Composite particles sinterable at a low temperature and allow forming a sintered body that exhibits a large extension are provided. The composite particles include microparticles having an average crystallite diameter of 0.6 to 10 μm and containing a metal, and nanoparticles adhered to a surface of the microparticle, having an average crystallite diameter of 3 to 100 nm, and containing a metal of a same kind as the metal contained in the microparticle.
1. A sintered body obtained from composite particles, the composite particles comprising:
microparticles having an average crystallite diameter of 0.6 to 10 μm, the microparticle containing a metal; and
nanoparticles adhered to a surface of the microparticle, the nanoparticles having an average crystallite diameter of 3 to 100 nm, the nanoparticle containing the same metal as the metal contained in the microparticle;
wherein the sintered body has an average crystallite diameter of 1.76 to 2.29 μm.
2. The sintered body obtained from composite particles according to claim 1 ,
wherein the composite particle has a specific surface area of 1.2 to 2000 cm −1 .
3. The sintered body obtained from composite particles according to claim 1 ,
wherein the nanoparticle is a spherical shaped particle.
4. The sintered body obtained from composite particles according to claim 1 , wherein the composite particles have a specific surface area of 260.9 to 2000 cm −1 .