Process and apparatus for producing single-walled carbon nanotubes
View Patent ↗A process and apparatus for catalytic production of single walled carbon nanotubes. Catalytic particles are exposed to different process conditions at successive stages wherein the catalytic particles do not come in contact with reactive (catalytic) gases until preferred process conditions have been attained, thereby controlling the quantity and form of carbon nanotubes produced. The reaction gas is preferably provided at a high space velocity to minimize CO 2 build-up. The process also contemplates processes and apparatus which recycle and reuse the gases and catalytic particulate materials, thereby maximizing cost efficiency, reducing wastes, reducing the need for additional raw materials, and producing the carbon nanotubes, especially SWNTs, in greater quantities and for lower costs.
1. A process for producing single-walled carbon nanotubes, comprising:
disposing catalytic particles into a reactor wherein the catalytic particles comprise a support-material and a catalytic material, the catalytic particles effective in catalyzing the conversion of a carbon-containing gas into single-walled carbon nanotubes;
removing air from the catalytic particles by exposing the catalytic particles to a heated inert gas;,
reducing the catalytic particles by exposing the catalytic particles to a heated reducing gas forming reduced catalytic particles; and
catalytically forming single-walled carbon nanotubes by exposing the reduced catalytic particles to a carbon-containing gas for a duration of time and at a temperature sufficient to cause catalytic production of single-walled carbon nanotubes thereby forming reacted catalytic particles bearing the single-walled carbon nanotubes.
2. The process of claim 1 wherein the catalytic material comprises cobalt and molybdenum.
3. The method process of claim 1 wherein the inert gas comprises a gas selected from the group consisting of He, Ar, and N 2 .
4. The method process of claim 1 wherein the carbon-containing gas comprises a gas selected from the group consisting of CO, CH 4 , C 2 H 4 , C 2 H 2 , or mixtures thereof.
5. The method process of claim 1 wherein the support material is selected from the group consisting of SiO 2 , Al 2 O 3 , MgO, ZrO 2 , zeolites, MCM-41, and Mg(Al)O.
6. The method process of claim 1 wherein the catalytic material comprises at least one of the metals selected from the group consisting of Co, Mo, Ni, Fe, W, or Nb.
7. The method process of claim 1 wherein the catalytic material comprises a Group VIII metal selected from the group consisting of Co, Ni, Ru, Rh, Pd, Ir, Fe, Pt, and mixtures thereof, and a Group VIb metal selected from the group consisting of Cr, Mo, W, and mixtures thereof and/or a Group Vb metal selected from the group consisting of V, Nb and Ta, and mixtures thereof.
8. The process of claim 1 wherein the reaction temperature is about 700° C. to about 1000° C.
9. The process of claim 1 wherein the reaction temperature is about 750° C. to about 950° C.
10. The process of claim 1 wherein the carbon-containing gas comprises carbon monoxide, a saturated aliphatic hydrocarbon, an unsaturated aliphatic hydrocarbon, an oxygenated hydrocarbon, an alcohol, and/or an aromatic hydrocarbon.
11. The process of claim 10 wherein the carbon-containing gas further comprises a diluent gas.
12. A process for producing single-walled carbon nanotubes, comprising:
disposing catalytic particles into a reactor wherein the catalytic particles comprise a support material and a catalytic material, the catalyst effective in catalyzing the conversion of a carbon-containing gas into carbon nanotubes;
treating the catalytic particles with a reduction process;
heating the catalytic particles to a reaction temperature; and
catalytically forming single-walled carbon nanotubes by exposing the catalytic particles to a carbon-containing gas for a duration of time and at a temperature sufficient to cause catalytic production of the single-walled carbon nanotubes thereby forming reacted catalytic particles bearing the single-walled carbon nanotubes.
13. The process of claim 12 wherein the catalytic material comprises cobalt and molybdenum.
14. The process of claim 12 wherein the step of heating the catalytic particles comprises exposing the catalytic particles to a heated inert gas.
15. The process of claim 12 further comprising the step of flushing the carbon-containing gas from the reacted catalytic particles.
16. The process of claim 12 further comprising the step of cooling the reacted catalytic particles.
17. The process of claim 12 further comprising the step of removing amorphous carbon from the reacted catalytic particles and treating the reacted catalytic particles to obtain the single-walled carbon nanotubes.
18. The process of claim 12 wherein the catalytic material is a metallic catalyst.
19. The process of claim 12 wherein the reaction temperature is about 700° C. to about 1000° C.
20. The process of claim 12 wherein the reaction temperature is about 750° C. to about 950° C.
21. The process of claim 12 wherein the carbon-containing gas comprises carbon monoxide, a saturated aliphatic hydrocarbon, an unsaturated aliphatic hydrocarbon, an oxygenated hydrocarbon, an alcohol, and/or an aromatic hydrocarbon.
22. The process of claim 12 wherein the carbon-containing gas further comprises a diluent gas.
23. The process of claim 12 comprising the additional step of treating the reacted catalytic particles to obtain the single-walled carbon nanotubes.
