Photocurable composition, cured body, gasket in which cured body is used, watertight structure, and method for manufacturing gasket
A photocurable composition is provided. A cured product formed by curing the photocurable composition has reworkability and excellent heat resistance while having flexibility. The photocurable composition includes a telechelic acrylic polymer having an acryloyl group at both ends; a polyfunctional acrylic polymer having acryloyl groups; a monofunctional acrylic monomer; and a fumed silica including at least one of a hydrophilic fumed silica or a fumed silica having a polar group. The photocurable composition has a Martens hardness of 0.07 to 0.75 N/mm 2 , where the Martens hardness is a hardness after the photocurable composition is cured.
1. A photocurable composition comprising:
a telechelic acrylic polymer having an acryloyl group at both ends, the telechelic acrylic polymer being present in an amount of 22 to 71 mass %;
a polyfunctional acrylic polymer having acryloyl groups, the polyfunctional acrylic polymer being present in an amount of 7 to 54 mass %;
a monofunctional acrylic monomer selected from a monofunctional alicyclic (meth)acrylic acid ester monomer, a monofunctional aliphatic (meth)acrylic acid ester monomer, a monofunctional ether-containing (meth)acrylic acid ester monomer, and a monofunctional imide-containing (meth)acrylic acid ester monomer, the monofunctional acrylic monomer being present in an amount of 3 to 27 mass %;
a polyfunctional photocurable monomer being present in an amount of 0 to 10 mass %; and
a fumed silica including at least one of a hydrophilic fumed silica or a fumed silica having a polar group, the fumed silica being present in an amount of 2 to 10 mass %, wherein
the photocurable composition has a Martens hardness of 0.07 to 0.75 N/mm 2 , where the Martens hardness is a hardness after the photocurable composition is cured.
2. The photocurable composition according to claim 1 , wherein the fumed silica includes the hydrophilic fumed silica and a hydrophobic fumed silica having a polar group.
3. The photocurable composition according to claim 1 , wherein the fumed silica having the polar group includes an amino-treated fumed silica.
4. The photocurable composition according to claim 1 , wherein the photocurable composition has an adhesion strength with respect to aluminum of 0.45 N/mm 2 or less, where the adhesion strength is an adhesion strength after the photocurable composition is cured and compressed at 70° C. for 22 hours.
5. The photocurable composition according to claim 1 , wherein the photocurable composition has a compression set of 40% or less, where the compression set is a compression set after the photocurable composition is cured and allowed to stand at 120° C. for 100 hours in accordance with JIS K6262:2013.
6. A cured body of the photocurable composition according to claim 1 .
7. A gasket comprising a cured body of the photocurable composition according to claim 1 .
8. A watertight structure comprising:
a case having an opening;
a cap member closing the opening; and
a gasket made of a cured body of the photocurable composition according to claim 1 , the gasket being provided on at least one of the case or the cap member, the gasket being a gasket that liquid-tightly seals the opening by being compressed and deformed by fitting between the case and the cap member.
9. A method for manufacturing a gasket, the method comprising the steps of:
applying the photocurable composition according to claim 1 to an object that is to be sealed; and
irradiating the applied photocurable composition with actinic radiation.