High-efficiency visible-light catalytic material and preparation method and application thereof
A high-efficiency visible-light catalytic material, a preparation method and an application thereof are provided by the present application, relating to the technical field of photocatalytic materials. The present application prepares photocatalytic material Ag@AgCl/CA by compounding Ag@AgCl and calcium alginate gel, and the prepared photocatalytic material is shaped as small particles. The photocatalytic material Ag@AgCl/CA is used to degrade tetracycline antibiotics.
1. A preparation method of a high-efficiency visible-light catalytic material, comprising following steps:
(1) mixing cationic emulsifier and sodium alginate in a solution, followed by ultrasonically dispersing;
(2) adding AgNO 3 , Ca(NO 3 ) 2 and NaCl into a mixed solution prepared in the step (1) in sequence, followed by stirring, standing, filtering and collecting precipitate; and
(3) adding the precipitate obtained in the step (2) into water, then irradiating with an ultraviolet lamp, filtering, washing and freeze-drying to obtain Ag @AgCl/CA as the high-efficiency visible-light catalytic material;
wherein the cationic emulsifier is cetyltrimethyl ammonium bromide.
2. The preparation method according to claim 1 , wherein a duration for the standing in the step (2) is 4-8 h.
3. The preparation method according to claim 1 , wherein a mass ratio of the sodium alginate to the AgNO 3 , the Ca(NO 3 ) 2 and the NaCl is 1:(2-3.5):4:(0.5-2).
4. The preparation method according to claim 1 , wherein in the step (3), a power for the irradiating with the ultraviolet lamp is 10 W, and a duration is 30 min.