24. A process for producing single-walled carbon nanotubes, comprising:
disposing catalytic particles into a reactor wherein the catalytic particles comprise a support material and a catalytic material comprising Co and Mo;
heating the catalytic particles to a reaction temperature wherein the reaction temperature is about 750° C. to about 950° C.; and
catalytically forming single-walled carbon nanotubes by exposing the catalytic particles to a carbon-containing gas for a duration of time and at a temperature sufficient to cause catalytic production of the single-walled carbon nanotubes thereby forming reacted catalytic particles bearing the single-walled carbon nanotubes.
25. A process for producing single-walled carbon nanotubes, comprising:
disposing catalytic particles into a reactor wherein the catalytic particles comprise a support material and a catalytic material;
treating the catalytic particles with a reduction process;
heating the catalytic particles to a reaction temperature wherein the reaction temperature is about 750° C. to about 950° C.; and
catalytically forming single-walled carbon nanotubes by exposing the catalytic particles to a carbon-containing gas for a duration of time and at a temperature sufficient to cause catalytic production of the single-walled carbon nanotubes thereby forming reacted catalytic particles bearing the single-walled carbon nanotubes.
26. A process for producing single-walled carbon nanotubes, comprising:
disposing catalytic particles into a reactor wherein the catalytic particles comprise a support material and a catalytic material;
heating the catalytic particles to a reaction temperature wherein the reaction temperature is about 750° C. to about 950° C., and
wherein the catalytic particles are heated by exposing the catalytic particles to a heated inert gas; and
catalytically forming single-walled carbon nanotubes by exposing the catalytic particles to a carbon-containing gas for a duration of time and at a temperature sufficient to cause catalytic production of the single-walled carbon nanotubes thereby forming reacted catalytic particles bearing the single-walled carbon nanotubes.
27. A process for producing single-walled carbon nanotubes, comprising:
disposing catalytic particles into a reactor wherein the catalytic particles comprise a support material and a catalytic material;
heating the catalytic particles to a reaction temperature wherein the reaction temperature is about 750° C. to about 950° C.;
catalytically forming single-walled carbon nanotubes by exposing the catalytic particles to a carbon-containing gas for a duration of time and at a temperature sufficient to cause catalytic production of the single-walled carbon nanotubes thereby forming reacted catalytic particles bearing the single-walled carbon nanotubes; and
flushing the carbon-containing gas from the reacted catalytic particles.
28. A process for producing single-walled carbon nanotubes, comprising:
disposing catalytic particles into a reactor wherein the catalytic particles comprise a support material and a catalytic material;
heating the catalytic particles to a reaction temperature wherein the reaction temperature is about 750° C. to about 950° C.;
catalytically forming single-walled carbon nanotubes by exposing the catalytic particles to a, carbon-containing gas for a duration of time and at a temperature sufficient to cause catalytic production of the single-walled carbon nanotubes thereby forming reacted catalytic particles bearing the single-walled carbon nanotubes; and
removing amorphous carbon from the reacted catalytic particles to obtain the single-walled carbon nanotubes.
29. A process for producing single-walled carbon nanotubes, comprising:
disposing catalytic particles into a reactor wherein the catalytic particles comprise a support material and a catalytic material;
heating the catalytic particles to a reaction temperature wherein the reaction temperature is about 750° C. to about 950° C.; and
catalytically forming single-walled carbon nanotubes by exposing the catalytic particles to a carbon-containing gas for a duration of time and at a temperature sufficient to cause catalytic production of the single-walled carbon nanotubes thereby forming reacted catalytic particles bearing the single-walled carbon nanotubes, wherein the carbon-containing gas further comprises a diluent gas.
30. A process for producing single-walled carbon nanotubes, comprising:
disposing catalytic particles into a reactor wherein the catalytic particles comprise a support material and a catalytic material;
heating the catalytic particles to a reaction temperature wherein the reaction temperature is about 750° C. to about 950° C.;
catalytically forming single-walled carbon nanotubes by exposing the catalytic particles to a carbon-containing gas for a duration of time and at a temperature sufficient to cause catalytic production of the single-walled carbon nanotubes thereby forming reacted catalytic particles bearing the single-walled carbon nanotubes; and
treating the reacted catalytic particles to obtain the single-walled carbon nanotubes.
31. A process for producing single-walled carbon nanotubes, comprising:
disposing catalytic particles into a reactor wherein the catalytic particles comprise a support material and a catalytic material comprising Co and Mo;
heating the catalytic particles to a reaction temperature; and
catalytically forming single-walled carbon nanotubes by exposing the catalytic particles to a carbon-containing gas for a duration of time and at a temperature sufficient to cause catalytic production of the single-walled carbon nanotubes thereby forming reacted catalytic particles bearing the single-walled carbon nanotubes, and wherein the carbon-containing gas comprises carbon monoxide, a saturated aliphatic hydrocarbon, an unsaturated aliphatic hydrocarbon, an oxygenated hydrocarbon, an alcohol, and/or an aromatic hydrocarbon.
