Thermoplastic resin composition
A thermoplastic resin composition includes a first copolymer including a conjugated diene-based polymer, a unit derived from an aromatic vinyl-based monomer, and a unit derived from a vinyl cyan-based monomer; a second copolymer including a unit derived from an aromatic vinyl-based monomer and a unit derived from a vinyl cyan-based monomer; and, with respect to 100 parts by weight of the sum of the first copolymer and the second copolymer, 2.0 to 10 parts by weight of a third copolymer having a soft segment including a unit derived from a polyalkylene glycol and a hard segment including unit derived from an aromatic dicarboxylic acid or aromatic dicarboxylate and a unit derived from a linear aliphatic diol; and 2.5 to 10 parts by weight of a fourth copolymer including an aromatic dicarboxylic acid-derived unit, a unit derived from a linear aliphatic diol, and a unit derived from a cyclic aliphatic diol.
1. A thermoplastic resin composition comprising:
a first copolymer including a conjugated diene-based polymer, a unit derived from an aromatic vinyl-based monomer, and a unit derived from a vinyl cyan-based monomer;
a second copolymer including a unit derived from an aromatic vinyl-based monomer and a unit derived from a vinyl cyan-based monomer;
with respect to 100 parts by weight of sum of the first copolymer and the second copolymer, 2.0 to 10 parts by weight of a third copolymer having a soft segment including a unit derived from a polyalkylene glycol and a hard segment including a unit derived from an aromatic dicarboxylic acid or aromatic dicarboxylate and a unit derived from a linear aliphatic diol; and
2.5 to 10 parts by weight of a fourth copolymer including an aromatic dicarboxylic acid-derived unit, a unit derived from a linear aliphatic diol, and a unit derived from a cyclic aliphatic diol,
wherein the second copolymer has a weight average molecular weight of 120,000 to 180,000 g/mol.
2. The thermoplastic resin composition of claim 1 , wherein the conjugated diene-based polymer has an average particle size of 0.2 to 0.5 μm.
3. The thermoplastic resin composition of claim 1 , wherein the first copolymer is an acrylonitrile/butadiene/styrene graft copolymer.
4. The thermoplastic resin composition of claim 1 , wherein the second copolymer is one or more selected from the group consisting of a styrene/acrylonitrile copolymer and an α-methylstyrene/acrylonitrile copolymer.
5. The thermoplastic resin composition of claim 1 , wherein the third copolymer is included in an amount of 2.5 to 7 parts by weight with respect to 100 parts by weight of the sum of the first copolymer and the second copolymer.
6. The thermoplastic resin composition of claim 1 , wherein the unit derived from the polyalkylene glycol of the third copolymer is a unit derived from one or more selected from the group consisting of polyethylene glycol, polypropylene glycol, poly(1, 2-butylene glycol), polypentylene glycol, polyhexylene glycol, polyheptylene glycol, polyoctylene glycol, polynonylene glycol, polydecylene glycol, and α-hydro-omega-hydroxypoly(oxy-1, 4-butanediyl),
the unit derived from the aromatic dicarboxylic acid or aromatic dicarboxylate is a unit derived from one or more selected from the group consisting of 1,4-benzene dicarboxylic acid, isophthalic acid, 2,6-naphthalene dicarboxylic acid, 1,5-naphthalene dicarboxylic acid, dimethyl terephthalate, dimethyl isophthalate, and dimethyl 2,6-naphthalene dicarboxylate, and
the unit derived from the unit derived from the linear aliphatic diol is a unit derived from one or more selected from the group consisting of 1,2-ethanediol, 1,3-propanediol, 1,4-butanediol, 1,5-pentanediol, and 1,6-hexanediol.
7. The thermoplastic resin composition of claim 1 , wherein the fourth copolymer is included in an amount of 2.5 to 7 parts by weight with respect to 100 parts by weight of the sum of the first copolymer and the second copolymer.
8. The thermoplastic resin composition of claim 1 , wherein the unit derived from the aromatic dicarboxylic acid of the fourth copolymer is a unit derived from one or more selected from the group consisting of 1,4-benzene dicarboxylic acid, isophthalic acid, 2,6-naphthalene dicarboxylic acid, and 1,5-naphthalene dicarboxylic acid,
the unit derived from the linear aliphatic diol is a unit derived from one or more selected from the group consisting of 1,2-ethanediol, 1,3-propanediol, 1,4-butanediol, 1,5-pentanediol, and 1,6-hexanediol, and
the unit derived from the cyclic aliphatic diol is a unit derived from one or more selected from the group consisting of 1,2-cyclohexanediol, 1,3-cyclohexanediol, 1,4-cyclohexanediol, 1,2-cyclohexanedimethanol, 1,3-cyclohexanedimethanol, 1,4-cyclohexanedimethanol, and 2,2,4,4-tetramethyl-1,3-cyclobutanediol.
9. The thermoplastic resin composition of claim 1 , further comprising a flame retardant and a flame retardant aid.
10. The thermoplastic resin composition of claim 9 , wherein the flame retardant is included in an amount of 10 to 30 parts by weight with respect to 100 parts by weight of the sum of the first copolymer and the second copolymer.
11. The thermoplastic resin composition of claim 9 , wherein the flame retardant is one or more selected from the group consisting of tetrabromobisphenol A, decabromodiphenyl oxide, decabrominated diphenyl ethane, 1,2-bis(2,4,6-tribromophenyl) ethane, octabromo-1,3,3-trimethyl-1-phenylindane, tetrabromobisphenol A-bis(2, 3-dibromopropyl ether), and 2,4,6-tris(2,4,6-tribromophenoxy)-1,3,5-triazine.
12. The thermoplastic resin composition of claim 9 , wherein the flame retardant aid is included in an amount of 1 to 15 parts by weight with respect to 100 parts by weight of the sum of the first copolymer and the second copolymer.
13. The thermoplastic resin composition of claim 9 , wherein the flame retardant aid is antimony trioxide.
14. The thermoplastic resin composition of claim 1 , wherein the thermoplastic resin composition has a flame resistance of at least V-0 according to UL-94.
15. The thermoplastic resin composition of claim 1 , wherein a 2 mm-thick specimen of the thermoplastic resin composition has a shrinkage of 0.45-0.65% in a machine direction according to ASTM D955.