Hydrogenated polymer and process for producing the same
The present invention relates to a hydrogenated polymer which is a hydrogenation product of a conjugated diene polymer having an average vinyl bond content of 20% by weight or more and less than 50% by weight and a weight average molecular weight of 60,000 to 600,000 to a degree such that 85% or more of the residual double bonds in the conjugated diene units are hydrogenated, and which has a molecular weight and a number of terminal methyl group carbons as measured by GPC/FTIR analysis satisfying relationship (1): Va−Vb ≧0.03 Vc (1) wherein Va, Vb and Vc represent the number of terminal methyl group carbon atoms per 1000 carbon atoms contained in a polymer whose molecular weight is twice the peak top molecular weight, half the peak top molecular weight, and the peak top molecular weight, respectively.
1. A hydrogenated polymer which is a hydrogenation product of a conjugated diene polymer having an average vinyl bond content of 20% by weight or more and less than 50% by weight and a weight average molecular weight of 60,000 to 600,000 to a degree such that 85% or more of residual double bonds in the conjugated diene units are hydrogenated, and which has a molecular weight and a number of carbon atoms of terminal methyl groups as measured by GPC/FTIR analysis satisfying relationship (1)
Va−Vb ≧0.03 Vc (1)
wherein Va, Vb and Vc represent the number of terminal methyl group carbon atoms per 1000 carbon atoms contained in a polymer whose molecular weight is twice the peak top molecular weight, half the peak top molecular weight, and the peak top molecular weight, respectively.
2. The hydrogenated polymer according to claim 1 , which has a molecular weight distribution of 1.2 to 6 as obtained by GPC analysis.
3. The hydrogenated polymer according to claim 1 , which has a melt flow ratio of 3 or greater.
4. The hydrogenated polymer according to claim 1 , wherein said conjugated diene polymer is polybutadiene.
5. A process for producing a hydrogenated polymer comprising continuously polymerizing a conjugated diene compound or a combination of a conjugated diene compound and an aromatic vinyl compound using an organic alkali metal compound as a polymerization initiator in the presence of a vinyl content modifier, followed by hydrogenation reaction,
wherein the amount of said vinyl content modifier is varied with respect to said organic alkali metal compound in the step of continuously polymerizing the conjugated diene compound or a combination of the conjugated diene compound and the aromatic vinyl compound so as to obtain a hydrogenated polymer having a molecular weight and a number of carbon atoms of terminal methyl groups as measured by GPC/FTIR analysis satisfying relationship (1)
Va−Vb ≧0.03 Vc (1)
wherein Va, Vb and Vc represent the number of terminal methyl group carbon atoms per 1000 carbon atoms contained in a polymer whose molecular weight is twice the peak top molecular weight, half the peak top molecular weight, and the peak top molecular weight, respectively.
6. A polymer composition comprising (a) 1 to 99 parts by weight of a hydrogenated polymer according to claim 1 and (b) 99 to 1 parts by weight of (b-1) a thermoplastic resin and/or (b-2) a rubbery polymer, the total amount of said components (a) and (b) taken as 100 parts by weight.
7. The hydrogenated polymer according to claim 1 , having bonded thereto an atomic group containing at least one polar group.
8. The hydrogenated polymer according to claim 1 , having bonded thereto an atomic group containing at least one polar group selected from a hydroxyl group, a carboxyl group, a carbonyl group, a thiocarbonyl group, an acid anhydride group, an amido group, an amino group, an imino group, an epoxy group, a thioepoxy group, an isocyanate group, an isothiocyanate group, a silicon halide group and an alkoxysilicon group.
9. The hydrogenated polymer according to claim 8 , wherein said atomic group containing at least one polar group is connected to an end of its polymeric chain.
10. The hydrogenated polymer according to claim 1 , having bonded thereto an α, β-unsaturated carboxylic acid or a derivative thereof.
11. A polymer composition comprising (a) 1 to 99 parts by weight of a hydrogenated polymer according to any one of claims 7 to 10 and (b) 99 to 1 parts by weight of (b-1) a thermoplastic resin and/or (b-2) a rubbery polymer, the total amount of said components (a) and (b) taken as 100 parts by weight.