Porous insulator, electrode, and nonaqueous power storage element
A porous insulator is provided. The porous insulator comprises a porous structure comprising a polymer compound having communicating pores, and a solid having a melting point or glass transition temperature lower than that of the polymer compound.
1. A porous insulator comprising:
a porous monolithic structure having communicating pores, wherein the porous monolithic structure comprises a polymer compound and has a bicontinuous monolithic structure,
wherein the porous monolithic structure is formed by polymerizing a polyfunctional polymerizable compound in a mixture with solid particles and a porogen by a polymerization induced phase separation method to form a mixture of the polymer compound, the solid particles and the porogen, then removing the porogen; and
wherein the solid particles have a melting point or glass transition temperature lower than that of the polymer compound.
2. The porous insulator of claim 1 , wherein the solid particles are resin particles.
3. The porous insulator of claim 1 , wherein the polymer compound has a cross-linked structure.
4. The porous insulator of claim 1 , wherein the porous monolithic structure does not contain a filler or a fibrous material.
5. The porous insulator of claim 4 , wherein the porous monolithic structure does not contain any of a filler having a melting point or a glass transition temperature greater than that of the polymer compound and a fibrous material having a melting point or a glass transition temperature greater than that of the polymer compound.
6. The porous insulator of claim 1 , wherein the volume ratio of the polymer compound to the solid particles is 1:4 or greater.
7. The porous insulator of claim 1 , wherein the bicontinuous monolithic structure has a backbone comprising a three-dimensional branched network structure of the polymer compound.
8. The porous insulator of claim 1 , which is in the form of a thin film having a thickness of from 3 μm to 50 μm.
9. The porous insulator of claim 1 , wherein the solid particles are resin particles having a melting point in the range of from 80 to 130° C.
10. The porous insulator of claim 1 , wherein the porous monolithic structure includes pores having a diameter of from 0.1 μm to 10 μm.
11. The porous insulator of claim 1 , wherein the solid particles are in the form of resin particles and the resin is at least one selected from the group consisting of polypropylene, polyethylene, and polyvinylidene difluoride.
12. The porous insulator of claim 1 , wherein polymer compound comprises polymerized units of tricyclodecane dimethanol diacrylate.
13. An electrode comprising:
an electrode substrate;
an electrode mixture overlying the electrode substrate, the electrode mixture comprising an active material; and
the porous insulator of claim 1 overlying the electrode mixture.
14. The electrode of claim 13 , wherein a part of the porous insulator is present in a part of the electrode mixture.
15. A nonaqueous power storage element comprising the electrode of claim 13 .
16. A shutdown electrode obtained by overheating the electrode of claim 13 .
17. The shutdown electrode of claim 16 , wherein at least a portion of the solid particles is present in the communicating pores of the porous monolithic structure.
18. The shutdown electrode of claim 16 , wherein at least a portion of the solid particles forms a coating layer over the active material.
19. A monolithic porous insulator, comprising:
a bicontinuous monolithic porous structure having a continuous network of communicating pores present in a solid matrix formed of a polymer compound and solid particles;
wherein the bicontinuous monolithic porous structure is formed by polymerizing a polyfunctional polymerizable compound in a mixture with solid particles and a porogen by a polymerization induced phase separation method to form a mixture of the polymer compound, the solid particles and the porogen, then removing the porogen; and
wherein the solid particles have a melting point or glass transition temperature lower than that of the polymer compound.
20. A porous insulator, comprising:
a porous structure having communicating pores, wherein the porous structure comprises a polymer compound and has a bicontinuous structure; and
a solid having a melting point or glass transition temperature lower than that of the polymer compound,
wherein the porous structure is formed by polymerizing a polyfunctional polymerizable compound in a mixture with the solid and a porogen by a polymerization induced phase separation method to form a mixture of the polymer compound, the solid and the porogen, then removing the porogen;
wherein the bicontinuous structure is present in the entire porous insulator.