High density alloy for improved mass properties of an article
The present invention is a nickel-tungsten-chromium alloy for an article of manufacture such as a portion of a golf club head ( 20 ). The nickel-tungsten-chromium alloy preferably has a density ranging from 9.0 g/cm 3 to 10.5 g/cm 3 , and a Rockwell Hardness ranging from 50 to 92. The nickel-tungsten-chromium alloy is capable of being investment cast to form the article of manufacture.
1. A method of manufacturing an article, the method comprising:
investment casting the article from a composition comprising 35 to 70 weight percent nickel, 20–35 weight percent tungsten and 10–30 weight percent chromium;
wherein the investment cast article has a density ranging from 9.0 g/cm 3 to 10.5 g/cm 3 , and a Rockwell Hardness ranging from 80 to 92;
wherein the article is a portion of a golf club head comprises a sole wall, a toe wall extending upward from the sole wall at a first end of the sole wall, a hosel extending upward from the sole wall at a second end of the sole wall, and a heel wall extending upward from the sole wall.
2. The method according to claim 1 wherein the composition further comprises 1 weight percent silicon.
3. The method according to claim 1 wherein the portion of a golf club head further comprises a top wall extending from the toe wall to the heel wall.