Silicon nitride ceramic sintered body and preparation method thereof
Disclosed are a silicon nitride ceramic sintered body and a preparation method thereof. The silicon nitride ceramic sintered body has a content of a silicon nitride crystalline phase of not less than 98 wt %, a relative density of not less than 99%, a porosity of not larger than 1%, a grain boundary phase including Li, O, N, and Si elements, and a total content of C, F, Al, Mg, K, Ca, Na and rare-earth metals elements of less than 0.1 wt %.
1. A silicon nitride ceramic sintered body, wherein the silicon nitride ceramic sintered body has a content of a silicon nitride crystalline phase of not less than 98 wt %, a relative density of not less than 99%, a porosity of not larger than 1%, a grain boundary phase comprising Li, 0, N, and Si elements, and a total content of C, F, Al, Mg, K, Ca, Na and rare-earth metals elements of less than 0.1 wt %.
2. The silicon nitride ceramic sintered body of claim 1 , wherein the silicon nitride ceramic sintered body has a total content of Li, O, N and Si elements of 99.7-100 wt %.
3. The silicon nitride ceramic sintered body of claim 1 , wherein the silicon nitride ceramic sintered body has a content of Li element of 0.15-0.6 wt %.
4. The silicon nitride ceramic sintered body of claim 1 , wherein the silicon nitride ceramic sintered body has a content of 0 element of less than 2 wt %.
5. The silicon nitride ceramic sintered body of claim 1 , wherein the silicon nitride crystalline phase in the silicon nitride ceramic sintered body has a particle size of 0.3-20 μm.
6. A method for preparing the silicon nitride ceramic sintered body of claim 1 , comprising:
mixing a silicon nitride powder with a lithium oxide source to obtain a mixture; and
placing the mixture into a mold and sintering under a protective gas atmosphere to obtain the silicon nitride ceramic sintered body,
wherein the lithium oxide source comprises one or more selected from the group consisting of Li 2 O, Li 2 CO 3 , CH 3 COOLi, Li 2 C 2 O 4 , C 2 H 5 OLi, CH 3 OLi, LiOCH(CH 3 ) 2 , CHLiO 2 , C 6 H 5 Li, and C 4 H 9 Li.
7. The method of claim 6 , wherein a content of Li element in the lithium oxide source accounts for 0.15-0.7 wt % of a content of the mixture.
8. The method of claim 6 , wherein the sintering is performed by hot-pressed sintering or spark plasma sintering; and the sintering is performed at a temperature of 1,350-1,800° C. and a pressure of 10-80 MPa for 0.5-5 h.
9. The method of claim 6 , wherein the silicon nitride powder has a particle size of 0.01-20 μm, a content of 0 element of not larger than 1.6 wt %, and a content of metallic impurities of not larger than 0.2 wt %.
10. The method of claim 6 , wherein the mixing is performed by wet-ball milling mixing; a ball mill medium of the wet-ball milling mixing comprises one selected from the group consisting of ethanol and water; a ratio of a total mass of the silicon nitride powder and the lithium oxide source to a mass of the ball mill medium is 1:1; a ratio of the total mass of the silicon nitride powder and the lithium oxide source to a mass of a mill ball is in a range of 1:(2-3); and the wet-ball milling mixing is performed at a rotational speed of 150-300 rpm for 2-10 h.
11. The silicon nitride ceramic sintered body of claim 3 , wherein the silicon nitride ceramic sintered body has a content of 0 element of less than 2 wt %.
12. The method of claim 6 , wherein the silicon nitride ceramic sintered body has a total content of Li, O, N and Si elements of 99.7-100 wt %.
13. The method of claim 6 , wherein the silicon nitride ceramic sintered body has a content of Li element of 0.15-0.6 wt %.
14. The method of claim 6 , wherein the silicon nitride ceramic sintered body has a content of 0 element of less than 2 wt %.
15. The method of claim 6 , wherein the silicon nitride crystalline phase in the silicon nitride ceramic sintered body has a particle size of 0.3-20 μm.