Method for preparing electro-conductive polymer binding agent and application
The present disclosure specifically relates to a method for preparing an electro-conductive polymer binding agent and an application, the method including the following steps: (1) dissolving 1,3,5,7-tetrakis(4-aminophenyl)adamantane and polyacrylic acid (PAA) in deionized water to form a solution A; (2) dissolving ammonium persulfate (APS) in deionized water to form a solution B; (3) mixing the solution A with the solution B to complete polymerization and cross-linking reactions, and performing vacuum filtration and washing to obtain a hydrogel; and (4) drying the hydrogel obtained in step (3) under vacuum conditions to obtain an electro-conductive polymer binding agent. Lithium-ion batteries obtained in the present disclosure feature high capacity, high cycle stability, and long service life.
1. A method for preparing an electro-conductive polymer binding agent for a negative electrode, comprising the following steps:
(1) dissolving 1,3,5,7-tetrakis(4-aminophenyl)adamantane and polyacrylic acid (PAA) in deionized water, followed by stirring at room temperature to form a solution A, a mass ratio of the 1,3,5,7-tetrakis(4-aminophenyl)adamantane to the PAA being 0.05-1;
(2) dissolving ammonium persulfate (APS) in deionized water to form a solution B, the APS being added in an amount of 1:3 of a mass of the 1,3,5,7-tetrakis(4-aminophenyl)adamantane;
(3) mixing the solution A with the solution B, followed by standing in an ice bath for 6-24 h to complete polymerization and cross-linking reactions, and performing vacuum filtration and washing to obtain a hydrogel; and
(4) drying the hydrogel obtained in step (3) under vacuum conditions to obtain an electro-conductive polymer binding agent.
2. The method for preparing an electro-conductive polymer binding agent according to claim 1 , wherein the solution A is at a concentration of 20 g/L-200 g/L.
3. The method for preparing an electro-conductive polymer binding agent according to claim 1 , wherein in step (4), the drying is performed at a temperature of 80-100° C. for a period of 1-12 h.
4. A method for forming a lithium battery, comprising:
applying the electro-conductive polymer binding agent prepared by the method according to claim 1 in a negative electrode of the lithium battery, the electro-conductive polymer binding agent being mixed with a silicon-based negative electrode material to prepare negative plates of the lithium battery.
5. A method for forming a lithium battery, comprising:
applying the electro-conductive polymer binding agent prepared by the method according to claim 2 in a negative electrode of the lithium battery, the electro-conductive polymer binding agent being mixed with a silicon-based negative electrode material to prepare negative plates of the lithium battery.
6. A method for forming a lithium battery, comprising:
applying the electro-conductive polymer binding agent prepared by the method according to claim 3 in a negative electrode of the lithium battery, the electro-conductive polymer binding agent being mixed with a silicon-based negative electrode material to prepare negative plates of the lithium battery.
7. The method of forming a lithium battery according to claim 4 , wherein the electro-conductive polymer binding agent is mixed with the silicon-based negative electrode material in deionized water to form a negative electrode slurry, and a copper foil is coated with the negative electrode slurry, followed by drying and slicing to obtain the negative plates of the lithium battery.
8. The method of forming a lithium battery according to claim 5 , wherein the electro-conductive polymer binding agent is mixed with the silicon-based negative electrode material in deionized water to form a negative electrode slurry, and a copper foil is coated with the negative electrode slurry, followed by drying and slicing to obtain the negative plates of the lithium battery.
9. The method of forming a lithium battery according to claim 6 , wherein the electro-conductive polymer binding agent is mixed with the silicon-based negative electrode material in deionized water to form a negative electrode slurry, and a copper foil is coated with the negative electrode slurry, followed by drying and slicing to obtain the negative plates of the lithium battery.