Magnesium alloy
View Patent ↗Magnesium alloy containing, in % by mass, 1.0 to 2.0% of Zn, 0.05 to 0.80% by mass of Zr, 0.05 to 0.40% by mass of Mn, and the balance consisting of Mg and unavoidable impurities. The magnesium alloy may further contain, in % by mass, 0.005% or more and less than 0.20% of Ca.
1. A magnesium alloy consisting of, in % by mass, 1.0 to 2.0% of Zn, 0.05 to 0.80% of Zr, 0.05 to 0.40% of Mn, and the balance consisting of Mg and unavoidable impurities, wherein the magnesium alloy consists of a matrix phase composed of single-phase solid solution and Zr-bearing precipitates dispersed in the matrix phase, wherein an amount of each of Fe, Ni, Co, and Cu as unavoidable impurities is less than 10 ppm, a total content of the unavoidable impurities is 30 ppm or less, and grain sizes of the precipitates are smaller than 500 nm.
2. A magnesium alloy consisting of, in % by mass, 1.0 to 2.0% of Zn, 0.05 to 0.80% of Zr, 0.05 to 0.40% of Mn, 0.005% to less than 0.20% of Ca, and the balance consisting of Mg and unavoidable impurities, wherein the magnesium alloy consists of matrix phase composed of single-phase solid solution and Zr-bearing precipitates dispersed in the matrix phase, wherein an amount of each of Fe, Ni, Co, and Cu as unavoidable impurities is less than 10 ppm, a total content of the unavoidable impurities is 30 ppm or less, and grain sizes of the precipitates are smaller than 500 nm.
3. The magnesium alloy according to claim 1 , wherein the magnesium alloy is free from rare earth elements and aluminum.
4. The magnesium alloy according to claim 1 , wherein an average grain size of the matrix phase is 1 to 10 μm.
5. The magnesium alloy according to claim 1 , having, in the values measured according to JIS Z2241, a tensile strength of 230 to 380 MPa, a proof stress of 180 to 330 MPa, a fracture elongation of 10 to 30%.
6. A medical device including a metal member comprising the magnesium alloy according to claim 1 .
7. The magnesium alloy according to claim 2 , wherein the magnesium alloy is free from rare earth elements and aluminum.
8. The magnesium alloy according to claim 2 , wherein an average grain size of the matrix phase is 1 to 10 μm.
9. The magnesium alloy according to claim 2 , having, in the values measured according to JIS Z2241, a tensile strength of 230 to 380 MPa, a proof stress of 180 to 330 MPa, a fracture elongation of 10 to 30%.
10. A medical device including a metal member comprising the magnesium alloy according to claim 2 .