32. A process for producing single-walled carbon nanotubes, comprising:
disposing catalytic particles into a reactor wherein the catalytic particles comprise a support material and a catalytic material;
treating the catalytic particles with a reduction process;
heating the catalytic particles to a reaction temperature; and
catalytically forming single-walled carbon nanotubes by exposing the catalytic particles to a carbon-containing gas for a duration of time and at a temperature sufficient to cause catalytic production of the single-walled carbon nanotubes thereby forming reacted catalytic particles bearing the single-walled carbon nanotubes, and wherein the carbon-containing gas comprises carbon monoxide, a saturated aliphatic hydrocarbon, an unsaturated aliphatic hydrocarbon, an oxygenated hydrocarbon, an alcohol, and/or an aromatic hydrocarbon.
33. A process for producing single-walled carbon nanotubes, comprising:
disposing catalytic particles into a reactor wherein the catalytic particles comprise a support material and a catalytic material;
heating the catalytic particles to a reaction temperature by exposing the catalytic particles to a heated inert gas; and
catalytically forming single-walled carbon nanotubes by exposing the catalytic particles to a carbon-containing gas for a duration of time and at a temperature sufficient to cause catalytic production of the single-walled carbon nanotubes thereby forming reacted catalytic particles bearing the single-walled carbon nanotubes, and wherein the carbon-containing gas comprises carbon monoxide, a saturated aliphatic hydrocarbon, an unsaturated aliphatic hydrocarbon, an oxygenated hydrocarbon, an alcohol, and/or an aromatic hydrocarbon.
34. A process for producing single-walled carbon nanotubes, comprising:
disposing catalytic particles into a reactor wherein the catalytic particles comprise a support material and a catalytic material;
heating the catalytic particles to a reaction temperature; and
catalytically forming single-walled carbon nanotubes by exposing the catalytic particles to a carbon-containing gas for a duration of time and at a temperature sufficient to cause catalytic production of the single-walled carbon nanotubes thereby forming reacted catalytic particles bearing the single-walled carbon nanotubes, and wherein the carbon-containing gas comprises carbon monoxide, a saturated aliphatic hydrocarbon, an unsaturated aliphatic hydrocarbon, an oxygenated hydrocarbon, an alcohol and/or an aromatic hydrocarbon, and flushing the carbon-containing gas from the reacted catalytic particles.
35. A process for producing single-walled carbon nanotubes, comprising:
disposing catalytic particles into a reactor wherein the catalytic particles comprise a support material and a catalytic material;
heating the catalytic particles to a reaction temperature;
catalytically forming single-walled carbon nanotubes by exposing the catalytic particles to a carbon-containing gas for a duration of time and at a temperature sufficient to cause catalytic production of the single-walled carbon nanotubes thereby forming reacted catalytic particles bearing the single-walled carbon nanotubes, and wherein the carbon-containing gas comprises carbon monoxide, a saturated aliphatic hydrocarbon, an unsaturated aliphatic hydrocarbon, an oxygenated hydrocarbon, an alcohol, and/or an aromatic hydrocarbon; and
removing amorphous carbon from the reacted catalytic particles and treating the reacted catalytic particles to obtain the single-walled carbon nanotubes.
36. A process for producing single-walled carbon nanotubes, comprising:
disposing catalytic particles into a reactor wherein the catalytic particles comprise a support material and a catalytic material;
heating the catalytic particles to a reaction temperature; and
catalytically forming single-walled carbon nanotubes by exposing the catalytic particles to a carbon-containing gas for a duration of time and at a temperature sufficient to cause catalytic production of the single-walled carbon nanotubes thereby forming reacted catalytic particles bearing the single-walled carbon nanotubes, and wherein the carbon-containing gas comprises carbon monoxide, a saturated aliphatic hydrocarbon, an unsaturated aliphatic hydrocarbon, an oxygenated hydrocarbon, an alcohol, and/or an aromatic hydrocarbon and wherein the carbon-containing gas further comprises a diluent gas.
37. A process for producing single-walled carbon nanotubes, comprising:
disposing catalytic particles into a reactor wherein the catalytic particles comprise a support material and a catalytic material;
heating the catalytic particles to a reaction temperature;
catalytically forming single-walled carbon nanotubes by exposing the catalytic particles to a carbon-containing gas for a duration of time and at a temperature sufficient to cause catalytic production of the single-walled carbon nanotubes thereby forming reacted catalytic particles bearing the single-walled carbon nanotubes, and wherein the carbon-containing gas comprises carbon monoxide, a saturated aliphatic hydrocarbon, an unsaturated aliphatic hydrocarbon, an oxygenated hydrocarbon, an alcohol, and/or an aromatic hydrocarbon; and treating the reacted catalytic particles to obtain the single-walled carbon nanotubes.