Method for manufacturing oil gel capsules and method for manufacturing contact part for vehicle, including oil gel capsules
The present disclosure relates to manufacturing oil gel capsules and adding the same to an overlay layer of a contact part for a vehicle. The present disclosure may provide a method for manufacturing oil gel capsules and a method for manufacturing a contact part for a vehicle, including the oil gel capsules. The oil gels in the oil gel capsules manufactured by the present disclosure may respond to the temperature environment of a contact part for a vehicle, and an aggregation phenomenon of gelators or an aggregation phenomenon of surfactants may not occur even after an oil is released. Therefore, as oil gel capsules are added to an overlay layer, the present disclosure may improve low friction characteristics and seizure resistance characteristics of a contact part for a vehicle without any side effects caused by the above-described aggregation phenomenon.
1. A method for manufacturing oil gel capsules, the method comprising:
(a) manufacturing oil gels by mixing an oil and a gelator; and
(b) producing at least one or more oil gel capsules by mixing the oil gels and an aqueous surfactant solution;
wherein the oil is an engine oil, the gelator is 12-hydroxyoctadecanoic acid, and in step (a), a weight ratio of the 12-hydroxyoctadecanoic acid mixed with the engine oil is 1 to 10 wt % based on a total weight of the engine oil;
wherein the oil gels have a phase transition temperature of 60° C. or more and 70° C. or less; and wherein the oil gel capsules have a size of 0.1 μm or more and 1 μm or less.
2. The method of claim 1 , wherein the oil gel capsules are produced by surrounding the oil gel with a surfactant.
3. The method of claim 1 , wherein the oil gels in step (b) are in a liquid state.
4. The method of claim 1 , wherein in step (a), the oil and the gelator are mixed using an ultrasonic grinder.
5. The method of claim 1 , wherein in step (b), the oil gel and the aqueous surfactant solution are mixed using an ultrasonic grinder.
6. The method of claim 1 , wherein the aqueous surfactant solution is polyvinyl alcohol (PVA).
7. The method of claim 6 , wherein in step (b), the oil gels are mixed with 1 to 10 wt % of the aqueous surfactant solution.
8. The method of claim 1 , further comprising: (c) drying the aqueous surfactant solution.
9. The method of claim 8 , wherein in step (c), the aqueous surfactant solution is freeze-dried.
10. The method of claim 8 , wherein after step (c) is performed, the oil gel capsules are recovered as an oil powder in which at least two or more oil gel capsules are aggregated.
11. A lubricant comprising the oil gel capsules manufactured by the method for manufacturing oil gel capsules according to claim 1 .