Synthesis and functionalization of highly monodispersed iron and Core/Iron oxide shell magnetic particles with broadly tunable diameter
View Patent ↗Provided are methods for preparing iron nanoparticles and to iron nanoparticles produced by those methods. The invention also provides methods for coating the iron nanoparticles with oxides and functionalizing the iron nanoparticles with organic and polymeric ligands. Additionally, the invention provides methods of using such iron nanoparticles.
1. A process for the preparation of iron nanoparticles, comprising reacting a Fe 2+ salt with a reducing agent in the presence of a polymer surfactant and a base, wherein the iron nanoparticles have a diameter of between about 200 nm and about 1000 nm, and wherein the reacting is carried out in aqueous solution.
2. The process of claim 1 , wherein the Fe 2+ salt is selected from the group consisting of FeCl 2 , FeBr 2 , FeI 2 , and Fe(SO 4 ) 2 .
3. The process of claim 1 , wherein the reducing agent is selected from the group consisting of NaBH 4 , LiBH 4 , N 2 H 4 , NaH 2 PO, NaBH 3 CN, NaBH(OAc) 3 , a sulfite, and an amino acid.
4. The process of claim 1 , wherein the polymer surfactant is selected from the group consisting of polyvinylpyrrolidone (PVP), polyacrylic acid, polystyrene sulfonate, poly(allylamine hydrochloride), polyvinyl alcohol, poly(methacrylic acid), polyaspartic acid, poly(2-acrylamido-2-methyl-1-propanesulfonic acid), polyacrylamide, polypeptides, glycosaminoglycans, Triton X-100, polyethylene glycol nonyl phenyl ether, and a deoxyribonucleic acid.
5. The process of claim 4 , wherein the polymer surfactant is a PVP having a number average molecular weight of 1 to 80 kilodaltons.
6. The process of claim 1 , wherein the base is aqueous NaOH or KOH.
7. The process of claim 1 , wherein the concentration of polymer surfactant in water is 0.001 to 0.100 g/mL, the concentration of reducing agent is 0.01 to 1.0 M, and the concentration of base is 0.0001 to 1.0 M.
8. The process of claim 7 , wherein the polymer surfactant is PVP of 40 kilodaltons having a concentration of about 0.03 g/mL, the reducing agent is NaBH 4 having a concentration of about 0.1 M, and the base is NaOH having a concentration of about 0.6 mM to about 1.3 mM.