Resin film
Provides is a resin film containing a poly(3-hydroxyalkanoate) resin component. A tensile modulus of the resin film is from 500 to 2000 MPa. A swelling degree of the resin film, as measured by immersion of the resin film in methyl ethyl ketone for two hours, is from 1 to 5. Preferably, the poly(3-hydroxyalkanoate) resin component is a mixture of at least two poly(3-hydroxyalkanoate) resins differing in types and/or contents of constituent monomers.
1. A resin film, comprising:
a poly(3-hydroxyalkanoate) resin component comprising a copolymer (A) which is a copolymer of 3-hydroxybutyrate units and other hydroxyalkanoate units and in which a content of the other hydroxyalkanoate units is from 1 to 6 mol %, and a copolymer (B) which is a copolymer of 3-hydroxybutyrate units and other hydroxyalkanoate units and in which a content of the other hydroxyalkanoate units is at least 24 mol %,
wherein in the poly(3-hydroxyalkanoate) resin component, a proportion of the copolymer (A) is from 35 wt % to 80 wt %, and a proportion of the copolymer (B) is from 20 wt % to 65 wt %, the other hydroxyalkanoate units in the copolymer (B) are 3-hydroxyhexanoate units,
a tensile modulus of the resin film is from 500 to 1,500 MPa, and
a swelling degree of the resin film, as measured by immersion of the resin film in methyl ethyl ketone for two hours, is from 1 to 5.
2. The resin film according to claim 1 , wherein an average content of the other hydroxyalkanoate units in total monomer units constituting the poly(3-hydroxyalkanoate) resin component is from 8 to 18 mol %.
3. The resin film according claim 1 , wherein a tearing resistance of the resin film is from 7.9 to 200 N/mm.
4. The resin film according to claim 1 , wherein a thickness of the resin film is from 10 μm to 1 mm.
5. The resin film according to claim 1 , wherein the other hydroxyalkanoate units in the copolymer (A) are 3-hydroxyhexanoate units.
6. The resin film according to claim 5 , wherein in the poly(3-hydroxyalkanoate) resin component, the proportion of the copolymer (A) is from 45 to 80 wt %, and the proportion of the copolymer (B) is from 20 to 55 wt %.
7. The resin film according to claim 1 , wherein the other hydroxyalkanoate units in the copolymer (A) are selected from the group consisting of 3-hydroxyhexanoate units and 4-hydroxybutyrate units.
8. The resin film according to claim 1 , wherein the tensile modulus of the resin film is from 600 to 1,500 MPa.
9. The resin film according to claim 1 , wherein the tensile modulus of the resin film is from 700 to 1.500 MPa.
10. The resin film according to claim 1 , wherein the swelling degree of the resin film, as measured by immersion of the resin film in methyl ethyl ketone for two hours, is from 1 to 4.
11. The resin film according to claim 1 , wherein the swelling degree of the resin film, as measured by immersion of the resin film in methyl ethyl ketone for two hours, is from 1 to 2.5.
12. The resin film according to claim 1 , wherein in the poly(3-hydroxyalkanoate) resin component, the proportion of the copolymer (A) is from 45 to 80 wt %, and the proportion of the copolymer (B) is from 20 to 55 wt %.
13. The resin film according to claim 1 , wherein the content of the other hydroxyalkanoate units in the copolymer (B) is from 24 mol % to 50 mol %.
14. The resin film according to claim 1 , wherein the content of the other hydroxyalkanoate units in the copolymer (B) is from 24 mol % to 35 mol %.
15. The resin film according to claim 1 , wherein the content of the other hydroxyalkanoate units in the copolymer (B) is from 24 mol % to 30 mol %.
16. The resin film according to claim 1 , wherein in the poly(3-hydroxyalkanoate) resin component, the proportion of the copolymer (A) is from 35 wt % to 49 wt %, and the proportion of the copolymer (B) is from 51 wt % to 65 wt %.