Polysaccharide aldehydes prepared by oxidation method and used as strength additives in papermaking
View Patent ↗Polysaccharide aldehydes are prepared using selective oxidation involving the use of nitroxyl radical mediated aqueous oxidation with a limited amount of oxidant and defined reaction conditions. These polysaccharide aldehyde derivatives having maximum effective aldehyde and minimal carboxylic acid levels making them especially useful as wet, temporary wet and dry strength additives for paper.
1. A method of making paper having wet strength, temporary wet strength, and dry strength, the steps for making paper comprising:
oxidizing polysaccharide in an aqueous solution with an oxidant having an equivalent oxidizing power of up to about 14.18 g of active chlorine per mole of polysaccharide anhydrosugar unit (“ASU”) and an effective mediating amount of a nitroxyl radical,
carrying out the reaction at a temperature of at or less than about 15° C. and a pH of from about 8.0 to about 10.5,
wherein the resulting polysaccharide aldehyde derivative has up to about 15 mole % of C-6 aldehyde groups per mole of polysaccharide ASU and aldehyde to carboxylic acid ratios of greater than or equal to 0.5 based on moles of polysaccharide ASU of each functionality, and
adding as a strength aid to the paper an effective amount of the polysaccharide aldehyde derivative.
2. The method of making paper of claim 1 wherein the polysaccharide aldehyde derivatives are starch aldehyde derivatives.
3. The method of making paper of claim 1 wherein the polysaccharide is starch.
4. The method of claim 1 wherein the nitroxyl radical has the formula:
Y is selected from the group consisting of H, OH and NH—C(O)—CH3; and
R 1 , R 2 , R 3 and R 4 represent the same or different alkyl groups of 1 to 18 carbon atoms.
5. The method of claim 1 wherein the oxidant has an oxidizing power of from about 0.35 to about 14.18 g of active chlorine per mole of polysaccharide ASU.
6. The method of claim 5 wherein the oxidant has an oxidizing power of from about 1.77 to about 7.09 g of active chlorine per mole of polysaccharide ASU.
7. The method of claim 1 wherein the oxidant is sodium hypochlorite or sodium hypobromite.
8. The method of claim 7 wherein the oxidant is sodium hypochlorite and added in a limited amount of up to about 40 mole % based on the moles of polysaccharide ASU.
9. The method of claim 8 wherein the sodium hypochlorite is added in a limited amount of from about 5 to about 20 mole % based on the moles of polysaccharide ASU.
10. The method of claim 1 wherein the polysaccharide is modified with a cationic group.
11. The method of claim 1 wherein from about 1 to about 40 mole % of oxidant is used, the reaction temperature is from about 0 to about 15° C. and the PH is from about 8 to about 10.5.
12. The method of claim 11 wherein from about 5 to about 20 mole % of oxidant is used, the reaction temperature is from about 5 to about 10° C. and the PH is from about 9 to about 10.
13. The method of claim 1 wherein the oxidizing step is carried out in a granular state.
14. The method of claim 13 wherein the oxidizing step is performed at up to about 40% solids.
15. The method of claim 1 wherein the oxidizing step is carried out in a solution state.
16. The method of claim 15 wherein the oxidizing step is performed at up to about 30% solids.
17. Paper comprising a polysaccharide aldehyde derivative formed by an oxidation reaction and having up to about 15 mole % of C-6 aldehyde groups per mole of polysaccharide ASU and aldehyde to carboxylic acid ratios of greater than or equal to 0.5 based on moles of polysaccharide ASU of each functionality produced by the method of claim 1 .
18. Paper produced by the method of claim 17 wherein the polysaccharide aldehyde derivatives are starch aldehyde derivatives and the polysaccharide is starch.
19. A method of making paper having wet strength, temporary wet strength, and dry strength, the method of making paper comprising the step of:
adding as a strength aid to the paper an effective amount of an amphoteric polysaccharide aldehyde derivative formed by an oxidation reaction using an effective mediating amount of a nitroxyl radical and having from about 0.5 to about 25 mole % of cationic groups based on moles of polysaccharide anhydrosugar unit, from about 1 to about 15 mole % of C-6 aldehyde content based on moles of polysaccharide anhydrosugar unit, and from about 0 to about 20 mole % of carboxylic acid content based on moles of polysaccharide anhydrosugar unit.
20. Paper comprising as a strength aid an amphoteric polysaccharide aldehyde derivative formed by an oxidation reaction using an effective mediating amount of a nitroxyl radical and having from about 0.5 to about 25 mole % of cationic groups based on moles of polysaccharide anhydrosugar unit, from about 1 to about 15 mole % of C-6 aldehyde content based on moles of polysaccharide anhydrosugar unit, and from a 0 to about 20 mole % of carboxylic acid content based on moles of polysaccharide anhydrosugar unit.