , wherein
the content proportion of the fatty acid glyceride is 1 to 15 parts by weight with respect to 100 parts by weight of the conjugated diene polymer.
9. The latex composition according to claim 1 , which has a solid content concentration of 15 to 65 wt %.
10. The latex composition according to claim 1 , which has a solid content concentration of 15 to 45 wt %.