Bimetallic catalyst for catalytic partial oxidation of hydrocarbons
A bimetallic catalyst composition containing a mesh substrate having supported thereon an alumina washcoat on which are impregnated bimetallic particles of rhodium and ruthenium in specified amounts. A process for the catalytic partial oxidation of a hydrocarbon, such as methane or natural gas, involving contacting the hydrocarbon with an oxidant in the presence of the aforementioned bimetallic catalyst under reaction conditions sufficient to produce synthesis gas, that is, to a mixture of hydrogen and carbon monoxide.
1. A process of catalytic partial oxidation of a hydrocarbon, comprising contacting the hydrocarbon with an oxidant in the presence of a reforming catalyst under reaction conditions sufficient to produce a mixture of hydrogen and carbon monoxide; the reforming catalyst comprising a mesh substrate having supported thereon an alumina washcoat, on which are impregnated bimetallic particles comprising rhodium and ruthenium; the rhodium being present in an amount equal to or greater than about 5 percent and an amount equal to or less than about 54 percent, by weight, based on a total weight of the rhodium-ruthenium bimetallic particles; the ruthenium being present in an amount equal to or greater than about 46 percent and in an amount equal to or less than about 95 percent, by weight, based on the total weight of the rhodium-ruthenium bimetallic particles, wherein the rhodium and ruthenium occur in bimetallic particles having an average particle size ranging from 5.0 to 5.4 nanometers with a standard deviation no greater than 2.0 nm.
2. The process of claim 1 wherein the hydrocarbon is a gaseous hydrocarbon selected from C 1-4 gaseous hydrocarbons or a mixture thereof; or wherein the hydrocarbon is a liquid hydrocarbon selected from gasoline, kerosene, diesel, naphthas, gas oils, and mixtures thereof.
3. The process of claim 2 wherein the gaseous hydrocarbon is natural gas or methane.
4. The process of claim 1 wherein the oxidant is selected from oxygen, a mixture of oxygen and nitrogen, or a mixture of oxygen and an inert gas.
5. The process of claim 1 wherein a ratio of oxygen atoms in the oxidant to carbon atoms in the hydrocarbon ranges from 0.8:1 to 1.3:1.
6. The process of claim 1 wherein the bimetallic catalyst composition contains essentially no crystalline phase of rhodium oxide, ruthenium oxide, or mixed rhodium-ruthenium oxides.
7. The process of claim 1 wherein the mesh substrate is constructed from a metal or ceramic material.
8. The process of claim 1 wherein the mesh substrate has an ultra-short-channel-length ranging from 25 microns (μm) (0.001 inch) to 500 μm (0.02 inch).
9. The process of claim 8 wherein the mesh substrate comprises from 100 to 1,000 or more flow channels per square centimeter.
10. The process of claim 8 wherein the mesh substrate is configured with a plurality of channels or pores having a diameter ranging from about 0.25 millimeters (mm) to about 1.0 mm, with a void space greater than about 60 percent and up to about 80 percent.
11. The process of claim 1 wherein the mesh substrate comprises a porous structured material having from 5 to 80 pores per inch, and a relative density ranging from 2 to 15 percent, wherein relative density is taken as the density of the structured material divided by a density of solid parent material from which the structured material is constructed.
12. The process of claim 1 wherein the process is conducted at a temperature ranging from 650° C. to 1,200° C. and a pressure ranging from 14.7 psia to 100 psia.
13. The process of claim 1 wherein the process is conducted at a gas hourly space velocity ranging from greater than 20,000 hr −1 to less than 1,600,000 hr −1 .