Laminates and packaging containers
A laminate has a core layer and a skin layer on either side of the core layer, wherein the skin layer is formed of a copolymer having a glass transition point of 85° C. or more and 115° C. or below and consisting of 2,6-naphthalene dicarboxylic acid or its lower alkyl ester, terephthalic acid or its lower alkyl ester and ethylene glycol or a polymer alloy having a glass transition point of 85° C. or more and 115° C. or below and consisting of polyethylene terephthalate and polyethylene-2,6-naphthalate. Thus, it can be used suitably as a packaging container for food and drink, such as jelly containers, which has flavor resistance and aroma retention sufficient not to be limited by types of flavor used for jelly or the like, excels in sealing properties with a lid body, can be hermetically sealed with an easy-peel transparent lid body, and is also superior in gas barrier properties, impact resistance, heat resistance, cost efficiency and transparency.
1. A laminate having a core layer and a skin layer on either side of the core layer, wherein the skin layer is formed of a copolymer having a glass transition point of 85° C. or more and 115° C. or below and consisting of 2,6-naphthalene dicarboxylic acid or its lower alkyl ester, terephthalic acid or its lower alkyl ester and ethylene glycol or a polymer alloy having a glass transition point of 85° C. or more and 115° C. or below and consisting of polyethylene terephthalate and polyethylene-2,6-naphthalate,
wherein the core layer is formed of a polymer alloy consisting of a thermoplastic polyester resin and a heat-resistant resin, which contains 50 to 65 wt % of the heat-resistant resin having an Izod impact test value of 80 J/m to 850 J/m when tested with a ⅛″ notch under conditions of 23° C. and a relative humidity of 50% and having a glass transition point of 140° C. to 250° C.
2. The laminate according to claim 1 , wherein a molar ratio of 2,6-naphthalene group and phenylene group (2,6-naphthalene group/phenylene group) of the resin forming the skin layer is 30/70 to 92/8.
3. The laminate according to claim 1 , wherein the polymer alloy of the heat-resistant resin and the thermoplastic polymer resin is a polymer alloy of a polyarylate resin and polyethylene terephthalate.
4. A packaging container having a container body with an opening at the upper part, wherein the container body is formed of the laminate according to claim 1 .
5. The laminate according to claim 4 , wherein a molar ratio of 2,6-naphthalene group and phenylene group (2,6-naphthalene group/phenylene group) of the resin forming the skin layer is 30/70 to 92/8.
6. A laminate having a core layer and a skin layer on either side of the core layer, wherein the skin layer is formed of a copolymer having a glass transition point of 85° C. or more and 115° C. or below and consisting of 2,6-naphthalene dicarboxylic acid or its lower alkyl ester, terephthalic acid or its lower alkyl ester and ethylene glycol or a polymer alloy having a glass transition point of 85° C. or more and 115° C. or below and consisting of polyethylene terephthalate and polyethylene-2,6-naphthalate,
wherein:
an intermediate layer is disposed between the core layer and skin layer,
the core layer is formed of a amorphous resin including a thermoplastic resin as the main constituent, and
the intermediate layer is formed of a polymer alloy consisting of a thermoplastic polyester resin and a heat-resistant resin, which contains 50 to 65 wt % of the heat-resistant resin having an Izod impact test value of 80 J/m to 850 J/m when tested with a ⅛″ notch under conditions of 23° C. and a relative humidity of 50% and having a glass transition point of 140° C. to 250° C.
7. The laminate according to claim 6 , wherein the polymer alloy of the heat-resistant resin and the thermoplastic polymer resin is a polymer alloy of a polyarylate resin and polyethylene terephthalate.
8. The laminate according to claim 7 , wherein a molar ratio of 2,6-naphthalene group and phenylene group (2,6-naphthalene group/phenylene group) of the resin forming the skin layer is 30/70 to 92/8.
9. A packaging container having a container body with an opening at the upper part, wherein the container body is formed of the laminate according to claim 6 .
