IP Library › Granted Patent US 12,235,083
Granted Patent B1
US 12,235,083 · App. 18/602,596 · Granted Feb 25, 2025

Ballistic personal protective equipment (PPE) body armor and methods of producing the same

Inventors: Mario Colon (Dover, DE); Scott Spratt (Dover, DE); Eric Stern (Dover, DE)
Assignee: 8910 LLC
F41H5/0428
View Patent ↗
Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US 12,235,083
App. No.
18/602,596
Granted
Feb 25, 2025
Kind
B1
Abstract

Disclosed herein apparatus and associated methods relate to body armor comprising a plate having a ceramic tile bonded to front and back polyolefin layers by front and back pretreated prepreg layers. The pretreated prepreg layers may comprise epoxy resin sheets precooled for storage at 0° F. The polyolefin layers may comprise 940 and 1880 denier extruded polyolefin sheets. The stored cold prepreg sheets may be heated and the hot prepreg sheets used to join the ceramic tile with the extruded polyolefin sheets. The ceramic tile may be bonded to the extruded polyolefin sheets by cooling the ceramic tile, extruded polyolefin sheets and hot prepreg sheets in a −58° F. freezer, forming a cooled bonded plate. A backer comprising stacked plastic sheets may be connected to the plate. The cooled bonded plate may be cured by a curing cycle comprising 260° F. and 120 PSI using an autoclave.

Claims (30)

1. A shield comprising: a bonded plate connected to a backer, wherein said bonded plate comprises:

a ceramic tile having a frontside, a backside, a front polarized prepreg layer on the frontside of the ceramic tile and a back polarized prepreg layer on the backside of the ceramic tile;

a front extruded polyolefin layer bonded to the ceramic tile frontside; and

a back extruded polyolefin layer bonded to the ceramic tile backside.

2. The shield of claim 1 , wherein the front polarized prepreg layer and the back polarized prepreg layer are precooled at not greater than 0° F.

3. The shield of claim 1 , wherein the front extruded polyolefin layer is chemically bonded to the ceramic tile frontside.

4. The shield of claim 1 , wherein the back extruded polyolefin layer is chemically bonded to the ceramic tile backside.

5. The shield of claim 1 , wherein the front polarized prepreg layer and the back polarized prepreg layer comprise at least partially cured epoxy resin.

6. The shield of claim 1 , wherein the ceramic tile has a thickness from 6 mm to 13 mm.

7. The shield of claim 1 , wherein the ceramic tile comprises 30% to 60% silicon carbide and 20% to 30% alumina.

8. The shield of claim 1 , wherein the ceramic tile comprises 46% silicon carbide and 24% alumina.

9. The shield of claim 1 , wherein the ceramic tile frontside has a convex shape and the ceramic tile backside has a concave shape.

10. The shield of claim 1 , wherein the front extruded polyolefin layer and the back extruded polyolefin layer comprise 940 denier extruded polyolefin fabric.

11. The shield of claim 1 , wherein the front extruded polyolefin layer and the back extruded polyolefin layer comprise 1880 denier extruded polyolefin fabric.

12. The shield of claim 1 , wherein the shield is cured.

13. The shield of claim 1 , wherein the plate is cured.

14. The shield of claim 1 , wherein the backer comprises a frontside, a backside, and a plurality of stacked plastic sheets, wherein the backer frontside is connected with the plate backside.

15. The shield of claim 14 , wherein the backer is cured in mechanical union with the plate.

16. The shield of claim 14 , wherein the plurality of stacked plastic sheets comprises 42 plastic sheets.

17. The shield of claim 14 , wherein the plurality of stacked plastic sheets comprises at least one polyethylene sheet.

18. The shield of claim 14 , wherein at least one of the plurality of stacked plastic sheets comprises Ultra-High-Molecular-Weight Polyethylene (UHMWP).

19. The shield of claim 18 , wherein the UHMWP is HB50 UHMWP.

20. The shield of claim 14 , wherein at least one of the plurality of stacked plastic sheets is an extruded polyolefin.

21. The shield of claim 1 , wherein at least one film layer is in mechanical union with the backer.

22. The shield of claim 21 , wherein the at least one film layer is T-LINK L-F610 film.

23. The shield of claim 1 , wherein the shield further comprises a foam layer connected to the backer.

24. The shield of claim 23 , wherein the foam layer is XLPE FOAM.

25. The shield of claim 4 , wherein the shield further comprises a polyurea coating.

26. The shield of claim 1 , wherein the polarized front prepreg layer further comprises a plurality of aligned dipole moments.

27. The shield of claim 1 , wherein the polarized back prepreg layer further comprises a plurality of aligned dipole moments.

