Alkali-soluble resin additives and coating compositions including such additives
A coating composition is provided that is useful in coating metal substrates such as interior and/or exterior surfaces of food or beverage cans. In preferred embodiments, the coating composition is formulated using a physical blend of a preformed resin system and an alkali-soluble resin additive.
1. An aqueous coating composition capable of forming an adherent coating onto a metal substrate, the coating composition comprising a physical blend of:
a resin system comprising an acrylic polymer, a polyester polymer, a polyether polymer or a mixture or copolymer thereof; and
an alkali-soluble resin additive having a number average molecular weight of at least 1,000, in an amount less than 10 wt. % based on total resin solids in the coating composition;
wherein the alkali-soluble resin additive is present in the physical blend as a separate component;
wherein the coating is a spray application coating composition; and
wherein if the resin system comprises an acrylic polymer comprising an emulsion polymerized acrylic latex prepared from ethylenically unsaturated monomers, then the coating composition includes more than 50 wt. %, based on total resin solids in the coating composition, of the emulsion polymerized acrylic latex.
2. The coating composition of claim 1 , wherein the resin system comprises an emulsion polymerized acrylic latex.
3. The coating composition of claim 2 , wherein the acrylic latex is not emulsion polymerized in the presence of the alkali-soluble resin additive.
4. The coating composition of claim 1 , wherein the resin system and the alkali-soluble resin additive are not covalently attached to one another while present in the liquid coating composition prior to any cure of the liquid coating composition.
5. The coating composition of claim 1 , wherein the alkali-soluble resin additive comprises an at least partially neutralized acid- or anhydride-functional polymer.
6. The coating composition of claim 5 , wherein the polymer is formed from an ethylenically unsaturated monomer component that includes (i) acrylic acid, (ii) methyl methacrylate, styrene, or a mixture thereof and (iii) optionally one or more alkyl (meth)acrylates other than methyl methacrylate.
7. The coating composition of claim 5 , wherein the at least partially neutralized acid- or anhydride-functional polymer comprises an organic solution polymerized acrylic polymer.
8. The coating composition of claim 5 , wherein the acid- or anhydride-functional polymer exhibits an acid number, prior to neutralization, of at least 40 and less than 500 mg KOH per gram of resin.
9. The coating composition of claim 1 , wherein the alkali-soluble resin additive has a number average molecular weight of less than 50,000.
10. The coating composition of claim 1 , wherein the coating composition includes at least 0.25 wt. % and less than 5 wt. % of the alkali-soluble resin additive, based on total resin solids in the coating composition.
11. The coating composition of claim 1 , wherein the coating composition includes a crosslinker comprising one or more of (i) a resole phenolic crosslinker, (ii) a beta-hydroxyalkylamide crosslinker, or a mixture of (i) and (ii).
12. The coating composition of claim 1 , wherein the coating composition is substantially free of styrene.
13. The coating composition of claim 1 , wherein the coating composition is substantially free of each of bisphenol A, bisphenol F, and bisphenol S, including epoxides thereof.
14. The coating composition of claim 1 , wherein the coating composition has an average viscosity of from at least 5 seconds to less than 40 seconds, as measured by ASTM D1200-88.
15. The coating composition of claim 1 , wherein the coating composition includes from 15 to 25 wt. % of solids.
16. A method of preparing an aqueous coating composition capable of forming an adherent coating on a metal substrate, comprising the steps of:
providing an aqueous composition comprising a resin system comprising an acrylic polymer, a polyester polymer, a polyether polymer or a mixture or copolymer thereof, and
mixing the resin system with less than 10 wt. %, based on total resin solids in the coating composition, of an alkali-soluble resin additive having a number average molecular weight of at least 1,000 to provide a physical blend of the resin system and the alkali-soluble resin additive,
wherein the alkali-soluble resin additive is present in the physical blend as a separate component, and
wherein if the resin system comprises an acrylic polymer comprising an emulsion polymerized acrylic latex prepared from ethylenically unsaturated monomers, then the coating composition includes more than 50 wt. %, based on total resin solids in the coating composition, of the emulsion polymerized acrylic latex.
