Fire retardant and fire blocking composition for use in forest fires, and method of making same
View Patent ↗The invention refers to a flame-retarding and flame-blocking agent in the form of a liquid suspension that efficiently slows down the progress of fire and at the same time, blocks forest fires, acting as a chemical firebreak and as a fire extinguisher, as well as to a method of making the suspension. The application process comprises spraying the diluted aqueous suspension/solution of the invention on a strip of land, forest, or silviculture, without harming the environment, animals, agricultural products, and humans. The product acts for a long time after application, is stable for storage, effective regardless of the water used for dilution, easily dispersible in water, biodegradable without containing toxic products or releasing highly toxic gases, and free of heavy metals. The product has a synergistic action between its components, and it is intended to save lives, natural resources and heritage.
1. A fire retardant and fire blocking composition for use in forest fires, comprising a liquid composition with dissolved and suspended powders, comprising the following range of components:
a nitrogen compound generator of non-combustible gases when subjected to fire: from 17.43% to 44.07% by weight, on Dry Weight Basis (DWB);
a compound of weak acid character generator of non-combustible gases when subjected to fire: from 21.37% to 48.06% (DWB);
an adhesion-promoting compound: from 18.67% to 40.53% (DWB);
a dispersion and suspension facilitating compound: from 0.1% to 0.8% (DWB);
a wetting and surface tension reducing agent: 0.83% to 3.33% (DWB); and
a nitrification inhibiting agent: from 0.585% to 1.49% (DWB); complemented with
a solvent water regulated with organic acidity regulating component until a pH between 3.2 and 4.0 is obtained: between 38% and 50%, in total weight of the solution/suspension,
wherein the nitrogen compound generator is urea;
wherein the dispersion and suspension facilitating compound is sodium carboxymethyl cellulose; and
wherein the adhesion-promoting compound is kaolin with a particle diameter d50 ranging from 1 to 10 μm.
2. The fire retardant and fire blocking composition for use in forest fires according to claim 1 , wherein the compound with a weak acid character that generates incombustible gases is ammonium sulphate.
3. The fire retardant and fire blocking composition for use in forest fires according to claim 1 , wherein the wetting and surface tension reducing agent is polypropylene glycol with an average molecular weight of 2000.
4. The fire retardant and fire blocking composition for use in forest fires according to claim 1 , wherein the nitrification inhibiting agent is dicyandiamide (DCD).
5. The fire retardant and fire blocking composition for use in forest fires according to claim 1 , wherein the acidity regulating component is ascorbic acid.
6. The fire retardant and fire blocking composition for use in forest fires according to claim 1 , wherein the wetting and surface tension reducing agent is an alkoxylated alcohol Dynwet® 800N or similar, in the proportion 0.53 to 1.67% (DWB).
7. The fire retardant and fire blocking composition for use in forest fires according to claim 1 , wherein the nitrification inhibitor agent is 3,4-dimethylpyrazole phosphate (DMPP) in the same proportions.
8. The fire retardant and fire blocking composition for use in forest fires according to claim 1 , wherein the acidity regulating component is citric acid.
9. The fire retardant and fire blocking composition for use in forest fires according to claim 1 , wherein the acidity regulating component is tartaric acid.
10. The fire retardant and fire blocking composition for use in forest fires according to claim 1 , wherein the acidity regulating component is fumaric acid.
11. The fire retardant and fire blocking composition for use in forest fire according to claim 1 , comprising the following composition:
technical urea: 38.11% (DWB);
ammonium sulphate: 29.85% (DWB);
aolin d50 1.6 μm: 27.4% (DWB);
sodium carboxymethyl cellulose (CMC): 0.31% (DWB);
polypropylene glycol with average molecular weight 2000: 2.33% (DWB); and
dicyandiamide (DCD): 1% (DWB), supplemented with solvent water with acidity regulator ascorbic acid dosed until pH 3.8: 40% by weight, relative to the total weight of the concentrated solution/suspension.
12. FIRE RETARDANT AND FIRE BLOCKING COMPOSITION FOR USE IN FOREST FIRES, according to claim 1 , comprising the following composition:
Incombustible gas generator when submitted to fire technical urea: 39.2% (DWB)
Gas-generator compound of weak acid character ammonium sulphate: 30.71% (DWB)
Adhesion promoting compound kaolin d50 1.6 μm: 28.18% (DWB)
Dispersion and suspension facilitator sodium carboxymethyl cellulose (CMC): 0.31% (DWB)
Wetting agent Alkoxylated alcohol Dynwet® 800N from BYK Industries: 0.6% (DWB)
Nitrification inhibiting agent dicyandiamide (DCD): 1% (DWB)
Solvent process water: 40% by weight, relative to the total weight of the concentrated solution/suspension
Acidity regulator ascorbic acid: dosed to pH 3.8 in process water.
13. PROCESS OF PREPARATION OF THE FIRE RETARDANT AND FIRE BLOCKING COMPOSITION FOR USE IN FOREST FIRE, according to claim 1 , comprising the following steps:
Adding the concentration water to a jacketed vessel with indirect heating by water steam, with a high turbulence and dispersion stirrer, of the Dispermix® type or equivalent;
After heating to a temperature between 60° C. and 80° C., adding the acidity regulating agent until reaching the determined pH;
Adding the incombustible mineral adhesion-promoting agent, and dispersing it in the medium under agitation, keeping the temperature controlled;
Turning the water steam flow off, and adding urea and ammonium sulphate under stirring;
Finally, after the urea and ammonium sulphate dissolution time, adding the dispersion facilitating agent, the wetting agent and the nitrification inhibiting agent;
Waiting for the concentrated solution/suspension to cool, and packing it in closed containers.