Humidity indicators
Silica-based carrier impregnated with iron(III) or iron(II) salts functions as a humidity indicator giving a yellow/amber to nearly colourless colour change as the carrier humidifies.
1. A humidity indicator comprising a silica gel carrier containing an iron(II) and/or iron(III) salt or salts as an active indicator, the iron salt being a salt containing more than one cation of which one is iron(II) or iron(III) wherein the silica gel carrier changes color when exposed to humidity.
2. An indicator as claimed in claim 1 in which the iron salt is ammonium iron(III) sulphate, ammonium iron(II) sulphate or potassium iron(III) sulphate.
3. An indicator as claimed in claim 1 in which the iron(II) or iron(III) salt is present in an amount in the range 0.01 percent to 2.0 percent by weight expressed as Fe based upon weight of dry carrier.
4. A humidity indicator as claimed in claim 1 in which the silica gel is humidified silica gel.
5. A humidity indicator as claimed in claim 1 in which the silica gel is beaded or granular silica gel.
6. A method of monitoring the humidity level within an atmosphere comprising exposing a dried silica gel carrier containing an iron(II) and/or iron(III) salt or salts to said atmosphere and observing said silica gel carrier for color changes therein, the iron salt being a salt containing more than one cation of which one is iron(II) or iron(III).
7. A method as claimed in claim 6 in which the iron salt is ammonium iron(III) sulphate, ammonium iron(II) sulphate or potassium iron(III) sulphate.
8. A method of producing a humidity indicator comprising soaking silica gel carrier with a solution of an iron(II) and/or iron(III) salt or salts to impregnate the carrier and drying the impregnated carrier, the iron salt being a salt containing more than one cation of which one is iron(II) or iron(III) wherein the dried carrier changes color when exposed to humidity.
9. A humidity indicator in the form of an iron impregnated silica gel carrier produced by the method as claimed in claim 8 .
10. A humidity indicator composition comprising a silica gel carrier containing ferric sulphate wherein said ferric sulphate is present in an amount in the range 0.01 percent to 2.0 percent by weight expressed as Fe based upon weight of dry carrier and wherein said dried carrier changes color when exposed to humidity.
11. A method of monitoring the humidity level within an atmosphere comprising exposing a dried silica gel carrier containing ferric sulphate to said atmosphere and observing color changes therein.
12. A method of producing a colored humidity indicator comprising soaking a silica gel carrier with a solution of iron sulphate to secure impregnation of the carrier and drying the impregnated carrier wherein said iron sulphate is present in an amount in the range of 0.01 percent to 2.0 percent by weight expressed as Fe based upon weight of dry carrier, and wherein said dried carrier changes color when exposed to humidity.
13. A method as claimed in claim 12 in which the color of the indicator is enhanced by pH adjustment to higher values.
14. A method as claimed in claim 13 in which pH adjustment is effected by sodium hydroxide addition.
15. A method as claimed in claim 12 including incorporating into said silica gel carrier an alkali to adjust pH to higher values.
16. A colored humidity indicator compound comprising a silica based carrier containing a simple iron salt as an active indicator and in which the color of said humidity indicator is enhanced by the addition of a base.
17. A compound as claimed in claim 16 in which the iron salt comprises ferric sulphate.
18. A compound as claimed in claim 16 in which the carrier comprises silica gel.
19. A compound as claimed in claim 18 in which the silica gel is humidified silica gel.
20. A compound as claimed in claim 18 in which the silica gel is beaded or granular silica gel.
21. A method of monitoring the humidity level within an atmosphere comprising providing a dried silica based carrier which contains a simple iron salt as a colored indicator and in which the color of the indicator is enhanced by the addition of a base, exposing said carrier to said atmosphere and observing color changes therein.
22. A method as claimed in claim 21 in which the base is sodium hydroxide.
23. A method as claimed in claim 21 in which the iron salt comprises ferric sulphate.