17. A method of preparing a coated metal food or beverage can or portion thereof comprising the steps of:
providing a coating composition comprising a physical blend of:
a resin system comprising an acrylic polymer, a polyester polymer, a polyether polymer or a mixture or copolymer thereof; and
an alkali-soluble resin additive having a number average molecular weight of at least 1,000, in an amount less than 10 wt. % based on total resin solids in the coating composition;
spray applying the coating composition to an interior surface of a metal food or beverage container or portion thereof; and
curing the coating composition to form on the interior surface a continuous cured thermoset coating having an average film thickness of from 2 to 15 micrometers and a Tg greater than about 50° C.;
wherein the alkali-soluble resin additive is present in the uncured coating composition as a separate component; and
wherein if the resin system comprises an acrylic polymer comprising an emulsion polymerized acrylic latex prepared from ethylenically unsaturated monomers, then the coating composition includes more than 50 wt. %, based on total resin solids in the coating composition, of the emulsion polymerized acrylic latex.
18. An aluminum food or beverage container having a continuous cured inside spray coating having an average film thickness of from 2 to 15 micrometers and a Tg greater than about 50° C. formed from a coating composition comprising a physical blend of:
a resin system, the resin being selected from the group consisting of an acrylic polymer, a polyester polymer, a polyether polymer or a mixture or copolymer thereof, and
an alkali-soluble resin additive having a number average molecular weight of at least 1,000, in an amount less than 10 wt. % based on total resin solids in the coating composition;
wherein the alkali-soluble resin additive is present in the uncured coating composition as a separate component; and
wherein if the resin system comprises an acrylic polymer comprising an emulsion polymerized acrylic latex prepared from ethylenically unsaturated monomers, then the coating composition includes more than 50 wt. %, based on total resin solids in the coating composition, of the emulsion polymerized acrylic latex.
19. The coating composition of claim 7 , wherein the coating composition is a beverage inside spray coating composition that, when spray applied onto an interior of a 12 ounce two-piece drawn and ironed aluminum beverage can at 120 milligrams per can dry coating weight and cured at 180° C. to 200° C. (measured at the can dome) for 30 to 60 seconds, exhibits a global extraction of less than 50 ppm.
20. The coating composition of claim 19 , wherein the coating composition is substantially free of bisphenol A, and wherein the cured coating exhibits a value after drop damage of less than 3.5 mA.
21. The coating composition of claim 20 , wherein the coating composition includes a nitrogen-containing carboxyl-reactive crosslinker.
22. The coating composition of claim 21 , wherein the nitrogen-containing carboxyl-reactive crosslinker comprises a beta-hydroxyalkylamide crosslinker.
23. The coating composition of claim 20 , wherein the resin system comprises an acrylic polymer comprising an emulsion polymerized acrylic latex, and wherein the coating composition is essentially free of each of BPA, BPF, and BPS, including any diepoxides thereof.
24. The coating composition of claim 22 , wherein the resin system comprises an acrylic polymer comprising an emulsion polymerized acrylic latex having a Tg of greater than 20° C., and wherein the coating composition includes more than 50 wt. %, based on total resin solids in the coating composition, of the emulsion polymerized acrylic latex.
25. The coating composition of claim 1 , wherein the resin system comprises an emulsion polymerized acrylic latex prepared from ethylenically unsaturated monomers, and at least some monomers used to prepare the alkali-soluble resin additive are matched with monomers used to prepare the acrylic latex, so as to provide a smoother coating surface compared to a coating in which the alkali-soluble resin additive is omitted.
26. The coating composition of claim 25 , wherein more than 25 wt-% matched monomers are used to prepare the alkali-soluble resin additive and acrylic latex.
27. The coating composition of claim 25 , wherein more than 40 wt-% matched monomers are used to prepare the alkali-soluble resin additive and acrylic latex.
28. The coating composition of claim 25 , wherein more than 50 wt-% matched monomers are used to prepare the alkali-soluble resin additive and acrylic latex.