Crystal control and stability for high-performance perovskite solar cell
PbI 2 thin film crystallization control is prerequisite of high-quality perovskite layer for the sequentially solution-processed perovskite solar cells. According to the present invention, an efficient-and-simple method has been developed by adding halogen acid additive to improve perovskite thin-film quality and an efficiency of at least 15.2% is obtained. This approach improves coverage, uniformity and stability of pervoskite thin-film. In addition, a nanofiber scaffold is incorporated into the perovskite layer so as to reduce the amount of grain boundaries, thus substantially reducing electron recombination within these boundaries.
1. A solar cell comprising a perovskite layer and a substrate, the pervoskite layer covering the substrate with 100% surface coverage;
wherein the perovskite layer consists of an inorganic-organic perovskite material, the inorganic-organic perovskite material consisting of a lattice structure of CH 3 NH 3 PbI 3 and chloride (Cl) dopants introduced in the lattice structure;
wherein the perovskite layer is prepared by:
heating a mixture comprising a lead (II) iodide (PbI 3 ) solution and hydrochloric acid (HCl) on the substrate thereby forming a PbI 3 thin film consisting of hexagonal-plate shaped PbI 3 crystals on the substrate in view of the HCl, wherein the hexagonal-plate shaped PbI 3 crystals have a length-to-diameter ratio of 2:1 to 3:1; and a X-ray diffraction (XRD) pattern of the hexagonal-plate shaped PbI 3 crystals includes a peak from (110) plane and does not include a peak from (102) plane; and
depositing a CH 3 NH 3 I solution on the PbI 3 thin film formed on the substrate and heating the deposited CH 3 NH 3 I solution and the PbI 3 thin film thereby forming the perovskite layer; and
wherein the hexagonal-plate shaped PbI 3 crystals are formed in view of the HCl such that the perovskite layer is formed with the hexagonal-plate shaped PbI 3 crystals such that the perovskite layer covers the substrate with 100% surface coverage thereby increasing power conversion efficiency of the solar cell.
2. A solar cell comprising a perovskite layer and a substrate, the pervoskite layer covering the substrate with 100% surface coverage;
wherein the perovskite layer consists of an inorganic-organic perovskite material, the inorganic-organic perovskite material consisting of a lattice structure of CH 3 NH 3 PbI 3 and iodide dopants introduced in the lattice structure;
wherein the perovskite layer is prepared by:
heating a mixture comprising a lead (II) iodide (PbI 3 ) solution and hydrochloric acid (HI) on the substrate thereby forming a PbI 3 thin film consisting of hexagonal-plate shaped PbI 3 crystals on the substrate in view of the HI, wherein the hexagonal-plate shaped PbI 3 crystals have a length-to-diameter ratio of 2:1 to 3:1; and a X-ray diffraction (XRD) pattern of the hexagonal-plate shaped PbI 3 crystals includes a peak from (110) plane and does not include a peak from (102) plane; and
depositing a CH 3 NH 3 I solution on the PbI 3 thin film formed on the substrate and heating the deposited CH 3 NH 3 I solution and the PbI 3 thin film thereby forming the perovskite layer; and
wherein the hexagonal-plate shaped PbI 3 crystals are formed in view of the HI such that the perovskite layer is formed with the hexagonal-plate shaped PbI 3 crystals such that the perovskite layer covers the substrate with 100% surface coverage thereby increasing power conversion efficiency of the solar cell.