Two-component coating composition and method of preparation
Aqueous coating compositions containing (1) a first polymer containing reactive functional groups with a selected level of carboxylic acid functionality and (2) a polyfunctional crosslinker agent containing functional groups that are reactive with appropriate functional groups of the first polymer, are disclosed. The two-component polymer compositions provide a combination of durability and ready removability of the final coating after curing. Two-component polymer compositions based on the first polymer containing hydroxyl functionality in addition to carboxylic acid functionality and use of a polyisocyanate as the polyfunctional crosslinker agent are especially useful as floor polish compositions.
1. An aqueous coating composition comprising:
(1) a first polymer comprising, as polymerized units:
(a) 16 to 25 percent, based on the weight of the first polymer, of a monoethylenically unsaturated monomer containing an acidic functional group selected from one or more of carboxylic, sulfonic and phosphonic groups; and
(b) zero up to 60 percent, based on the weight of the first polymer, of a (meth)acrylic monomer containing one or more pendant reactive functional groups selected from hydroxy, thiol and amino groups; and
(c) zero up to 70 percent, based on the weight of the first polymer, of one or more vinyl aromatic monomers; and
(d) 15 to 90 percent, based on the weight of the first polymer, of one or more (C 1 -C 20 ) alkyl (meth)acrylate ester monomers; and
(e) zero up to 10 percent, based on the weight of the first polymer, of one or more other copolymerizable monomers;
(1) a polyfunctional crosslinker agent comprising pendant functional groups selected from one or more of isocyanate, carbodiimide, aziridinyl and epoxy groups;
(2) 0.1 to 15 percent, based on the weight of the aqueous coating composition, of coalescing agent;
(3) zero up to 10 percent, based on the weight of the aqueous coating composition, of additives selected from one or more of waxes, surfactants, defoamers, leveling agents, alkali-soluble resins and plasticizers; and
(4) 50 to 99 percent, based on the weight of the aqueous coating composition, of water;
wherein: the first polymer has a number average molecular weight from grteater than 50,000 up to 2,000,000; the polyfunctional crosslinker agent is used in an amount sufficient to provide from 0.2 to 5 equivalents of pendant functional groups per equivalent of corresponding pendant reactive functional groups in the first polymer; the combined amount of (1) and (2) is from 10 to 90 percent, based on the weight of the aqueous coating composition; and the sum of (1), (2), (3), (4) and (5) percents add up to 100 percent.