Graphene oxide composite membranes
A system involves interleaving high aspect ratio, rod-like aldehyde-modified cellulose nanomaterials (ACN) between graphene oxide (GO) sheets and utilizing crosslinkers to create a dense, crosslinked network that is highly permeable and selective to a molecule of interest, especially water and water vapor, and does not delaminate in water. This system, especially when combined with oxidative surface treatment of a membrane support substrate, leads to improved adhesion of the membrane on the substrate.
1 . A separation membrane comprising:
a surface functionalized substrate porous to a molecule of interest; and,
a film of a crosslinked composite deposited on the substrate, the composite comprising 60-99.999 wt % of graphene oxide (GO) and 0.001-40 wt % of an aldehyde-modified cellulose nanomaterial (ACN), all weight percentages based on weight sum of the GO and the ACN.
2 . The membrane of claim 1 , wherein the GO is in the composite in a range of 80-95 wt % and ACN is in the composite in a range of 5-20 wt %.
3 . The membrane of claim 1 , wherein the composite is crosslinked with a diamine.
4 . The membrane of claim 3 , wherein the diamine is 1,2-ethylenediamine.
5 . The membrane of claim 1 , wherein ACN is nanofibers having a length-to-diameter aspect ratio of at least 10:1.
6 . The membrane of claim 5 , wherein the aspect ratio is in a range of 100:1 to 1,000:1.
7 . The membrane of claim 1 , wherein the surface functionalized substrate comprises oxygen-containing species.
8 . The membrane of claim 1 , wherein the surface functionalized substrate has an oxidized surface.
9 . The membrane of claim 8 , wherein the oxidized surface is produced by corona discharge.
10 . The membrane of claim 1 , wherein the substrate comprises a polyolefin.
11 . The membrane of claim 10 , wherein the polyolefin is polyethylene.
12 . The membrane of claim 1 , wherein the molecule of interest is water.
13 . A process for producing a separation membrane as defined in claim 1 , the process comprising:
depositing an uncrosslinked composite comprising the graphene oxide (GO) and the aldehyde-modified cellulose nanomaterial (ACN) on a functionalized surface of the surface functionalized substrate to form a film of the uncrosslinked composite on the substrate; and,
crosslinking the composite to form the film of the crosslinked composite on the substrate.
14 . The process of claim 13 , wherein the uncrosslinked composite is deposited on the substrate by depositing a dispersion of the GO and ACN on the substrate and removing liquid components of the dispersion to form the film of the uncrosslinked composite on the substrate.
15 . The process of claim 14 , wherein the liquid components of the dispersion comprise an aqueous medium, an alcohol or a mixture thereof.
16 . The process of claim 13 , wherein crosslinking is performed with a crosslinker and the crosslinker is used in a mass ratio of crosslinker to GO in a range of 3:10 to 14:10.