Gypsum panels, systems, and methods
Gypsum panels and methods of making the same are provided. A method of making a gypsum panel includes forming a first gypsum slurry by combining stucco, water, a siliconate, and a phosphate salt or polymer, and setting the first gypsum slurry to form at least part of a core of the gypsum panel, wherein the gypsum panel displays a 2-hour water absorption test weight increase of at least 10 weight percent less than an otherwise identical comparative panel containing no phosphate salt or polymer in its core.
1. A method of making a gypsum panel, comprising:
forming a first gypsum slurry by combining stucco, water, a siliconate, siloxane, and a phosphate salt; and
setting the first gypsum slurry to form at least part of a core of the gypsum panel, wherein:
the gypsum panel displays a 2-hour water absorption test weight increase of at least 10 weight percent less than an otherwise identical comparative panel containing no phosphate salt in its core,
the siliconate is present in the first gypsum slurry in an amount of 25 lb/msf to about 50 lb/msf and the gypsum panel has a thickness of ¼ inch to about ¾ inch, and
a ratio of the siloxane to the siliconate in the first gypsum slurry is from 1:10 to 1:30.
2. The method of claim 1 , wherein the phosphate salt comprises sodium trimetaphosphate (STMP), sodium hexametaphosphate (SHMP), or ammonium polyphosphate (APP).
3. The method of claim 1 , wherein:
the siliconate is present in the first gypsum slurry in an amount of 25 lb/msf to 40 lb/msf, and
a thickness of the for gypsum panel is ¼ inch to ⅝ inch.
4. The method of claim 1 , wherein:
the siliconate is present in the first gypsum slurry in an amount of from 25 lb/msf to 30 lb/msf, and
a thickness of the gypsum panel is ¼ inch to ⅝ inch.
5. The method of claim 1 , wherein a ratio of siloxane to siliconate in the first gypsum slurry is from 1:15 to 1:20.
6. The method of claim 1 , wherein a ratio of siloxane to siliconate in the first gypsum slurry is 1:15.
7. The method of claim 1 , wherein:
the siloxane is present in the first gypsum slurry in an amount of from 1 lb/msf to 5 lb/msf, and
a thickness of the gypsum panel is ¼ inch to ⅝ inch.
8. The method of claim 1 , wherein:
the siloxane is present in the first gypsum slurry in an amount of from 2 lb/msf to 5 lb/msf, and
a thickness of the gypsum panel is ¼ inch to ⅝ inch.
9. The method of claim 1 , wherein the siliconate comprises sodium or potassium methylsiliconate, sodium or potassium ethyl siliconate, propylsiliconate, isopropylsiliconate, butylsiliconate, octylsiliconate, phenylsiliconate, or any combination thereof.
10. The method of claim 1 , wherein the siloxane comprises polymethylhydrogensiloxane.
11. The method of claim 1 , wherein:
the phosphate salt is present in the first gypsum slurry in an amount of 0.5 lb/msf to 50 lb/msf, and
a thickness of the gypsum panel is ¼ inch to ⅝ inch.
12. The method of claim 1 , wherein:
the phosphate salt is present in the first gypsum slurry in an amount of 10 lb/msf to 30 lb/msf, and
a thickness of the gypsum panel is ¼ inch to ⅝ inch.
13. The method of claim 1 , wherein:
the phosphate salt comprises STMP, SHMP, or APP, that is present in the first gypsum slurry in an amount of 0.5 lb/msf to 10 lb/msf, and
a thickness of the gypsum panel is ¼ inch to ⅝ inch.
14. The method of claim 1 , wherein the gypsum panel displays:
an average water absorption of not more than 15 percent by weight, after 2 hours of immersion, according to ASTM C1396/C1396M-14a (2014),
an average water absorption of not more than 15 percent by weight, after 2 hours of immersion, according to ASTM C1177/C117M-13 (2013), and/or
an average water absorption of not more than 5 percent by weight, after 2 hours of immersion, according to ASTM C1178/C1188M-13 (2013).
15. The method of claim 1 , further comprising depositing the first gypsum slurry onto a first surface of a facer material.
16. The method of claim 15 , wherein the facer material comprises a fiberglass mat or a paper facer.
17. A gypsum panel made by the method of claim 1 .