Process of forming oil-absorbent bodies
A process for forming an oil-sorbent composition of matter with bound combinations of styrene-butadiene-styrene (SBS) and ethylene propylene diene monomer (EPDM) utilizes a low-temperature extrusion process. The SBS, or both materials, may be in the form of multitudes of granules. In certain preferred embodiments, the combination is 10-30% by weight and the SBS is about 30% styrene and manufactured without talc. The composition of matter can be extruded into a solid, compliant body for use in a product for absorbing oil. The material can be extruded, in one preferred embodiment, into an extended cylinder body having an axial hole.
1. A process of forming a solid, compliant body for absorbing oil comprising:
(a) mixing styrene-butadiene-styrene and ethylene propylene diene monomer;
(b) heating the mixture to a temperature below the melting point of the styrene-butadiene-styrene material, wherein the ethylene propylene diene monomer material of the mixture becomes plasticized;
(c) extruding the resulting mixture through a die; and
(d) allowing the extruded mixture to cool and expand.
2. The process of claim 1 wherein part (a) comprises mixing only styrene-butadiene-styrene and ethylene propylene diene monomer.
3. The process of claim 2 wherein part (a) comprises mixing granules of styrene-butadiene-styrene and granules of ethylene propylene diene monomer.
4. The process of claim 1 wherein part (a) comprises mixing granules of styrene-butadiene-styrene with a styrene content of about 30% and without talc.
5. The process of claim 1 wherein part (a) comprises mixing granules of styrene-butadiene-styrene that are sifted to retain particles in the range of about 4-20 mesh with granules of ethylene propylene diene monomer.
6. The process of claim 1 wherein part (a) comprises mechanically agitating the materials in the barrel of an extruder.
7. The process of claim 1 wherein part (b) comprises heating the mixture to a temperature between about 105° F. and 120° F.
8. The process of claim 1 wherein part (c) comprises using a circular die and a central mandrel to form the extruded material into a tubular shape.
9. The process of claim 8 further comprising cutting the extruded mixture into lengths that are longer than the diameter of the circular die.
10. The process of claim 1 wherein air is allowed to remain in the extruded mixture and whereby the expansion of part (d) causes fissures to form in the surfaces of the resulting body.
11. The process of claim 1 wherein the ethylene propylene diene monomer in part (a) is in the range of about 10-30% by weight.
12. A process of forming a plurality of solid, compliant bodies for absorbing oil comprising:
(a) mixing quantities of styrene-butadiene-styrene and ethylene propylene diene monomer;
(b) heating the mixture to a temperature below the melting point of the styrene-butadiene-styrene material, wherein the ethylene propylene diene monomer material of the mixture becomes plasticized;
(c) thereafter extruding the partially plasticized mixture through a die;
(d) thereafter repeatedly cutting the extruded material to form a quantity of bodies; and
(e) thereafter allowing the bodies to cool and expand.
13. The process of claim 12 further comprising placing the resulting bodies in a container.
14. The process of claim 13 wherein placing the resulting bodies in a container comprises placing the resulting bodies in a sack comprised of a mesh material that is porous to both water and oil.
15. The process of claim 12 wherein part (c) comprises using a circular die.
16. The process of claim 15 wherein part (d) comprises creating at least some of the bodies into lengths that are longer than the diameter of the circular die.
17. A process of forming a plurality of solid, compliant bodies for absorbing oil comprising:
(a) mixing a first multitude of granules of styrene-butadiene-styrene and a second multitude of granules of ethylene propylene diene monomer by mechanically agitating the granules in the barrel of an extruder;
(b) heating the mixture to a temperature below the melting point of the styrene-butadiene-styrene material, wherein the ethylene propylene diene monomer material of the mixture becomes plasticized;
(c) thereafter extruding the partially plasticized mixture through a circular die;
(d) thereafter repeatedly cutting the extruded material to form a quantity of bodies that are longer than the diameter of the circular die; and
(e) thereafter allowing the bodies to cool and expand.
18. The process of claim 17 wherein part (a) comprises mixing only the two multitudes and wherein the first multitude has a styrene content of about 30% and lacks talc.
19. The process of claim 17 wherein part (c) comprises using a central mandrel to form the extruded material into a tubular shape.
20. The process of claim 17 wherein air is allowed to remain in the extruded mixture and whereby the expansion of part (d) causes fissures to form in the surfaces of the resulting body.