Steel material for welded steel pipe, having excellent longitudinal uniform elongation, manufacturing method therefor, and steel pipe using same

1. A steel material for a welded steel pipe, the steel material comprising, by wt %, carbon (C): 0.02 to 0.07%, silicon (Si): 0.05 to 0.3%, manganese (Mn): 0.8 to 1.8%, aluminum (Al): 0.005 to 0.05%, nitrogen (N): 0.001 to 0.01%, phosphorus (P): 0.020% or less, sulfur (S): 0.003% or less, nickel (Ni): 0.05 to 0.3%, chromium (Cr): 0.05 to 0.5%, niobium (Nb): 0.01 to 0.1%, and a balance of iron (Fe) and inevitable impurities,

wherein 20 to 50% of polygonal ferrite by area fraction, a low-temperature transformation phase, and a second phase are included as a microstructure, and

the low-temperature transformation phase is acicular ferrite and bainite,

wherein the acicular ferrite is included in an amount of 20 to 40% by area fraction, and

wherein 5% or less, including 0%, of the second phase is included by area fraction.

2. The steel material of claim 1 , further comprising at least one selected from the group consisting of, by wt %, molybdenum (Mo): 0.05 to 0.3%, titanium (Ti): 0.005 to 0.02%, copper (Cu): 0.3% or less, vanadium (V): 0.01 to 0.07%, and calcium (Ca): 0.0005 to 0.005%.

3. The steel material of claim 1 , wherein the second phase is at least one of martensite-austenite constituent, degenerated pearlite, and cementite.

4. The steel material of claim 1 , wherein the steel material has uniform elongation of 8% or more and yield strength of 600 MPa or less.

5. A welded steel pipe, having excellent longitudinal uniform elongation, obtained by pipe making and welding a steel material for a welded steel pipe of claim 1 .

6. The steel material of claim 1 , the steel material comprising, by wt %, manganese (Mn): 0.8 to 1.35%.