Uncured pontic material for orthodontic clear aligners or retainers
The present disclosure is generally directed toward a pontic material that is pliable and easily moldable, possesses a higher tear resistance to resist fragmenting and thus is long lasting, can be pigmented to achieve a good color match to adjacent teeth, and be fashioned into a pontic by the patient at home so as to free the orthodontist and their staff from having to do this purely aesthetic and time-consuming procedure. In addition, the pontic material of the present disclosure is typically permanently pliable so that an untrained person such as a patient would have unlimited time to make corrections to the shape of the material to obtain an aesthetically pleasing shape and typically do so without the use of tools or any specialized tools or equipment.
1. A pontic material comprising a combination of an uncured, uncrosslinked silicone rubber base material and at least one metal oxide pigment mixed therein;
wherein the pontic material is never cured;
wherein the uncured, uncrosslinked silicone rubber base material makes up about 99.90 to about 99.99 weight percent of the pontic material;
wherein the at least one metal oxide pigment comprises titanium dioxide in an amount of about 0.06 weight percent of the pontic material or less; and
wherein the pontic material is opaque at a thickness of 3 mm, mostly opaque at a thickness of 2.5 mm, and at least partially translucent at a thickness of 2 mm or less.
2. The pontic material of claim 1 , wherein the pontic material is pliable with human fingers without the use of tools and wherein the pontic material is free of any adhesive component.
3. The pontic material of claim 1 , wherein the at least one metal oxide pigment further comprises a metal oxide pigment chosen from a group consisting of brown iron oxide blend, yellow iron oxide, and combinations thereof and wherein the pontic material is pliable with human fingers without the use of tools before, during and after use as a pontic within a user's mouth.
4. The pontic material of claim 3 , wherein the at least one metal oxide pigment is a plurality of metal oxide pigments and the pontic material consists of the combination of the uncured, uncrosslinked silicone rubber base material and the plurality of metal oxide pigments mixed therein such that the pontic material has a color of a human tooth and wherein the pontic material is permanently pliable.
5. The pontic material of claim 1 , wherein the at least one metal oxide pigment further comprises a metal oxide pigment chosen from a group consisting of brown iron oxide blend, yellow iron oxide, and combinations thereof.
6. The pontic material of claim 1 , wherein the pontic material consists essentially of the uncured, uncrosslinked silicone rubber base material and the at least one metal oxide pigment mixed therein.
7. The pontic material of claim 1 , wherein the pontic material consists of the uncured, uncrosslinked silicone rubber base material and the at least one metal oxide pigment mixed therein.
8. The pontic material of claim 1 , wherein the at least one metal oxide pigment is a blend of the titanium dioxide, a brown iron oxide blend, a yellow iron oxide, and combinations thereof.
9. The pontic material of claim 1 , wherein the pontic material is configured to be positioned within an interior of an aligner or retainer such that the pontic material is engaged with an inner surface of the aligner or retainer.
10. The pontic material of claim 1 , wherein the at least one metal oxide pigment is a single metal oxide pigment that is the titanium dioxide and the titanium dioxide is present in an amount of from about 0.020 to about 0.055 weight percent of the pontic material.
11. The pontic material of claim 1 , wherein the at least one metal oxide pigment further comprises a blend of iron oxide in an amount of from about 0.0025 to about 0.0075 weight percent of the pontic material.
12. The pontic material of claim 1 , wherein the at least one metal oxide pigment further comprises a blend of a first iron oxide in an amount of from about 0.0005% to about 0.015% by weight of the pontic material and a second iron oxide in an amount from about 0.002% to about 0.0075% by weight of the pontic material.
13. The pontic material of claim 1 , wherein the pontic material is free of an adhesive and the pontic material is an extruded pontic material.
14. The pontic material of claim 1 , wherein the at least one metal oxide pigment comprises from about 0.020 to about 0.055 weight percent of the titanium dioxide, a first iron oxide in an amount of about 0.01 or less weight percent of the pontic material, a second iron oxide in an amount of about 0.003 weight percent of the pontic material, and 0.001 percent by weight brown iron oxide.
15. A kit comprising:
a pontic material that forms a finger pliable pontic that is free of a curing catalyst and the finger pliable pontic is uncured before use as a pontic within a wearer's mouth, during use within a wearer's mouth and after use within a wearer's mouth; and wherein the pontic material used to form the finger pliable pontic consists of a combination of an uncured, uncrosslinked silicone rubber base material in an amount of 99.90 to about 99.99 weight percent of the pontic material and at least one metal oxide pigment mixed therein in an amount of up to about 0.06 weight percent of the pontic material; and
a plastic orthodontic aligner or retainer.
16. The kit of claim 15 further comprising an elongated shaping tool configured to shape the pontic material into the pontic at a tooth location of the plastic orthodontic aligner or retainer.
17. The kit of claim 16 , wherein the at least one metal oxide pigment is a blend of titanium dioxide, a brown iron oxide blend, a yellow iron oxide, and combinations thereof and wherein the pontic material is permanently pliable; and
wherein the pontic material is opaque at a thickness of 3 mm and translucent under a thickness of about 2.5 mm about 2.5 mm.
18. The kit of claim 15 , wherein the pontic material is uncured and the pontic material is free of an adhesive.
19. A method of forming a pontic comprising the steps of:
placing a pontic material into contact with a teeth facing surface of a plastic orthodontic aligner or retainer; wherein the pontic material comprises a combination of an uncured, uncrosslinked silicone rubber base material and a metal oxide pigment mixed therein and wherein the uncured, uncrosslinked silicone rubber base material makes up about 99.90 to about 99.99 weight percent of the pontic material;
wherein the metal oxide pigment comprises titanium dioxide in an amount of about 0.06 weight percent of the pontic material or less; and
wherein the pontic material is opaque at a thickness of 3 mm, mostly opaque at a thickness of 2.5 mm, and at least partially translucent at a thickness of 2 mm or less; and
forming a shape of an entire tooth or a portion of a tooth from the pontic material such that when the plastic orthodontic aligner or retainer is worn the pontic mimics the existence of the entire tooth or a portion of a tooth; and
wherein the pontic material never cures:
before the pontic material is formed into the shape of an entire tooth or a portion of a tooth;
while the pontic material is formed into the shape of an entire tooth or a portion of a tooth; or
after the pontic material is formed into the shape of an entire tooth or a portion of a tooth.
20. The method of forming a pontic of claim 19 , wherein the step of forming of the pontic material is done using a force applicator chosen from the group consisting of: a human's fingers; and an elongated molding tool to mold the pontic material into the shape of the entire tooth or the portion of the tooth;
wherein the metal oxide pigment is a blend of the titanium dioxide, a first iron oxide blend, and a second iron oxide; and
wherein the pontic material is permanently uncured and is free of a curing catalyst.