Carbonaceous materials coated with a metal or metal oxide, a preparation method thereof, and a composite electrode and lithium secondary battery comprising the same
View Patent ↗A carbon anode active material for lithium secondary battery comprising a cluster or thin film layer of a metal or metal oxide coated onto the surface of the carbon active material, a preparation method thereof, and a metal-carbon hybrid electrode and a lithium secondary battery comprising the same. The carbon active material is prepared through a gas suspension spray coating method. An electrode comprising the carbon active material according to the present invention shows excellent conductivity, high rate charge/discharge characteristics, cycle life characteristics and electrode capacity close to theoretical value.
1. A preparation method of a carbon active material for a lithium secondary batter, which comprises a thin film or a cluster layer of a metal or metal oxide coated onto the surface of the carbon at a thickness of 1-300 nm, comprising the steps of:
(a) floating carbon particles in a gas at a temperature below 100° C.;
(b) coating a metal salt onto the carbon particles by spraying a solution of the metal salt to the layer of the floated carbon particles; and
(c) heating the metal salt coated-carbon particles under a gas atmosphere selected from the group consisting of hydrogen, nitrogen and argon at a temperature of 200-800° C., thereby to obtain a metal or metal oxide-coated carbon active material.
2. The method according to claim 1 , wherein the metal or metal oxide is selected from the group consisting of Li, Al, Sn, Bi, Si, Sb, Ni, Cu, Ti, V, Cr, Mn, Fe, Co, Ag, and alloys and oxides thereof.
3. The method according to claim 1 , the metal salt is selected from the group consisting of nitrates and chlorides of Li, Al, Sn, Bi, Si, Sb, Ni, Cu, Ti, V, Cr, Mn, Fe, Co and Ag, CH 3 CO 2 Li, (CH 3 ) 3 Al, (C 2 H 5 ) 3 Al, (C 4 H 9 ) 3 Al, (CH 3 ) 3 Bi, (C 2 H 5 ) 3 Sb, (C 3 H 7 ) 3 Sb, CF 3 CO 2 Ag, CH 3 CO 2 Ag, (C 2 H 5 O) 4 Si, (C 2 H 5 ) 3 SiH, (CH 3 ) 4 Sn, (C 2 H 5 ) 4 Sn, Cu(hfac) 2 , Cu(acac), Cu(DPM), (hfac)Cu(I)MP and (Hfac)Cu(I)(DMB).
4. The method according to claim 1 , wherein a solvent for the solution of the metal salt is water, a mixture of water and an alcohol, a mixture of water and acetone and a mixture of water, an alcohol and acetone.
5. The method according to claim 1 , wherein the carbon particle is graphite, cokes or hard carbon.
6. A carbon anode, comprising the carbon active material prepared by the method of claim 1 .
7. A lithium secondary battery, comprising an anode comprising the carbon active material prepared by the method of claim 4 and a cathode selected from the group consisting of LiCoO 2 , LiMn 2 O 4 , LiNiO 2 , V 2 O 5 and V 6 O 13 .