Continuity (2)
Provisional Application 63591872 · Oct 20, 2023
Provisional Application 63591748 · Oct 19, 2023
References Cited (36)
US 4457985A · Harpell et al. · 1984 [cited by applicant]
US 5196212A · Knoblach · 1993 [cited by applicant]
US 7074483B2 · Morin · 2006 [cited by applicant]
US 7919418B2 · Bhatnagar et al. · 2011 [cited by applicant]
US 11002518B2 · Wibby et al. · 2021 [cited by applicant]
US 11432605B1 · Eleazer · 2022 [cited by applicant]
US 11536540B2 · Van Heerden · 2022 [cited by applicant]
US 20110203450A1 · Carbajal et al. · 2011 [cited by applicant]
US 20130061739A1 · Cheong et al. · 2013 [cited by applicant]
US 20150268010A1 · Strauss · 2015 [cited by examiner]
US 20150323292A1 · Strauss · 2015 [cited by applicant]
US 20150362293A1 · Strauss · 2015 [cited by examiner]
US 20230098166A1 · Metral et al. · 2023 [cited by applicant]
CA 2072639A1 · 1991 [cited by examiner]
CN 214010114U · 2021 [cited by applicant]
WO 99366066A1 · 1999 [cited by applicant]
WO WO2011049819A2 · 2011 [cited by examiner]
Okabe et al.; “Molecular Dynamics Simulation of Crosslinked Epoxy Resins: Curing and Mechanical Properties” European Polymer Journal, vol. 80, pp. 78-88; Jul. 2016. [cited by applicant]
Budelmann et al.; “Adhesion-cohesion balance of prepreg tack in thermoset automated fiber placement. Part 1: Adhesion and surface wetting” Composites Part C: Open Access 6 (2021) 100204. [cited by applicant]
Likharev, Konstantin K. (Libretexts); “Polarization of Dielectrics” Chapter 3.3; Jun. 2018. [cited by applicant]
Likharev, Konstantin K. (Libretexts); “Electrostatics of Linear Dielectrics” Chapter 3.4; Jun. 2018. [cited by applicant]
Shirasu et al.; “Molecular dynamics simulation of cross-linking processes and material properties for epoxy resins using first-principle calculation combined with global reaction route mapping algorithms” ResearchGate, … [cited by applicant]
Vaidya et al.; “Performance of hybrid Innegra-carbon fiber composites” Scientific Reports, 13:20876; 2023. [cited by applicant]
Yu et al.; “A novel manufacturing method for aligned discontinuous fibre composites (High Performance-Discontinuous Fibre method)” Science Direct, Composites Part A: Applied Science and Manufacturing; vol. 65, pp. 175-1… [cited by applicant]
Lyondell Basell; “A Guide to Polyolefin Film Extrusion” www.LYB.com. [cited by applicant]
Wienzek et al.; “Automated Fabrication of Elastomeric Prepregs for Soft Robotics Applications” WILEY-VCH Verlag GmbH & Co. KGaA 69469 Weinheim, Germany, 2016. [cited by applicant]
Composites One; “Pregregs” https://www.compositesone.com/product/prepreg/. [cited by applicant]
Baghad et al; “Cure kinetics and autoclave-pressure dependence on physical and mechanical properties of woven carbon/epoxy 8552S/AS4 composite laminates” Polymers and Polymer Composites, vol. 29(9S), S903-S913; 2021. [cited by applicant]
Saint-Gobain Ceramics & Refractories; “Forceram Shield” Bonded SiC Shield, Personal Protection Shield; https://www.ceramicsrefractories.saint-gobain.com/products/products-application/ceramic-protection/forceram-shield. [cited by applicant]
Wikipedia; “Bulletproof vest” https://en.wikipedia.org/wiki/Bulletproof_vest. [cited by applicant]
Cromer et al.; “Consolidation of Braided Carbon Fiber/Thermoplastic Tubes by Induction Heating” CAMX 2023. [cited by applicant]
Yuan et al.; “Ceramic-based dielectrics for electrostatic energy storage applications: Fundamental aspects, recent progress, and remaining challenges” Chemical Engineering Journal, vol. 446, Part 1, 136315; Oct. 15, 202… [cited by applicant]
Zhoo et al.; “Characterization of prepreg-prepreg and prepreg-tool friction for unidirectional carbon fiber/epoxy pregreg during hot diaphragm forming process” Polymer Testing, vol. 84, 106440; Apr. 2020. [cited by applicant]
Wikipedia; “Dialectric” https://en.wikipedia.org/wiki/Dielectric. [cited by applicant]
Drakopoulos et al.; “Dielectric Behavior of Nonpolar Polymers and Their Composites: The Case of Semicrystalline Polyolefins” Crystallization as Studied by Broadband Dielectric Spectroscopy; pp. 243-265; First Online: Oc… [cited by applicant]
Elert, Glenn; “Discussion: the basic idea” The Physics Hypertextbook; Dielectrics. [cited by applicant]