Compositions incorporating silica fibers
Embodiments of the invention include articles incorporating fibrous fragments of mats of silica fibers and methods for producing such articles. The fiber mats may be formed via electrospinning of a sol gel produced with a silicon alkoxide reagent, such as tetraethyl ortho silicate, alcohol solvent, and an acid catalyst.
1 . A method of making a composition, the method comprising:
electrospinning a sol-gel to form a non-woven mat of silica fibers;
coating at least a portion of the mat with a liquid composition or immersing at least a portion of the mat within a liquid composition; and
curing the liquid composition.
2 . The method of claim 1 , wherein the liquid composition comprises a paint, an epoxy, a urethane, or an adhesive.
3 . The method of claim 1 , wherein the sol-gel is prepared with tetraethylorthosilicate (TEOS).
4 . The method of claim 1 , further comprising, prior to electrospinning the sol-gel, producing the sol-gel from an initial sol comprising 70% to 90% TEOS by weight, 8% to 25% ethanol by weight, an acid catalyst, and water.
5 . The method of claim 4 , wherein the initial sol is free of inorganic salts.
6 . The method of claim 4 , wherein producing the sol-gel comprises ripening the initial sol for at least 2 days at a humidity of 40% to 80% and a temperature of 50° F. to 90° F.
7 . The method of claim 6 , wherein the initial sol is ripened for at least 3 days.
8 . The method of claim 6 , wherein the sol-gel is electrospun when the weight of the sol-gel ranges from 10% to 60% of a starting weight of the initial sol prior to ripening.
9 . The method of claim 6 , wherein the sol-gel is electrospun when production of ethylene vapor therefrom ranges from 10% to 40% relative to the initial sol prior to ripening.
10 . The method of claim 4 , wherein the initial sol is not exposed to a temperature of over 150° F. before or during production of the sol-gel.
11 . The method of claim 4 , wherein the initial sol is not exposed to a temperature of over 100° F. before or during production of the sol-gel.
12 . The method of claim 4 , wherein producing the sol-gel from the initial sol comprises ripening the initial sol within an enclosure, the enclosure comprising, for controlling an atmosphere within the enclosure during ripening of the initial sol, (i) a humidity sensor and a humidifier configured to control humidity within the enclosure, and (ii) a vent and a fan configured to draw gases away from the initial sol.
13 . The method of claim 12 , wherein the humidifier is configured to control the humidity within the enclosure to a level of 40% to 80%.
14 . The method of claim 1 , wherein the liquid composition is a paint, the paint comprising a binder, one or more diluents, and one or more pigments or dyes.
15 . The method of claim 1 , wherein, prior to electrospinning, the sol-gel is not exposed to a temperature of over 150° F.
16 . The method of claim 1 , wherein, prior to electrospinning, the sol-gel is not exposed to a temperature of over 100° F.
17 . The method of claim 1 , wherein the liquid composition comprises a silica fiber powder therewithin.
18 . The method of claim 17 , further comprising forming the silica fiber powder by:
electrospinning a second sol-gel to form a second non-woven mat of silica fibers; and
fragmenting the second mat to form the silica fiber powder.
19 . The method of claim 18 , further comprising, prior to electrospinning the second sol-gel, producing the second sol-gel from a second initial sol comprising 70% to 90% tetraethylorthosilicate (TEOS) by weight, 8% to 25% ethanol by weight, an acid catalyst, and water.
20 . The method of claim 19 , wherein the second initial sol is free of inorganic salts.