10. A laminate having a core layer and a skin layer on either side of the core layer, wherein the skin layer is formed of a copolymer having a glass transition point of 85° C. or more and 115° C. or below and consisting of 2,6-naphthalene dicarboxylic acid or its lower alkyl ester, terephthalic acid or its lower alkyl ester and ethylene glycol or a polymer alloy having a glass transition point of 85° C. or more and 115° C. or below and consisting of polyethylene terephthalate and polyethylene-2,6-naphthalate,
wherein:
an intermediate layer is disposed between the core layer and the skin layer,
the core layer is formed of a amorphous resin including a thermoplastic polyester resin as the main constituent, and
the intermediate layer is formed of a copolymer having a glass transition point of 110° C. or more and consisting of 2,6-naphthalene dicarboxylic acid or its lower alkyl ester, terephthalic acid or its lower alkyl ester and ethylene glycol or a polymer alloy having a glass transition point of 110° C. or more and consisting of polyethylene terephthalate and polyethylene-2,6-naphthalate.
11. The laminate according to claim 10 , wherein a molar ratio of 2,6-naphthalene group and phenylene group (2,6-naphthalene group/phenylene group) of the resin forming the skin layer is 30/70 to 92/8.
12. A packaging container having a container body with an opening at the upper part, wherein the container body is formed of the laminate according to claim 10 .
13. A laminate having a core layer and a skin layer on either side of the core layer, wherein the skin layer is formed of a copolymer having a glass transition point of 85° C. or more and 115° C. or below and consisting of 2,6-naphthalene dicarboxylic acid or its lower alkyl ester, terephthalic acid or its lower alkyl ester and ethylene glycol or a polymer alloy having a glass transition point of 85° C. or more and 115° C. or below and consisting of polyethylene terephthalate and polyethylene-2,6-naphthalate,
wherein:
an intermediate layer is disposed between the core layer and the skin layer,
the core layer consists of an innermost layer formed of polyamide which is obtained by melt polymerization of a diamine component containing 70 mol % or more of metaxylylene diamine and a dicarboxylic acid component containing 70 mol % or more of adipic acid and an adhesive layer laminated on ether side of the innermost layer, and
the intermediate layer is formed of a polymer alloy consisting of a thermoplastic polyester resin and a heat-resistant resin, which contains 50 to 65 wt % of the heat-resistant resin having an Izod impact test value of 80 J/m to 850 J/m when tested with a ⅛″ notch under conditions of 23° C. and a relative humidity of 50% and having a glass transition point of 140° C. to 250° C.
14. The laminate according to claim 13 , wherein the polymer alloy of the heat-resistant resin and the thermoplastic polymer resin is a polymer alloy of a polyarylate resin and polyethylene terephthalate.
15. The laminate according to claim 14 , wherein a molar ratio of 2,6-naphthalene group and phenylene group (2,6-naphthalene group/phenylene group) of the resin forming the skin layer is 30/70 to 92/8.
16. The laminate according to claim 13 , wherein an intermediate core layer of a amorphous resin which includes a thermoplastic polyester resin as the main constituent is disposed between the intermediate layer and the adhesive layer on one side of the core layer.
17. A packaging container having a container body with an opening at the upper part, wherein the container body is formed of the laminate according to claim 13 .
18. A laminate having a core layer and a skin layer on either side of the core layer, wherein the skin layer is formed of a copolymer having a glass transition point of 85° C. or more and 115° C. or below and consisting of 2,6-naphthalene dicarboxylic acid or its lower alkyl ester, terephthalic acid or its lower alkyl ester and ethylene glycol or a polymer alloy having a glass transition point of 85° C. or more and 115° C. or below and consisting of polyethylene terephthalate and polyethylene-2,6-naphthalate,
wherein the core layer consists of an innermost layer formed of polyamide which is obtained by melt polymerization of a diamine component containing 70 mol % or more of metaxylylene diamine and a dicarboxylic acid component containing 70 mol % or more of adipic acid and an adhesive layer laminated on ether side of the innermost layer.
19. The laminate according to claim 18 , wherein an intermediate core layer formed of a amorphous resin which includes a thermoplastic polyester resin as the main constituent is disposed between the skin layer and the adhesive layer on one side of the core layer.
20. A packaging container having a container body with an opening at the upper part, wherein the container body is formed of the laminate according to claim 18 .