Low-temperature processing method for improving 4H—SIC/SIO
Disclosed are a low-temperature processing method for improving a 4H—SiC/SiO 2 interface based on a supercritical oxynitride, and use thereof. The method includes: performing standard cleaning on a silicon carbide sample to be processed; performing dry-oxygen oxidation on the cleaned silicon carbide sample to grow an oxide layer; placing the silicon carbide sample having the oxide layer on a support in a steady-state supercritical chamber; controlling a pressure and injecting nitrogen-oxygen gas into the supercritical device; increasing a temperature in the supercritical device from 23° C. to 500° C.; maintaining the above supercritical state until the processing ends; reducing a temperature of a reactor to room temperature after reaction ends, reducing the pressure to an atmospheric pressure, and taking out the reactor. The present disclosure allows for effective and quick decrease in the 4H—SiC/SiO 2 interface state density, and also a significant decrease in the processing temperature.
1 . A low-temperature processing method for improving a 4H—SiC/SiO 2 interface based on a supercritical oxynitride, the method comprising:
step S1 of placing a silicon carbide sample with an oxide layer into a steady-state supercritical chamber;
step S2 of sealing the steady-state supercritical chamber and injecting nitrogen-oxygen gas into the steady-state supercritical chamber, and controlling an initial pressure;
step S3 of performing temperature- and pressure-increasing processing on the steady-state supercritical chamber; and
step S4 of maintaining a temperature and a pressure at which the temperature- and pressure-increasing processing is performed in step S3 until reaction completes, reducing the pressure to an atmospheric pressure, and taking out the sample, to complete low-temperature processing,
wherein in step S2, a content of the nitrogen-oxygen gas is greater than or equal to 10% of a volume of a reactor of the steady-state supercritical chamber, and the initial pressure ranges from 5 MPa to 25 MPa.
2 . The method according to claim 1 , wherein the nitrogen-oxygen gas contains N 2 O and NO, and the remaining gas in the reactor of the steady-state supercritical chamber contains O 2 and N 2 from atmosphere.
3 . The method according to claim 1 , wherein in step S3, the steady-state supercritical chamber has a temperature ranging from 50° C. to 500° C. and an initial pressure ranging from 10 MPa to 100 MPa.
4 . The method according to claim 1 , wherein in step S4, a reaction time in a supercritical state is 1 hour to 5 hours.
5 . The method according to claim 1 , wherein the low-temperature processed 4H—SiC/SiO 2 has an interface state density ranging from 1×10 11 eV −1 cm −2 to 1×10 12 eV −1 cm −2 , a breakdown electric field ranging from 10 MV/cm to 13 MV/cm, and a gate-oxide leakage current density ranging from 1×10 −10 A·cm −2 to 1×10 −8 A·cm −2 .
6 . A low-temperature processing method for improving a 4H—SiC/SiO 2 interface based on a supercritical oxynitride, the method comprising:
performing high-temperature oxidation on an n-type 4H—SiC semiconductor material after standard cleaning, and then placing the n-type 4H—SiC semiconductor material into a reactor of a steady-state supercritical chamber, and injecting nitrogen-oxygen gas into the reactor;
bringing the nitrogen-oxygen gas into a supercritical state by increasing a temperature, wherein a pressure in the reactor increases with an increase of the temperature;
maintaining the supercritical state when a predetermined processing temperature of 50° C. to 500° C. and a predetermined pressure of 10 MPa to 100 MPa are reached, until a reaction ends; and
lowering the temperature until the pressure is reduced to an atmospheric pressure, and taking out a processed sample,
wherein a content of the nitrogen-oxygen gas is greater than or equal to 10% of a volume of the reactor of the steady-state supercritical chamber, and an initial pressure in the reactor ranges from 5 MPa to 25 MPa.