Coating for rubber gloves
A composition for a damp hand donnable glove using a novel coating. The novel coating results in the formation of domains of variable size and height. The coating has a polyurethane polymer, an aqueous wax dispersion and a surfactant.
1. An aqueous coating composition for coating the interior surface of gloves comprising:
an acrylic polymer dispersion;
a polyurethane latex dispersion; and
an agglomerated polyvinyl chloride latex;
wherein said agglomerated polyvinyl chloride latex forms domains of variable size and height enhancing wet donnability of the gloves.
2. The coating of claim 1 wherein the acrylic polymer is in an amount from about 0.1% to about 10% based on the total coating weight.
3. The coating of claim 1 wherein the polyurethane latex dispersion is in an amount from about 0.1% to about 10% based on the total coating weight.
4. The coating of claim 1 wherein the agglomerated polyvinyl chloride latex is in an amount from about 0.1% to about 10% based on the total coating weight.
5. An aqueous coating composition for coating the interior surface of gloves comprising:
a styrene acrylic emulsion;
an aqueous wax dispersion;
a nonionic surfactant;
an anionic surfactant; and
potassium hydroxide;
wherein said styrene acrylic emulsion and said aqueous wax dispersion form domains of variable size and height enhancing wet donnability of the gloves.
6. The coating of claim 5 wherein the aqueous wax dispersion is a polyethylene wax.
7. The coating of claim 5 wherein the styrene acrylic emulsion is in an amount from about 0.1% to about 10% based on the total coating weight.
8. The coating of claim 5 wherein the aqueous wax dispersion is in an amount from about 0.1% to about 10% based on the total coating weight.
9. The coating of claim 5 wherein the nonionic surfactant is in an amount from about 0.0 1% to about 0.1% based on the total coating weight.
10. The coating of claim 5 wherein the anionic surfactant is in an amount from about 0.01% to about 0.1% based on the total coating weight.
11. The coating of claim 5 wherein the potassium hydroxide is present in an amount from about 0.0 1% to about 1.0% based on the total coating weight.
12. An aqueous coating composition for coating the interior surface of gloves comprising:
a polyurethane latex dispersion;
an aqueous wax dispersion;
a nonionic surfactant;
an anionic surfactant; and
potassium hydroxide;
wherein said polyurethane latex dispersion and said aqueous wax dispersion form domains of variable size and height enhancing wet donnability of the gloves.
13. The coating of claim 12 wherein the aqueous wax dispersion is a polyethylene wax.
14. The coating of claim 12 wherein the polyurethane latex dispersion is in an amount from about 0.1% to about 10% based on the total coating weight.
15. The coating of claim 12 wherein the aqueous wax dispersion is in an amount from about 0.1% to about 10% based on the total coating weight.
16. The coating of claim 12 wherein the nonionic surfactant is in an amount from about 0.01% to about 0.1% based on the total coating weight.
17. The coating of claim 12 wherein the anionic surfactant is in an amount from about 0.01% to about 0.1% based on the total coating weight.
18. The coating of claim 12 wherein the potassium hydroxide is present in an amount from about 0.01% to about 1.0% based on the total coating weight.
19. A process for making a glove with enhanced wet donnability, the process comprising the steps of:
applying a standard coagulant to a clean ceramic former in the shape of a hand;
drying the standard coagulant, thus forming a coagulant coating on the former; dipping the former with the coagulant coating into compounded latex to form a rubber film on the former in the shape of a hand;
leaching the rubber film by dipping the former with the rubber film in water;
dipping the former with leached rubber film in an aqueous coating solution, the coating solution comprising:
a styrene acrylic emulsion,
an aqueous wax dispersion,
a nonionic surfactant,
an anionic surfactant, and
potassium hydroxide,
drying the coated rubber film to promote formation of domains in the coating on the interior surface of the glove; and
curing the coated rubber film to form the glove.
20. A process for making a glove with enhanced wet donnability, the process comprising the steps of:
applying a standard coagulant to a clean ceramic former in the shape of a hand;
drying the standard coagulant, thus forming a coagulant coating on the former;
dipping the former with the coagulant coating into compounded latex to form a rubber film on the former in the shape of a hand;
leaching the rubber film by dipping the former with the rubber film in water;
dipping the former with leached rubber film in an aqueous coating solution, the coating solution comprising:
a polyurethane latex,
an aqueous wax dispersion,
a nonionic surfactant,
an anionic surfactant, and
potassium hydroxide,
drying the coated rubber film to promote formation of domains in the coating on the interior surface of the glove; and
curing the coated rubber film to form the glove.
21. A latex glove having a dry coating made by drying an aqueous coating composition on the interior surface of the glove, the aqueous coating comprising:
an acrylic polymer dispersion;
a polyurethane latex dispersion; and
an agglomerated polyvinyl chloride latex;
wherein said agglomerated polyvinyl chloride latex forms domains of variable size and height enhancing wet donnability of the glove.
22. A latex glove having a dry coating made by drying an aqueous coating composition on the interior surface of the glove, the aqueous coating comprising:
a styrene acrylic emulsion;
an aqueous wax dispersion;
a nonionic surfactant;
an anionic surfactant; and
potassium hydroxide;
wherein said styrene acrylic emulsion and said aqueous wax dispersion form domains of variable size and height enhancing wet donnability of the glove.
23. A latex glove having a dry coating made by drying an aqueous coating composition on the interior surface of the glove, the aqueous coating comprising:
a polyurethane latex dispersion;
an aqueous wax dispersion;
a nonionic surfactant;
an anionic surfactant; and
potassium hydroxide;
wherein said polyurethane latex dispersion and said aqueous wax dispersion form domains of variable size and height enhancing wet donnability of the glove.