Coated nickel-rich ternary material, preparation method and application thereof
The present disclosure belongs to the field of battery materials, and discloses a coated nickel-rich ternary material and a preparation method and application thereof. The coated nickel-rich ternary material has a chemical formula of LiNi x Co y Mn z O 2 ·a[M 3 (PO 4 ) 2 ·bH 2 O], Where 0.6≤x≤0.8, 0.1≤y≤0.2, 0.1≤z≤0.2, x+y+z=1, 0.01≤a≤0.03, 3≤b≤8, M 3 (PO 4 ) 2 ·bH 2 O is at least one selected from the group consisting of nickel phosphate, cobalt phosphate and manganese phosphate; the coated nickel-rich ternary material has a flower-like structure. The preparation method of the present disclosure provides phosphate ions through the prepared phosphate solution, performs coating in a liquid phase environment, and synthesizes the precursor simultaneously by microwave hydrothermal synthesis, which is beneficial to the full contact between the phosphates and the precursor, and ensures the surface of the nickel-rich ternary precursor is uniformly coated with the phosphates. The method is simple and has good coating effect.
1 . A coated nickel-rich ternary material, wherein the coated nickel-rich ternary material has a chemical formula of LiNi x Co y Mn z O 2 ·a[M 3 (PO 4 ) 2 ·bH 2 O], wherein 0.6≤x≤0.8, 0.1≤y≤0.2, 0.1≤z≤0.2, x+y+z=1, 0.01≤a≤0.03, 3≤b≤8; said M 3 (PO 4 ) 2 ·bH 2 O is at least one selected from the group consisting of nickel phosphate, cobalt phosphate and manganese phosphate; the coated nickel-rich ternary material has a flower-like structure, and is a phosphate-coated nickel-rich ternary material; and a method for preparing the coated nickel-rich ternary material comprises the following steps:
(1) dissolving a nickel source, a cobalt source, and a manganese source in a solvent to obtain solution A, adding and mixing a surfactant with the solution A to obtain solution B, wherein the nickel source is at least one selected from the group consisting of a sulfate of nickel, a nitrate of nickel, and an acetate of nickel; the cobalt source is at least one selected from the group consisting of a sulfate of cobalt, a nitrate of cobalt, and an acetate of cobalt; the manganese source is at least one selected from the group consisting of a sulfate of manganese, a nitrate of manganese, and an acetate of manganese;
(2) mixing a solution of a phosphate salt with the solution B to obtain a mixture, subjecting the mixture to a microwave hydrothermal treatment to obtain precipitate C, wherein the microwave hydrothermal treatment is carried out at a temperature of 140° C.-220° C. for 10-20 minutes;
(3) washing the precipitate C with water, followed by drying and grinding the precipitate C to obtain coated nickel-rich ternary precursor powder D; and
(4) mixing the coated nickel-rich ternary precursor powder D with a lithium source to obtain a mixture, followed by subjecting the mixture to calcinating, grinding and screening to obtain the coated nickel-rich ternary material.
2 . The coated nickel-rich ternary material according to claim 1 , wherein a first reversible capacity of the coated nickel-rich ternary material is 173-195 mAh/g at a current of 0.1 C; a surface area of the coated nickel-rich ternary material is 27-38 m 2 /g.
3 . A lithium battery comprising the coated nickel-rich ternary material according to claim 2 .
4 . The coated nickel-rich ternary material according to claim 1 , wherein in step (2), the phosphate salt is at least one selected from the group consisting of ammonium dihydrogen phosphate, diammonium phosphate and ammonium phosphate.
5 . The coated nickel-rich ternary material according to claim 1 , wherein the calcinating is carried out at a temperature of 600° C.-900° C. for 8-16 h.
6 . The coated nickel-rich ternary material according to claim 1 , wherein in step (4), the lithium source is lithium carbonate or lithium hydroxide.
7 . The coated nickel-rich ternary material according to claim 1 , wherein in step (4), a molar ratio of lithium in the lithium source to a total amount of metal elements in the coated nickel-rich ternary precursor powder D is (1-1.1):1.
8 . A lithium battery comprising the coated nickel-rich ternary material according to claim 1 .